Preparation method of photocuring film coated glass magnesium trim board

A glass-magnesium interior panel and light-curing technology, which is applied in covering/lining, surface pretreatment, and devices for coating liquid on the surface, etc., can solve the problems of poor environmental performance, high decorativeness, and low cost, and achieve The effect of long service life, high decoration and exquisite patterns

Inactive Publication Date: 2016-12-07
ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of no decorative effect of decorative interior panels, poor quality of interior panels with decorative effects, and poor environmental protection performance, we have proposed a method for preparing light-cured film-coated glass magnesium interior panels, which can be achieved by using the present invention High decorative, low cost, long life purpose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of photocuring film coated glass magnesium trim board
  • Preparation method of photocuring film coated glass magnesium trim board
  • Preparation method of photocuring film coated glass magnesium trim board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for preparing a light-cured film-coated glass magnesium interior panel, the steps are as follows:

[0025] (1) Substrate sanding and dust removal: Use a sander to sand the glass magnesium board on both sides to make it smooth, the abrasive belt is 100 mesh, and the sanding time is 30 minutes; after the sanding is completed, use the vortex dust collector to remove the floating dust on the surface Clear and remove static electricity at the same time.

[0026] (2) Roller primer: Roller coat a layer of adhesive primer on the surface of the glass magnesium board, and the amount of adhesive primer roller coating is 15g / m 2 , by 50mj / cm 2 After energy UV light curing, roll coat a layer of sealing primer, the amount of sealing primer is 20g / m 2 , by 200mj / cm 2 Energy UV light curing, and then sanding, the abrasive belt is 300 mesh, after the sanding is completed, use the vortex dust collector to remove the floating dust on the surface, remove static electricity, and...

Embodiment 2

[0040] A method for preparing a light-cured film-coated glass magnesium interior panel, the steps are as follows:

[0041](1) Substrate sanding and dust removal: Use a sander to sand the glass magnesium board on both sides to make it smooth, the abrasive belt is 100 mesh, and the sanding time is 30 minutes; after the sanding is completed, use the vortex dust collector to remove the floating dust on the surface Clear and remove static electricity at the same time.

[0042] (2) Roller primer: Roller coat a layer of adhesive primer on the surface of glass magnesium board, the amount of adhesive primer roller coating is 17g / m 2 , by 100mj / cm 2 After energy UV light curing, roll coat a layer of sealing primer, the amount of sealing primer is 30g / m 2 , by 300mj / cm 2 Energy UV light curing, and then sanding, the abrasive belt is 300 mesh, after the sanding is completed, use the vortex dust collector to remove the floating dust on the surface, remove static electricity, and then ro...

Embodiment 3

[0049] A method for preparing a light-cured film-coated glass magnesium interior panel, the steps are as follows:

[0050] (1) Substrate sanding and dust removal: use a sander to sand the glass magnesium board on both sides to make it smooth, the abrasive belt is 120 mesh, and the sanding time is 20 minutes; after the sanding is completed, use a vortex dust collector to remove dust on the surface Clear and remove static electricity at the same time.

[0051] (2) Roller primer: Roller coat a layer of adhesive primer on the surface of the glass magnesium board, and the amount of adhesive primer roller coating is 20g / m 2 , by 150mj / cm 2 After energy UV light curing, roll a layer of sealing primer, the amount of sealing primer is 40g / m 2 , by 400mj / cm 2 Energy UV light curing, and then sanding, the abrasive belt is 350 mesh, after the sanding is completed, use the vortex dust collector to remove the floating dust on the surface, remove the static electricity, and then roll coat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
drying shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a photocuring film coated glass magnesium trim board. The preparation method comprises the steps of base material sanding and dust removal, priming paint roller coating, first-time infrared heating wire irradiation, film adhesive roller coating, second-time infrared heating wire irradiation, finishing paint roller coating, detection, packaging and delivery. The preparation method has the beneficial effects that patterns are exquisite, and the decoration performance is high; one-time molding is achieved, and no subsequent processing is needed; the cost is low, and the service life period is long; and the board of this kind can become a high-grade decoration material due to the excellent physical performance of the board.

Description

technical field [0001] The invention relates to the field of decorative materials, in particular to a method for preparing a light-cured film-coated glass magnesium interior panel. Background technique [0002] At present, there are many green and environmentally friendly boards emerging at home and abroad. Among them, the glass magnesium board has superior physical properties. The glass magnesium board (commonly known as magnesium oxide board) is a ternary system of magnesium oxide, magnesium chloride, and water. It is a new type of non-combustible decorative material compounded with a stable magnesium cementitious material, a medium-alkaline glass fiber mesh as a reinforcing material, and a lightweight material as a filler. Processed by special production technology, it has the characteristics of fire prevention, waterproof, odorless, non-toxic, non-freezing, non-corrosion, non-cracking, unchanged, non-combustible, high strength and light weight, convenient construction, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D1/38B05D3/02B05D3/06B05D3/12B05D7/00E04F13/14
CPCB05D1/38B05D3/0263B05D3/067B05D3/12B05D7/586B05D2203/30E04F13/0871
Inventor 杨卓舒唐小明贺泽凡杨静钰
Owner ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com