High-hardness weather-resistant metallic coating for photo frame

A metal flash paint, high hardness technology, applied in the direction of anti-corrosion paint, coating, etc., can solve the problem that the hardness and weather resistance of the metal flash paint cannot be satisfied.

Inactive Publication Date: 2016-11-09
蚌埠市禹会区贵宾装饰材料商行
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Then the hardness and weather resistance of the metal flash paint in the prior art can not meet the needs of actual use, so it is urgent to design a metal flash paint with excellent hardness and weather resistance to meet the needs of actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The present invention proposes a high-hardness weather-resistant metal glitter coating for photo frames, and its raw materials include by weight: 50 parts of acrylic modified alkyd resin, 20 parts of modified aluminum powder, 5 parts of acrylic microgel core-shell emulsion, acetoacetic acid 6 parts of ethyl methacrylate, 3 parts of water-based amino resin, 3.5 parts of rheology modified resin, 4.5 parts of polyester resin, 2.5 parts of cellulose acetate butyrate, 3.5 parts of ethylene glycol butyl ether, 4.5 parts of pearl powder, 3.5 parts of carbon black, 3 parts of polyethylene wax, 4 parts of rheological additive BYK-425, 3 parts of water-based defoamer BYK028, 3.5 parts of water-based leveling agent BYK-333, 4.5 parts of deionized water.

[0017] The modified aluminum powder is prepared according to the following process: mix 10 parts of aluminum powder and 3 parts of isopropanol in parts by weight, ultrasonically disperse for 30 minutes, then add 4 parts of tetraet...

Embodiment 2

[0019] The present invention proposes a high-hardness weather-resistant metal glitter coating for photo frames, the raw materials of which include by weight: 45 parts of acrylic modified alkyd resin, 25 parts of modified aluminum powder, 2 parts of acrylic microgel core-shell emulsion, acetoacetic acid 9 parts of ethyl methacrylate, 1 part of water-based amino resin, 5 parts of rheology modified resin, 3 parts of polyester resin, 4 parts of cellulose acetate butyrate, 2 parts of ethylene glycol butyl ether, 6 parts of pearl powder, 1 part of carbon black, 4 parts of polyethylene wax, 3 parts of rheological additive BYK-425, 5 parts of water-based defoamer BYK028, 2 parts of water-based leveling agent BYK-333, 6 parts of deionized water.

[0020] The modified aluminum powder is prepared according to the following process: mix 5 parts of aluminum powder and 5 parts of isopropanol in parts by weight, ultrasonically disperse for 20 minutes, then add 6 parts of tetraethyl silicate a...

Embodiment 3

[0022] The present invention proposes a high-hardness weather-resistant metal glitter coating for photo frames, and its raw materials include by weight: 55 parts of acrylic modified alkyd resin, 15 parts of modified aluminum powder, 8 parts of acrylic microgel core-shell emulsion, acetoacetic acid 3 parts of ethyl methacrylate, 5 parts of water-based amino resin, 2 parts of rheology modified resin, 6 parts of polyester resin, 1 part of cellulose acetate butyrate, 5 parts of butyl ether, 3 parts of pearl powder, 6 parts of carbon black, 2 parts of polyethylene wax, 5 parts of rheological additive BYK-425, 1 part of water-based defoamer BYK028, 5 parts of water-based leveling agent BYK-333, 3 parts of deionized water.

[0023] The modified aluminum powder is prepared according to the following process: mix 15 parts of aluminum powder and 1 part of isopropanol in parts by weight, ultrasonically disperse for 40 minutes, then add 2 parts of tetraethyl silicate and 8 parts of ammonia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-hardness weather-resistant metallic coating for a photo frame. The metallic coating is prepared from acrylic modified alkyd resin, modified aluminum powder, acrylic microgel core-shell emulsion, acetoacetoxy ethyl methacrylate, waterborne amino resin, rheological modified resin, polyester resin, cellulose acetate butyrate, ethylene glycol butyl ether, pearl powder, carbon black, polyethylene wax, a rheological auxiliary BYK-425, a waterborne defoamer BYK028, a waterborne leveling agent BYK-333 and deionized water. The metallic coating is high in hardness and good in weather resistance.

Description

technical field [0001] The invention relates to the field of flash paint, in particular to a high-hardness weather-resistant metal flash paint for photo frames. Background technique [0002] At present, the scaly aluminum powder in the metallic flash paint forms a multi-layer parallel arrangement in the coating film, which can effectively reflect ultraviolet rays, infrared rays and visible light, delay its aging damage to the coating film, and can also effectively prevent water, air, etc. And the penetration of ions, because of its unique decorative and anti-corrosion effects, it is more and more used in the surface coating of photo frames. [0003] However, the hardness and weather resistance of the metal flash coatings in the prior art cannot meet the needs of actual use, so it is urgent to design a metal flash coating with excellent hardness and weather resistance to meet the needs of actual use. Contents of the invention [0004] In order to solve the technical proble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More