Green glaze for ceramics for daily use

A ceramic and celadon technology, which is applied in the field of daily-use ceramic celadon glaze materials, can solve problems such as retention, production level, and low quality of celadon, and achieve the effect of simple composition, green glaze color, and fine glaze surface

Inactive Publication Date: 2016-12-07
安徽省德邦瓷业有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic products are widely used all over the world. Daily-use ceramics have become an indispensable part of people's daily life. At present, the production of daily-use ceramic green glaze only stays in the production of art porcelain and small batches of daily-use porcelain. In terms of level, celadon still stays at the level of thick glaze and thick body, and the production of celadon with good quality is relatively small. Therefore, a new type of celadon glaze is urgently needed to meet the needs of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The present invention adopts the following technical schemes to realize: this kind of daily-use ceramic green glaze is composed of the following raw materials in parts by weight: 45-50 parts of silicon dioxide, 35-40 parts of kaolin, 5-16 parts of talc, 5 parts of white jade bodhi ~8 parts, titanium carbide 1~2.8 parts, soda ash 1~5 parts, bloodstone 4~12 parts, purple gold soil 12~35 parts, ethylene glycol 8~20 parts, calcium oxide 5~14 parts, graphite powder 0.1~0.8 parts 0.1-0.5 parts of phosphotungstic acid, 20-25 parts of aluminum silicate fiber, 3-8 parts of lubricant and 4-12 parts of thickener.

[0009] As a preferred version of the present invention, the daily-use ceramic green glaze is composed of the following raw materials in parts by weight: 46-50 parts of silicon dioxide, 35-38 parts of kaolin, 8-16 parts of talc, 6-8 parts of white jade bodhi, carbonized 1.5~2.3 parts of titanium, 2~5 parts of soda ash, 6~10 parts of chicken blood stone, 14~23 parts of pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses green glaze for ceramics for daily use. The green glaze is prepared from the following raw materials in parts by weight: 45-50 parts of silicon dioxide, 35-40 parts of kaolin, 5-16 parts of talcum, 5-8 parts of Arenga pinnata, 1-2.8 parts of titanium carbide, 1-5 parts of sodium carbonate, 4-12 parts of bloodstone, 12-35 parts of Zijin clay, 8-20 parts of ethylene glycol, 5-14 parts of calcium oxide, 0.1-0.8 part of graphite powder, 0.1-0.5 part of phosphotungstic acid, 20-25 parts of aluminum silicate fibers, 3-8 parts of lubricant and 4-12 parts of thickener. The green glaze for the ceramics for daily use is simple in composition, easy to clean, high in strength, good in thermal stability and verdant in glaze color and is non-toxic and environmentally friendly, and the burnt ceramic glazed surface is delicate and is good in glossiness.

Description

technical field [0001] The invention relates to a daily-use ceramic glaze, in particular to a daily-use ceramic green glaze. Background technique [0002] Ceramic products are widely used all over the world. Daily-use ceramics have become an indispensable part of people's daily life. At present, the production of daily-use ceramic green glaze only stays in the production of art porcelain and small batches of daily-use porcelain. In terms of level, celadon still stays at the level of thick glaze and thick body, and the production of celadon with good quality is relatively rare. Therefore, a new type of celadon glaze is urgently needed to meet the needs of use. Contents of the invention [0003] The purpose of the present invention is to solve the above problems, and provides a daily-use ceramic green glaze. [0004] In order to achieve the above object, the invention provides a kind of daily-use ceramic celadon glaze material, which is made up of the following raw material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20
CPCC03C8/20
Inventor 姚永祥
Owner 安徽省德邦瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products