Softening treatment process of cotton fiber

A treatment process, cotton fiber technology, applied in the field of cotton fiber softening treatment process, can solve the problems of fiber strength decrease, cellulose molecular chain oxidative fracture, cotton fiber poor hygroscopicity, etc., to improve and regulate metabolism, good antibacterial effect , good yellowing resistance effect

Inactive Publication Date: 2016-11-09
CHANGXING XINTIANLONG PRINTING & DYEING CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The presence of these impurities makes the cotton fiber poor in hygroscopicity and difficult to dye in the subsequent process.
The traditional process uses alkali treatment. While removing impurities such as pectin and wax in cotton fibers, it not only oxidizes and breaks some cellulose molecular chains, reduces the degree of polymerization, and reduces the strength of fibers, but also seriously pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A softening treatment process for cotton fibers, comprising the following steps:

[0025] A. Pretreatment: Boil the cotton fiber in an alkaline solution with a pH of 7-8, lower the temperature to 45°C, add alkaline pectinase for degumming for 12 minutes, and then boil to inactivate the enzyme;

[0026] B. Bleaching: reduce the water temperature to 35°C, add 8g / L 25% hydrogen peroxide, 4g / L bleach stabilizer, 5g / L chitosan, and keep warm for 30min;

[0027] C. Dyeing: After taking out the cotton fabric and simply rinsing it, put it into a natural dye solution for dyeing, wherein the amount of natural dye added is 12g / L, the leveling agent is 1.5g / L, and the liquor ratio is 1:30. 25min;

[0028] D, softening treatment: soak cotton fiber with softener solution, described softener solution comprises 10g / L organosilicon softener, 70g / L glycerol, 4g / L wetting agent, 3g / L EDTA, 0.5g / L mulberry leaf powder, the bath ratio is 1:25, the temperature is 52°C, the treatment time i...

Embodiment 2

[0036] A softening treatment process for cotton fibers, comprising the following steps:

[0037] A. Pretreatment: Boil the cotton fiber in an alkaline solution with a pH of 7-8, lower the temperature to 40°C, add alkaline pectinase for degumming for 15 minutes, and then boil to inactivate the enzyme;

[0038] B. Bleaching: Lower the water temperature to 30°C, add 10g / L of 25% hydrogen peroxide, 5g / L of bleach stabilizer, and 3g / L of chitosan, and keep warm for 25 minutes;

[0039] C. Dyeing: After taking out the cotton fabric and simply rinsing it, put it into the natural dye solution for dyeing. The amount of natural dye added is 15g / L, the leveling agent is 1g / L, the bath ratio is 1:45, soak for 20min ;

[0040] D, softening treatment: soak cotton fiber with softener solution, described softener solution comprises 11g / L organosilicon softener, 60g / L glycerol, 5g / L wetting agent, 2g / L EDTA, 0.5g / L mulberry leaf powder, the bath ratio is 1:20, the temperature is 55°C, the tr...

Embodiment 3

[0048] A softening treatment process for cotton fibers, comprising the following steps:

[0049] A. Pretreatment: Boil the cotton fiber in an alkaline solution with a pH of 7-8, lower the temperature to 50°C, add alkaline pectinase for degumming for 10 minutes, and then boil to inactivate the enzyme;

[0050] B. Bleaching: reduce the water temperature to 40°C, add 5g / L 25% hydrogen peroxide, 5g / L bleach stabilizer, 3g / L chitosan, and keep warm for 35min;

[0051] C. Dyeing: After taking out the cotton fabric and simply rinsing it, put it into a natural dye solution for dyeing, wherein the amount of natural dye added is 5g / L, the leveling agent is 2g / L, the bath ratio is 1:20, soak for 30min ;

[0052] D, softening treatment: soak cotton fiber with softener solution, described softener solution comprises 9g / L organosilicon softener, 80g / L glycerol, 3g / L wetting agent, 5g / L EDTA, 0.2g / L mulberry leaf powder, the bath ratio is 1:30, the temperature is 50°C, the treatment time i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a softening treatment process of cotton fiber. The softening treatment process is characterized by adding folium mori micro powder and isoalcohol polyoxyethylene on the basis of the conventional softening process of cotton fiber, and effectively dispersing the folium mori micro powder in organosilicone continuous films on the surfaces of fabrics. The treated cotton fiber has a good antibacterial effect and also has excellent yellowing resistance; natural dyes and plant antibacterial agents are used in the treatment process; the treated cotton fiber is environment-friendly and healthy.

Description

technical field [0001] The invention relates to the technical field of cotton textiles, in particular to a cotton fiber softening treatment process. Background technique [0002] At present, the production of cotton colored spinning mainly adopts alkali treatment. There are many problems in this method, mainly because the pretreatment and dyeing of cotton fibers are the key processes of the colored spinning process. In addition to 94% cellulose fiber, cotton fiber also has 6% impurities (cellulose symbiosis such as pectin, wax, ash, etc.). The presence of these impurities makes the cotton fiber poor in hygroscopicity and difficult to dye in the subsequent process. The traditional process uses alkali treatment to remove impurities such as pectin and wax in cotton fibers, and at the same time, it not only oxidizes and breaks some cellulose molecular chains, reduces the degree of polymerization, and reduces the strength of fibers, but also seriously pollutes the environment. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M13/148D06M15/53D06M13/00D06P1/34D06P1/613D06P3/60D06P1/647D06L3/02D06M101/06
CPCD06M15/6436D06M13/00D06M13/148D06M15/53D06M16/00D06M2101/06D06M2200/50D06P1/34D06P1/613D06P1/647D06P3/60
Inventor 严建民沈泽平
Owner CHANGXING XINTIANLONG PRINTING & DYEING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com