A kind of glass fiber sizing agent for chopped strand mat and preparation method thereof

A technology of glass fiber and sizing agent, applied in the field of glass fiber sizing agent for chopped strand mat, can solve the problems that the mechanical and mechanical properties cannot meet the requirements of high-performance glass fiber mat, glass fiber cutability, poor clustering and dispersibility, etc. The effect of optimized formulation components, excellent chopped performance, and simplified configuration and preparation process

Active Publication Date: 2017-09-29
SHANDONG FIBERGLASS GRP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a glass fiber sizing for chopped strand mat, which solves the problem that the existing sizing produces poor glass fiber cutting, bunching and dispersibility, and the mechanical properties cannot meet the requirements of high-performance glass. Fiber Mat Problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass fiber sizing agent for chopped strand mat and preparation method thereof
  • A kind of glass fiber sizing agent for chopped strand mat and preparation method thereof
  • A kind of glass fiber sizing agent for chopped strand mat and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The technical scheme of the present invention will be further described below through specific examples, but the protection scope of the present invention is not limited thereto:

[0036] Referring to Table 1, in the following examples, coupling agent 1 is γ-(methacryloxy)propyltrimethoxysilane, the model is KH570, and coupling agent 2 is γ-glycidyl propane trimethoxysilane, The model is KH560; the antistatic agent is ammonium chloride; the pH regulator is industrial grade glacial acetic acid, purchased from Jining Xuli Chemical Co., Ltd.; lubricant 1 is cationic lubricant, model is 6760L, lubricant 2 is nonionic lubricant The agent was purchased from Jiangsu Haian Petrochemical Plant, model PEG200MO; the polyvinyl acetate emulsion was collected from 682 of Frankin Company.

[0037] Preparation method:

[0038] (1). Add part of deionized water to the pre-mixing container, add glacial acetic acid while stirring, adjust the pH value to 5.0~7.0, and then slowly add γ-(met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass fiber impregnating compound for a chopped strand mat. The impregnating compound is prepared from, by mass, 0.5-3% of silane coupling agent, 3-15% of polyester emulsion, 1-5% of polyvinyl acetate emulsion, 1-6% of lubricant, 0.2-2% of antistatic agent, surfactant, 0.06-2% of pH regulator and the balance deionized water; the pH value of the impregnating compound ranges from 2 to 10. The glass fiber impregnating compound enables glass fibers to have good bundling performance, cutting performance and dispersibility, the finished product is good in softness, compatibility with resin is good, impregnating is fast, and the product has good mechanical properties.

Description

technical field [0001] The invention belongs to the field of glass fiber sizing, in particular to a glass fiber sizing for chopped strand mats. Background technique [0002] Glass fiber chopped strand mat is a medium-alkali or alkali-free material made of continuous glass fiber strands chopped into 50mm lengths, uniformly distributed without orientation, and combined with a binder (or emulsion binder). Glass fiber non-woven felt products. Glass fiber is an inorganic non-metallic material, and it is an indispensable and important raw material in various fields such as petrochemical industry, electronic power, road transportation, aerospace and so on. It has been produced abroad since the early 1970s, and has now developed into one of the main products of glass fiber. Since the late 1970s and early 1980s, my country began to develop its own production equipment and technology for chopped strand mat. Through continuous technological innovation and technology introduction, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information