Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of putty powder and construction technology, applied in the direction of filling slurry, etc., can solve the problems of easy yellowing, mildew, cracking, etc., and achieve the effect of good leveling, strong adhesion, and good water resistance
Inactive Publication Date: 2016-11-23
CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD
View PDF1 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The existing anti-cracking putty powder for construction needs to be improved in leveling, adhesion, water resistance, strength, grinding resistance, acid and alkali corrosion resista...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0053] The anti-cracking putty powder for construction consists of the following components in parts by weight:
[0054] 1-2 parts of sucrose fatty acid ester,
[0055] 2.1 parts gum arabic powder,
[0056] 1.3 parts sodium lauryl sulfonate,
[0057] 1.2 parts lauryltrimethylammonium sulfate,
[0058] 0.9 parts of alkylamine polyoxyethylene ether oxide,
[0059] 0.9 parts phytate,
[0060] 3.6 parts sodium carboxymethylcellulose,
[0061] 15 parts sodium bentonite,
[0062] 30 parts guar gum,
[0063] 50 parts of ash calcium powder.
Embodiment 2
[0065] The anti-cracking putty powder for construction consists of the following components in parts by weight:
[0066] 1 part sucrose fatty acid ester,
[0067] 2.1 parts gum arabic powder,
[0068] 1.3 parts sodium lauryl sulfonate,
[0069] 1.2 parts lauryltrimethylammonium sulfate,
[0070] 0.9 parts of alkylamine polyoxyethylene ether oxide,
[0071] 0.9 parts phytate,
[0072] 3.6 parts sodium carboxymethylcellulose,
[0073] 15 parts sodium bentonite,
[0074] 30 parts guar gum,
[0075] 50 parts of ash calcium powder.
Embodiment 3
[0077] The anti-cracking putty powder for construction consists of the following components in parts by weight:
[0078] 2 parts sucrose fatty acid esters,
[0079] 2.1 parts gum arabic powder,
[0080] 1.3 parts sodium lauryl sulfonate,
[0081] 1.2 parts lauryltrimethylammonium sulfate,
[0082] 0.9 parts of alkylamine polyoxyethylene ether oxide,
[0083] 0.9 parts phytate,
[0084] 3.6 parts sodium carboxymethylcellulose,
[0085] 15 parts sodium bentonite,
[0086] 30 parts guar gum,
[0087] 50 parts of ash calcium powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses building anti-cracking putty powder which is prepared from the following components in parts by weight, 1-2 parts of sucrose fatty acid ester, 2.1 parts of gum Arabic powders, 1.3 parts of sodium dodecyl sulfate, 1.2 parts of dodecyl trimethyl ammonium sulfate, 0.9 part of oxide alkylamine polyoxyethylene ether, 0.9 part of inositol hexaphosphate, 3.6 parts of sodium carboxymethyl cellulose, 15 parts of sodium bentonite, 30 parts of guar gum and 50 parts of ash-calcium powder. The building anti-cracking putty powder is good in leveling property and water resistance, high in adhesive force, high in strength, resistant to grinding, acid and alkaline corrosion, high and low temperature change and mildew, and cannot hollow, peel, crack, fall off, yellow, mildew and generate black spots after being affected with water and damp.
Description
technical field [0001] The invention relates to an anti-cracking putty powder for construction. Background technique [0002] The existing anti-cracking putty powder for construction needs to be improved in leveling, adhesion, water resistance, strength, grinding resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance. After drying, it is prone to hollowing, peeling, cracking, and shedding, and it is prone to yellowing, mold, and black spots. Contents of the invention [0003] The object of the present invention is to provide a kind of anti-cracking putty powder for construction, which has good leveling property, strong adhesion, good water resistance, high strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature change resistance, mildew resistance, After being exposed to water and damp, there will be no hollowing, peeling, cracking, and shedding, and there will be no yellowing, mol...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 范毓明
Owner CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD
Login to view more 
Login to view more