Method for producing porous shale sintering brick from crystal solid waste shale coal gangue

A technology of coal gangue and sintered bricks, which is applied in the field of solid waste production of building materials, can solve the problems of increasing the difficulty of forming, high plasticity requirements of raw materials, etc., and achieve the effect of raising emission standards

Inactive Publication Date: 2016-11-23
ZHEJIANG PUJIANG JIANGHE NEW BUILDING MATERIALS CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production process of sintered porous bricks and sintered hollow bricks is the same as that of ordinary sintered bricks, but due to the holes in the green body, the difficulty of molding is increased, so the plasticity of raw materials is highly required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for producing porous shale sintered bricks using crystal solid waste shale gangue, the method comprising the following steps:

[0026] 1) According to 8% of construction waste, 20% of crystal solid waste, 42% of shale, 15% of coal gangue tailings, and 15% of road waste;

[0027] 2) Use shale as the main sintered brick material, mix crystal solid waste, and add coal gangue mine tailings, after crushing and vigorous stirring, add crystal wastewater with 15% of the total weight of solid materials during stirring, and mix evenly;

[0028] 3) After mixing evenly, the raw materials are sent to the storage room for plasticity treatment. After the plasticity uniformity reaches the molding requirements, the mixture is sent to the strong mixer through the grab machine and the conveyor, and then sent to the hard plastic extruder after stirring. All kinds of porous blocks are sent into the professional drying kiln, and the waste heat of drying is to use the waste flue gas ...

Embodiment 2

[0031] A method for producing porous shale sintered bricks using crystal solid waste shale gangue, the method comprising the following steps:

[0032] 1) According to 10% of construction waste, 12% of crystal solid waste, 50% of shale, 20% of coal gangue tailings, and 8% of road waste;

[0033] 2) Shale is used as the main sintered brick material, mixed with crystal solid waste, and coal gangue mine tailings are added, after crushing and strong stirring, crystal wastewater with a total weight of 10-15% of solid materials is added during stirring, and mixed evenly ;

[0034] 3) After mixing evenly, the raw materials are sent to the storage room for plasticity treatment. After the plasticity uniformity reaches the molding requirements, the mixture is sent to the strong mixer through the grab machine and the conveyor, and then sent to the hard plastic extruder after stirring. All kinds of porous blocks are sent into the professional drying kiln, and the waste heat of drying is t...

Embodiment 3

[0037] A method for producing porous shale sintered bricks using crystal solid waste shale gangue, the method comprising the following steps:

[0038] 1) According to 15% of construction waste, 10% of crystal solid waste, 50% of shale, 20% of coal gangue tailings, and 5% of road waste;

[0039] 2) Shale is used as the main sintered brick material, mixed with crystal solid waste, and coal gangue mine tailings are added, after crushing and strong stirring, crystal wastewater with a total weight of 10-15% of solid materials is added during stirring, and mixed evenly ;

[0040] 3) After mixing evenly, the raw materials are sent to the storage room for plasticity treatment. After the plasticity uniformity reaches the molding requirements, the mixture is sent to the strong mixer through the grab machine and the conveyor, and then sent to the hard plastic extruder after stirring. All kinds of porous blocks are sent into the professional drying kiln, and the waste heat of drying is t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for producing a building material from solid wastes, in particular to a method for producing a porous shale sintering brick from crystal solid waste shale coal gangue. According to the method, crystal solid waste shale is used, coal gangue tailings are added in proportion, the mixture is crushed and strongly stirred, crystal wastewater is added during stirring and uniformly mixed, raw materials are sent into a storage chamber for plasticity treatment and can be sent into a strong stirrer by a grab machine and a conveyor and then sent into a hard-plastic extruder after being stirred to form various porous building blocks, the building blocks are sent into a special drying kiln by a ferry vehicle to be preheated, the mixture forms a porous brick, and the porous brick enters a calcining kiln to be calcined after being dried. The porous shale sintering brick has high strength, good durability, standard size, complete outline, uniform color and luster and as well as primitive, plain and natural appearance, can be used for a dry wall, and can also be used for any external decoration. Thus, the porous shale sintering brick replacing a clay brick is an upgraded new building material product with great development prospect.

Description

technical field [0001] The invention relates to a method for producing building materials from solid waste, in particular to a method for producing porous shale sintered bricks by utilizing crystal solid waste shale coal gangue. Background technique [0002] In Pujiang, known as the capital of crystal, the processing and sales of crystal materials have become one of the main sources of income for thousands of households. Its vigorous development has enriched the majority of peasant brothers, cultivated a large number of social talents, and also promoted the development of logistics, transportation, packaging and other related industries, and promoted the social and economic development of Pujiang. However, due to the characteristics of the crystal industry, such as low technical level requirements, many geographical distribution points, large quantities, and wide areas, the distribution of the entire industry is unreasonable; the processing of crystal materials in Pujiang Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B33/132
CPCY02P40/60
Inventor 吴建华黄忠城张光华
Owner ZHEJIANG PUJIANG JIANGHE NEW BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap