Rustproof solution based on nano ceramic materials and preparation method thereof

A nano-ceramic and solution technology, which is applied in the direction of metal material coating process, etc., can solve the problems of reducing precision, generating rust pits, affecting service life, etc., and achieves the effect of good bonding, improving metal surface performance, and improving oxidation resistance

Active Publication Date: 2017-01-04
HEFEI ORIENT METALLURGICAL EQUIP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no matter whether steel materials are used or placed in the atmospheric environment for a long time, they will gradually undergo chemical or electrochemical reactions with the surrounding medium, causing surface corrosion
Slight corrosion can make the surface lose its metallic luster and reduce precision. In severe cases, rust pits will appear on the surface, which will deteriorate or even break the mechanical properties of steel products and affect their service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A solution for rust prevention based on nano-ceramic materials, said solution is a mixed solution prepared from multiple components, and the mass of each component in every 600 grams of mixed solution satisfies in grams:

[0049] 3-(2,3-Glycidoxy)propyltrimethoxysilane 13.5

[0050] Silane hydrolyzate 2.75

[0051] Ethyl silicate 0.65

[0052] Sodium metasilicate pentahydrate 34

[0053] Nano ceramics 65

[0054] Silica sol 10

[0055] Sodium carbonate 2.65

[0056] Sodium Gluconate 4

[0057] Sodium citrate 2.25

[0058] Isopropanol 102

[0059] Deionized water 363.2.

[0060] Among them, the weight parts of raw materials are 0.4-0.6 parts of ethyl silicate, 0.7-0.9 parts of sodium metasilicate pentahydrate, 0.4-0.6 parts of sodium carbonate, 1.9-2.1 parts of sodium gluconate, 1.5-1.7 parts of sodium citrate, deionized 20-25 parts of water constitute the silane hydrolyzate.

[0061] Among them, the silane hydrolyzate also includes 6-8 parts of silane hydrolyz...

Embodiment 2

[0071] A solution for rust prevention based on nano-ceramic materials, said solution is a mixed solution prepared from multiple components, and the mass of each component in every 600 grams of mixed solution satisfies in grams:

[0072] 3-(2,3-Glycidoxy)propyltrimethoxysilane 12

[0073] Silane hydrolyzate 2

[0074] Ethyl silicate 0.5

[0075] Sodium metasilicate pentahydrate 33

[0076] Nanoceramics 60

[0077] Silica sol 8

[0078] Sodium carbonate 2.5

[0079] Sodium Gluconate 3

[0080] sodium citrate 2

[0081] Isopropanol 100

[0082] Deionized water 377.

[0083] Among them, the weight parts of raw materials are 0.4-0.6 parts of ethyl silicate, 0.7-0.9 parts of sodium metasilicate pentahydrate, 0.4-0.6 parts of sodium carbonate, 1.9-2.1 parts of sodium gluconate, 1.5-1.7 parts of sodium citrate, deionized 20-25 parts of water constitute the silane hydrolyzate.

[0084] Among them, the silane hydrolyzate also includes 6-8 parts of silane hydrolyzate, 10-14 par...

Embodiment 3

[0094] A solution for rust prevention based on nano-ceramic materials, said solution is a mixed solution prepared from multiple components, and the mass of each component in every 600 grams of mixed solution satisfies in grams:

[0095] 3-(2,3-Glycidoxy)propyltrimethoxysilane 15

[0096] Silane hydrolyzate 3.5

[0097] Ethyl silicate 0.8

[0098] Sodium metasilicate pentahydrate 35

[0099] Nanoceramics 70

[0100] Silica sol 12

[0101] Sodium carbonate 2.8

[0102] Sodium Gluconate 5

[0103] Sodium citrate 2.5

[0104] Isopropanol 105

[0105] Deionized water 348.4.

[0106] Among them, the weight parts of raw materials are 0.4-0.6 parts of ethyl silicate, 0.7-0.9 parts of sodium metasilicate pentahydrate, 0.4-0.6 parts of sodium carbonate, 1.9-2.1 parts of sodium gluconate, 1.5-1.7 parts of sodium citrate, deionized 20-25 parts of water constitute the silane hydrolyzate.

[0107] Among them, the silane hydrolyzate also includes 6-8 parts of silane hydrolyzate, 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rustproof solution based on nano ceramic materials and a preparation method thereof. The solution is mixture liquid prepared from various constituents. The constituents in every 600 grams of the mixture liquid comprise, in grams, 3-(2,3-Epoxypropoxy) propyltrimethoxysilicane, silane hydrolysate, ethyl silicate, sodium metasilicate pentahydrate, nano ceramic, a silica solution, sodium carbonate, gluconic acid sodium salt, sodium citrate, isopropanol and the balance deionized water. According to the rustproof solution based on the nano ceramic materials and the preparation method thereof, the nano ceramic materials are added into the rustproof silane solution, and a rigid layer is formed on the surface of a silanization composite film generated on the metal surface through the added nano ceramic materials, so that oxidation resistance and abrasion resistance of the metal surface are improved.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, in particular to a solution for antirust based on nano-ceramic materials and a preparation method thereof. Background technique [0002] Iron and steel materials have high strength and hardness, as well as good plasticity and processability, so it is the most widely used structural material in the world today. However, no matter whether steel materials are used or placed in the atmospheric environment for a long time, they will gradually undergo chemical or electrochemical reactions with the surrounding medium, causing surface corrosion. Mild corrosion can cause the surface to lose its metallic luster and reduce precision. In severe cases, rust pits will appear on the surface, which will deteriorate or even break the mechanical properties of steel products and affect their service life. According to reports, in industrially developed countries, the annual loss due to corrosion of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/60C23C22/62C23C22/66
CPCC23C22/60C23C22/62C23C22/66C23C2222/20
Inventor 吴鹏赵仕堂吴迪梁海峰王孟祥王磊
Owner HEFEI ORIENT METALLURGICAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com