Deep punching production process of metal cover with silk sarface feeling

A production process and metal cover technology, which is applied in the field of deep-drawing metal cover production technology, can solve the problems of long cycle, complicated process and high cost, and achieve a highly decorative effect.

Inactive Publication Date: 2005-06-15
SHANGHAI FENGHUA ZHAOZHI NEW MATERIAL TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is complicated, the cycle is long, the output is low, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] The composition of various coatings is as follows by weight %:

[0009] 1) Composition of primer

[0010] Average molecular weight 700-900 bisphenol A epoxy resin 3

[0011] Average molecular weight 1600-3500 Bisphenol A epoxy resin 5

[0012] Average molecular weight 6000~12000 Neopentyl glycol saturated linear polyester resin 75

[0013] Butanol etherified melamine formaldehyde resin 7

[0014] Isobutanol etherified melamine formaldehyde resin 5

[0015] Aminomethylated Polyether Amino Polyurethane 5

[0016] 2) Composition of topcoat

[0017] Average molecular weight 700-900 bisphenol A epoxy resin 5

[0018] Average molecular weight 1600-3500 Bisphenol A epoxy resin 2

[0019] Average molecular weight 6000~12000 Neopentyl glycol saturated linear polyester resin 80

[0020] Saturated linear polyester resin with an average molecular weight of 15,000 to 20,000 5

[0021] Butanol etherified melamine formaldehyde resin 3

[0022] Aminomethylated Polyether Amino...

Embodiment 2

[0042] The composition of various coatings is as follows by weight %:

[0043] 1) Composition of primer

[0044] Average molecular weight 700-900 Bisphenol A epoxy resin 8

[0045] Average molecular weight 1600-3500 Bisphenol A epoxy resin 4

[0046] Average molecular weight 6000~12000 Neopentyl glycol saturated linear polyester resin 70

[0047] Butanol etherified melamine formaldehyde resin 8

[0048] Isobutanol etherified melamine formaldehyde resin 2

[0049] Aminomethylated Polyether Amino Polyurethane 8

[0050] 2) Composition of topcoat

[0051] Average molecular weight 700-900 Bisphenol A epoxy resin 6

[0052] Average molecular weight 1600-3500 Bisphenol A epoxy resin 2

[0053] Average molecular weight 6000~12000 Neopentyl glycol saturated linear polyester resin 75

[0054] Saturated linear polyester resin with an average molecular weight of 15,000-20,000 8

[0055] Butanol etherified melamine formaldehyde resin 4

[0056] Aminomethylated Polyether Amino Poly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a production process for deep-drawing metal caps with a silky surface feel, which is characterized in that it comprises the following steps: first, degreasing and decontaminating the metal surface; One of the four kinds of paints is coated and cured; the metal plate is deep-drawn 2 to 5 times on the punching machine to obtain a cylinder with a diameter of 30 mm and a height of ≤ 70 mm with a silky surface; finally, the surface of the cylinder is convex Press machining or / and printing processing to obtain deep-drawn metal bottle caps with a height of ≤70mm and a silky surface feel. Used for the packaging of high-end food, wine, beverages, etc.

Description

technical field [0001] The invention relates to a production process of a deep-drawn metal cover, in particular to a production process of a deep-drawn metal cover with a silk surface feel. Background technique [0002] The traditional method of preparing a high-gloss, high-stretch metal cover is to first coat a high-stretch paint on the surface of the metal plate, and then carry out mechanical deep drawing processing after high-temperature curing to obtain a semi-finished product, and then spray or flow coat a high-strength coating on the semi-finished paint surface. Solids clear coating that cures at high temperature to form a high gloss finish. The process is complicated, the cycle is long, the output is low, and the cost is high. Contents of the invention [0003] The purpose of the present invention is to provide a coating with different coefficients of expansion on a metal plate. After mechanical deep drawing, the outer surface coating presents a highly decorative s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/14B21D51/48
Inventor 赵力曾燕
Owner SHANGHAI FENGHUA ZHAOZHI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap