Method of using coconut fiber for preparing nano fibril of different scales and application

A technology of coconut shell fiber and fiber, which is applied in the field of preparing nano-fibrils of different scales by oxidation method, which can solve the problems of chemical method pollution, easy-to-corrosion equipment, and high efficiency, and achieve the effects of low corrosion, low energy consumption, and high efficiency

Active Publication Date: 2017-01-04
DONGHUA UNIV
View PDF26 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical method has pollution and is easy to corrode the equipment, but the efficiency is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of using coconut fiber for preparing nano fibril of different scales and application
  • Method of using coconut fiber for preparing nano fibril of different scales and application
  • Method of using coconut fiber for preparing nano fibril of different scales and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A kind of method that utilizes coconut shell fiber to prepare nano-fibrils of different scales, concrete steps are:

[0049] (1) Opening and removing impurities, scouring and swelling, and cleaning to remove adherent impurities: the coconut shells are loosened by mechanical striking, rubbing and pulling, and the adhered coconut shell fibers and impurities at the roots are removed to obtain fiber clusters. The fiber mass is scoured, washed and squeezed to remove water. The specific steps of scouring, washing and squeezing to remove water include placing the fiber mass in a beaker, completely submerging it in water, and placing it in a 98°C water bath Carry out scouring and swelling for 1 hour, stir with a rotating speed of 500rpm while scouring, and use a multi-stage roller device to squeeze the fiber mass to remove water after scouring, wash with water, and then squeeze to remove water; the scouring, Washing and extruding to remove the water cycle for 4 times to remove ...

Embodiment 2

[0055] A kind of method that utilizes coconut shell fiber to prepare nano-fibrils of different scales, concrete steps are:

[0056] (1) Opening and removing impurities, scouring and swelling, and cleaning to remove adherent impurities: the coconut shells are loosened by mechanical striking, rubbing and pulling, and the adhered coconut shell fibers and impurities at the roots are removed to obtain fiber clusters. The fiber mass is scoured, washed and squeezed to remove water. The specific steps of scouring, washing and squeezing the water include placing the fiber mass in a beaker, completely submerging it in water, and placing it in a water bath at 80°C. Carry out scouring and swelling for 3 hours, stir with a rotating speed of 500rpm while scouring, and use a multi-stage roller device to squeeze the fiber mass to remove water after scouring, wash with water, and then squeeze to remove water; the scouring, Washing and extruding to remove the water cycle for 3 times to remove t...

Embodiment 3

[0062] A kind of method that utilizes coconut shell fiber to prepare nano-fibrils of different scales, concrete steps are:

[0063] (1) Opening and removing impurities, scouring and swelling, and cleaning to remove adherent impurities: the coconut shells are loosened by mechanical striking, rubbing and pulling, and the adhered coconut shell fibers and impurities at the roots are removed to obtain fiber clusters. The fiber mass is scoured, washed and squeezed to remove water. The specific steps of scouring, washing and squeezing to remove water include placing the fiber mass in a beaker, completely submerged in water, and placed in a 70°C water bath Carry out scouring and swelling for 3 hours, stir with a rotating speed of 500rpm while scouring, and use a multi-stage roller device to squeeze the fiber mass to remove water after scouring, wash with water, and then squeeze to remove water; the scouring, Washing and extruding to remove the water cycle for 3 times to remove the int...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method of using coconut fiber for preparing nano fibril of different scales. The method is characterized by including the steps that swelled and separated native cellulose fiber and part of unicellular tubular fiber are completely soaked in a mixed solution containing NaOH and NaClO according to the solid-liquid weight ratio of 1:30-1:50, the concentration of NaOH in the mixed solution containing NaOH and NaClO is 20-80 g / L, the concentration of NaClO is 15-65 g / L, and the fiber is stirred at the temperature of 60-98 DEG C and synchronously vibrated for 1-20 h with ultrasonic waves to obtain the mixed solution containing the nano fibril; centrifugal separation is carried out on the obtained mixed solution containing the nano fibril for the first time to remove impurities, and then subnatant is taken to carry out the steps A, B and C. Targeting swelled and dissolved fibril mesenchyme and ultrasonic microbubble impact enlargement are used to efficiently separate micron fibril and base fibril in a low-damage mode, which is beneficial for high-technology and refined cyclic utilization of the coconut fiber and beneficial for sustainable development of cellulosic fiber resources.

Description

technical field [0001] The invention relates to a method for preparing nano-fibrils of different scales by utilizing coconut shell fibers, in particular to a method and application of preparing nano-fibrils of different scales by an oxidation method. Background technique [0002] Cellulose is an inexhaustible, inexhaustible, green, non-polluting renewable resource in nature. The annual growth of plant cellulose on the earth is as high as hundreds of millions of tons, exceeding the total existing oil reserves, but the utilization amount is very small. Most of them are naturally degraded and burned as fuel, which itself is a kind of pollution. It is reported that the loss caused by environmental pollution and ecological damage has accounted for 15% of the total GDP, which means that there is a 9% economic growth on the one hand and a loss rate of 15% on the other. When human society is faced with many problems such as resource poverty, energy crisis, and environmental polluti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01C1/00
CPCD01C1/00