Formula and preparation method of novel environment-friendly brick

An environmentally friendly brick, a new type of technology, applied in the field of construction, can solve the problems of consuming large land resources and not meeting the sustainable development of resource and environmental protection, achieve good adsorption effect, improve crosslinking and adhesion, and have good heat resistance Effect

Inactive Publication Date: 2017-01-04
桃江县众泰新型建材有限责任公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, with the increase of population, land resources are becoming more and more scarce, and the preparation of traditional clay bricks consumes a lot of land resources, which does not meet the strategic requirements of resource environmental protection and sustainable development, so in the future, clay bricks will be Replaced by new bricks that are more economical and environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A new type of environmentally friendly brick formula, which includes the following raw materials in proportion by mass: 60 parts of calcium carbide powder, 30 parts of industrial waste residue, 6 parts of nano-ferrite wave-absorbing material, 5 parts of latex, 6 parts of polyester fiber, and 8 parts of activated carbon parts, 6 parts of nano-magnesium oxide, 4 parts of nano-zinc oxide, and 10 parts of activator.

[0028] A kind of preparation method of novel environment-friendly brick, it comprises the following steps:

[0029] Step 1) Raw material preparation: Weigh the raw materials of each component according to the specified mass ratio of new environmental protection bricks; place calcium carbide powder and industrial waste residue in a crusher for crushing; after crushing, grind to make more than 95% fine powder Diameter≤0.1mm;

[0030] Step 2) mixing and stirring: pour the raw materials prepared in step 1) into a blender, add water and stir evenly to form a slurr...

Embodiment 2

[0035] A new type of environmentally friendly brick formula, which includes the following raw materials in proportion by mass: 68 parts of calcium carbide powder, 32 parts of industrial waste residue, 7 parts of nano-ferrite wave-absorbing material, 6 parts of latex, 7 parts of polyester fiber, and 10 parts of activated carbon parts, 7 parts of nano-magnesium oxide, 5 parts of nano-zinc oxide, and 12 parts of activator.

[0036] A kind of preparation method of novel environment-friendly brick, it comprises the following steps:

[0037] Step 1) Raw material preparation: Weigh the raw materials of each component according to the specified mass ratio of new environmental protection bricks; place calcium carbide powder and industrial waste residue in a crusher for crushing; after crushing, grind to make more than 95% fine powder Diameter≤0.1mm;

[0038] Step 2) mixing and stirring: pour the raw materials prepared in step 1) into a blender, add water and stir evenly to form a slur...

Embodiment 3

[0043] A new type of environmentally friendly brick formula, which includes the following raw materials in proportion by mass: 75 parts of calcium carbide powder, 35 parts of industrial waste, 8 parts of nano-ferrite wave-absorbing material, 7 parts of latex, 8 parts of polyester fiber, and 12 parts of activated carbon parts, 8 parts of nano-magnesium oxide, 6 parts of nano-zinc oxide, and 13 parts of activator.

[0044] A kind of preparation method of novel environment-friendly brick, it comprises the following steps:

[0045] Step 1) Raw material preparation: Weigh the raw materials of each component according to the specified mass ratio of new environmental protection bricks; place calcium carbide powder and industrial waste residue in a crusher for crushing; after crushing, grind to make more than 95% fine powder Diameter≤0.1mm;

[0046] Step 2) mixing and stirring: pour the raw materials prepared in step 1) into a blender, add water and stir evenly to form a slurry;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a formula and a preparation method of a novel environment-friendly brick and belongs to the field of buildings. The novel environment-friendly brick is prepared from the following raw materials in parts by weight: 60-75% of calcium carbide powder, 30-35 parts of industrial residues, 6-8 parts of a nano wave absorbing material, 5-7 parts of a sound-proof material, 6-8 parts of a flexible fiber, 8-12 parts of active carbon, 6-8 parts of nano magnesium oxide, 4-6 parts of nano zinc oxide and 10-13 parts of an exciting agent. The invention aims at providing the formula and the preparation method of the novel environment-friendly brick. Industrial residues are fully utilized, so that the cost of raw materials for production is lowered, and the environmental pollution is reduced. The method is simple, and easy to implement and popularize; the prepared novel environment-friendly brick is high in strength, high in fire-fighting and anti-crack property and good in heat insulation property, and also has the effects of resisting bacteria, preventing mildew, resisting aging, resisting corrosion, preventing electromagnetic wave radiation, achieving ultrastrong sound insulation, and the like.

Description

technical field [0001] The invention belongs to the field of construction, and in particular relates to a formula of a novel environment-friendly brick and a preparation method thereof. Background technique [0002] Existing building bricks are mainly clay bricks prepared from clay as raw material. At present, with the increase of population, land resources are becoming more and more scarce, and the preparation of traditional clay bricks consumes a lot of land resources, which does not meet the strategic requirements of resource environmental protection and sustainable development, so in the future, clay bricks will be It is replaced by a new type of brick that is more economical and environmentally friendly. Contents of the invention [0003] The purpose of the present invention is to address the above problems, to provide a new type of environmentally friendly brick formula and its preparation method, which fully utilizes industrial waste residues, reduces the cost of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/18C04B111/28C04B111/20C04B111/52
CPCC04B28/18C04B2111/20C04B2111/28C04B2111/52C04B18/04C04B14/322C04B16/0683C04B14/022C04B14/363C04B22/066C04B22/06C04B2103/0045C04B2103/0068C04B40/024
Inventor 刘琨卢落平
Owner 桃江县众泰新型建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com