Water treatment material for heavy metal wastewater and preparing method thereof

A technology for water treatment and heavy metals, applied in water/sewage treatment, adsorption water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problems of less repeated use times and low adsorption efficiency, and achieve good adsorption effect Effect

Inactive Publication Date: 2016-12-07
何晓东
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, ion exchange and adsorption are also widely used, and activated carbon adsorption and exchange are commonly used; however, due to the characteristics of the pore structure of the activated carbon adsorption process, the treatment efficiency of heavy metal ions needs to be further improved, and the number of repeated uses after regeneration is less, and the adsorption efficiency not tall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] S1: Wash 10 parts of Pine Leaf Fern, 6 parts of Equisetum and 7 parts of Water Chestnut Root and crush them to 60 mesh;

[0023] S2: Mix and stir 20 parts of phenolic resin, 8 parts of salicyl alcohol, 3 parts of 2-amino-5-nitrothiazole and 2 parts of ammonium acetate, and react at 580r / min for 1h at a temperature of 60℃;

[0024] S3: Add 12 parts of propylene glycol and 7 parts of cellulose ether to the product obtained in step S1, and extract Soxhlet at 60°C for 20 minutes;

[0025] S4: Mix the product obtained in step S2, the product obtained in step S3, 6 parts of 2-hydroxyethyl acrylate, 3 parts of potassium oxalyl and 4 parts of 3'-hydroxyacetophenone, and react at a temperature of 40°C for 2h; The water treatment material can be obtained after filtering and drying.

Embodiment 2

[0029] S1: Wash 13 parts of Pine Leaf Fern, 11 parts of Equisetum and 10 parts of Water Chestnut Root and crush them to 80 mesh;

[0030] S2: Mix and stir 30 parts of phenolic resin, 12 parts of salicyl alcohol, 6 parts of 2-amino-5-nitrothiazole and 6 parts of ammonium acetate, and react at a temperature of 70°C at 580r / min for 2h;

[0031] S3: Add 15 parts of propylene glycol and 12 parts of cellulose ether to the product obtained in step S1, and extract Soxhlet at 80°C for 40 minutes;

[0032] S4: Mix the product obtained in step S2, the product obtained in step S3, 10 parts of 2-hydroxyethyl acrylate, 7 parts of potassium oxalyl and 8 parts of 3'-hydroxyacetophenone, and react for 3 hours at a temperature of 50°C; The water treatment material can be obtained after filtering and drying.

Embodiment 3

[0036] S1: Wash 10 parts of Pine Leaf Fern, 10 parts of Equisetum, and 10 parts of Water Chestnut Root and crush them to 60 mesh;

[0037] S2: Mix 22 parts of phenolic resin, 9 parts of salicyl alcohol, 4 parts of 2-amino-5-nitrothiazole and 3 parts of ammonium acetate, and react at 580r / min for 1h at a temperature of 60℃;

[0038] S3: Add 14 parts of propylene glycol and 7 parts of cellulose ether to the product obtained in step S1, and extract Soxhlet at 60°C for 20 min;

[0039] S4: Mix the product obtained in step S2, the product obtained in step S3, 6 parts of 2-hydroxyethyl acrylate, 7 parts of potassium oxalyl and 5 parts of 3'-hydroxyacetophenone, and react for 2 hours at a temperature of 40°C; The water treatment material can be obtained after filtering and drying.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water treatment material for heavy metal wastewater. The water treatment material is prepared from, by weight, 10-13 parts of psilotum nudum, 6-11 parts of horsetail, 7-10 parts of water chestnut root, 20-30 parts of phenolic resin, 12-15 parts of propylene glycol, 8-12 parts of salicylol, 7-12 parts of cellulose ether, 3-6 parts of 2-amino-5-nitrothiazole, 6-10 parts of 2-hydroxy ethyl acrylate, 2-6 parts of ammonium acetate, 3-7 parts of potassium oxonate and 4-8 parts of 3'-hydroxyacetophenone. The water treatment material is mainly prepared from phenolic resin modified by plants such as psilotum nudum, horsetail and water chestnut root. The treatment material is good in effect of adsorbing heavy metal ions and good in reuse effect after being regenerated simply.

Description

Technical field [0001] The invention belongs to the field of wastewater treatment materials, and particularly relates to a water treatment material for heavy metal wastewater and a preparation method thereof. Background technique [0002] While the rapid development of the national economy has brought people great material satisfaction, it has also brought a series of pollution problems. Especially for the pollution of water sources, water is the material that people rely on for survival. The heavy metal pollution is one of the biggest hazards that cause water pollution. The main sources of water pollution caused by heavy metals are: wastewater pollution from mining, metal smelting, metal processing, and chemical production; man-made pollution sources such as pesticides, fertilizers and household garbage. Due to their high toxicity, heavy metals cannot be metabolized and decomposed by themselves in the environment, and their bioaccumulation effects are obvious, they are likely ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/28B01J20/26B01J20/30C02F101/22C02F101/20
CPCC02F1/288B01J20/262C02F2101/20C02F2101/22
Inventor 何晓东
Owner 何晓东
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap