Preparation process for thin ferrite sheet

A ferrite sheet and preparation process technology, which is applied to manufacturing tools, ceramic molding machines, etc., can solve the problems of low yield of thin ferrite sheets, easily deformed reject rate, large amount of raw materials, etc. Not easy to deform, small amount of effect

Active Publication Date: 2016-12-07
滨海华源磁业有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the shortcomings of the prior art described above, the purpose of the present invention is to provide a preparation process for thin ferrite sheets, which is used to solve the problem of large amount of raw materials, low yield and low efficiency of thin ferrite sheets in the prior art. Problems of easy deformation and high scrap rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process for thin ferrite sheet
  • Preparation process for thin ferrite sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 1) Press 80g ferrite raw material to obtain ferrite slab, the thickness of the ferrite slab is 10mm, and the diameter of the ferrite slab is 50mm; the ferrite raw material is Fe 2 o 3 , ZnO and Mn 3 o 4 , Fe 2 o 3 Accounting for 70wt% of the ferrite raw material, ZnO accounting for 8wt% of the ferrite raw material, Mn 3 o 4 Accounting for 22wt% of the ferrite raw material;

[0034] 2) Sintering, slicing and cleaning the ferrite slab obtained in step 1), and slicing it with a circular ferrite sheet cutting bracket, as figure 1 with figure 2 As shown, the annular ferrite sheet cutting bracket at least includes an iron plate 1, a left glass plate 2, a middle glass plate 3 and a right glass plate 4, and the left glass plate 2, the middle glass plate 3 and The right glass plate 4 is arranged on the iron plate 1, and a first glass strip 5 is respectively arranged on both sides of the left glass plate 2, and the distance between the first glass strips 5 is not greater...

Embodiment 2

[0037] 1) 780g ferrite raw material is pressed to obtain a ferrite slab, the thickness of the ferrite slab is 20mm, and the diameter of the ferrite slab is 100mm; the ferrite raw material is Fe 2 o 3 , ZnO and Mn 3 o 4 , Fe 2 o 3 Accounting for 73wt% of ferrite raw materials, ZnO accounts for 7wt% of ferrite raw materials, Mn 3 o 4 Accounting for 20wt% of the ferrite raw material; the ferrite raw material can also include Co 2 o 3 , NiO and CaO, etc., with Fe 2 o 3 , ZnO and Mn 3 o 4 Based on the total weight of Co 2 o 3 : 0.02wt%, NiO: 0.03wt%, CaO: 0.04wt%;

[0038] 2) Sintering, slicing and cleaning the ferrite slab obtained in step 1), and slicing it with a circular ferrite sheet cutting bracket, as figure 1 with figure 2 As shown, the annular ferrite sheet cutting bracket at least includes an iron plate 1, a left glass plate 2, a middle glass plate 3 and a right glass plate 4, and the left glass plate 2, the middle glass plate 3 and The right glass plate ...

Embodiment 3

[0041]1) 6g of ferrite raw material is pressed to obtain a ferrite slab, the thickness of the ferrite slab is 15mm, and the diameter of the ferrite slab is 10mm; the ferrite raw material is Fe 2 o 3 , ZnO and Mn 3 o 4 , Fe 2 o 3 Accounting for 72wt% of the ferrite raw material, ZnO accounts for 9wt% of the ferrite raw material, Mn 3 o 4 It accounts for 19wt% of the ferrite raw material; the ferrite raw material can also include Co 2 o 3 , NiO and CaO, etc., with Fe 2 o 3 , ZnO and Mn 3 o 4 Based on the total weight of Co 2 o 3 : 0.04wt%, NiO: 0.01wt%, CaO: 0.02wt%;

[0042] 2) Sintering, slicing and cleaning the ferrite slab obtained in step 1), and slicing it with a circular ferrite sheet cutting bracket, as figure 1 with figure 2 As shown, the annular ferrite sheet cutting bracket at least includes an iron plate 1, a left glass plate 2, a middle glass plate 3 and a right glass plate 4, and the left glass plate 2, the middle glass plate 3 and The right glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of ferrite sheet preparation, in particular to a preparation process for a thin ferrite sheet. The preparation process comprises the following steps that (1) a ferrite raw material is pressed, a thick ferrite sheet is obtained, and the thickness of the thick ferrite sheet is 10-20 mm; and (2) the thick ferrite sheet obtained in the step (1) is subjected to sintering, slicing and washing. According to the preparation process for the thin ferrite sheet, the using amount of the raw material is decreased, the yield of the thin ferrite sheet and the efficiency are high, deformation is not prone to occurring, and the rejection rate is low.

Description

technical field [0001] The invention relates to the field of preparation of ferrite sheets, in particular to a preparation process of thin ferrite sheets. Background technique [0002] Ferrite is a metal oxide with ferromagnetic properties. In terms of electrical properties, the resistivity of ferrite is much larger than that of metal and alloy magnetic materials, and it also has higher dielectric properties. The magnetic properties of ferrite are also shown to have higher magnetic permeability at high frequencies. Therefore, ferrite has become a widely used non-metallic magnetic material in the field of high frequency and weak current. [0003] The existing thin ferrite sheet preparation process generally uses ferrite raw materials such as Fe 2 o 3 , ZnO and Mn 3 o 4 Direct pressing into thin sheets requires a large amount of raw materials, low efficiency, easy deformation, and high scrap rate. Contents of the invention [0004] In view of the shortcomings of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B28B11/14B28B3/00
CPCB28B3/00B28B11/14
Inventor 薛志萍
Owner 滨海华源磁业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap