Heat-shrinkage-resistant lithium ion battery diaphragm and polyethylene composition adopted by same

A lithium-ion battery and polymer polyethylene technology, which is applied in the field of polyolefin compositions, can solve the problems of unfavorable battery separators, incomplete sealing of pore-forming agents, and easy outflow.

Active Publication Date: 2017-01-11
LIAOYUAN HONGTU LI ION BATTERY DIAPHRAGM TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There are some defects in the traditional battery separator wet preparation process, including: in the casting process, a casting roll with cooling function is usually used for single-sided cooling, and the pore-forming agent is not completely sealed and easy to flow out, resulting in uneven distribution of micropores ;The extrusion equipment in different production steps is different, resulting in different product quality and appearance, and it is difficult to control the consistency; usually the surface of the extrusion equipment and stretching tension equipment is smooth, and the surface of the manufactured diaphragm is smooth, and the adhesion with other substances The ability is poor, which is not conducive to the development of new battery separators; the drying equipment after extraction usually uses two methods of water gun and air gun at the same time, resulting in water marks on the surface of the separator, and the flatness is not good enough
[0006] At present, in the prior art, there is a method of laminating multilayer polyolefin films to make multilayer composite lithium ion battery separators. Not only is the operation complicated, the product quality is unstable, and the equipment used often requires special design.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-shrinkage-resistant lithium ion battery diaphragm and polyethylene composition adopted by same
  • Heat-shrinkage-resistant lithium ion battery diaphragm and polyethylene composition adopted by same
  • Heat-shrinkage-resistant lithium ion battery diaphragm and polyethylene composition adopted by same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0232] The polyethylene composition used to prepare heat-shrinkable lithium-ion battery separators includes the following components by weight:

[0233]

[0234]

[0235] in,

[0236] The number average molecular weight of high molecular polyethylene is 500,000,

[0237] The number average molecular weight of UHMWPE is 1.4 million,

[0238] The average molecular weight of white oil is 200,

[0239] The particle size of the nano-magnesium chloride is 50-70nm.

[0240] Above-mentioned composition is made lithium-ion battery diaphragm according to the following method:

[0241]Step 1), extrusion: melt and mix high molecular polyethylene and nano-magnesium chloride, add ultra high molecular polyethylene, 4,4-thiobis(6-tert-butyl meta cresol), 2,4-dihydroxybenzophenone, sodium octadecyl quaternary ammonium and Tween 80 are added to the extruder by the second feed port, white oil is fed by the first pore-forming agent feed port and The second pore-forming agent feed port ...

Embodiment 2

[0248] The composition for preparing lithium-ion battery diaphragm comprises the following components by weight:

[0249]

[0250] in,

[0251] The number average molecular weight of high molecular weight polyethylene is 300,000.

[0252] The number average molecular weight of UHMWPE is 1.3 million.

[0253] The average molecular weight of white oil is 180;

[0254] The particle size of the nano-magnesium chloride is 60-90nm.

[0255] The above-mentioned composition is prepared lithium-ion battery diaphragm according to the following method:

[0256] Step 1), extrusion: melt and mix high molecular polyethylene and nano-magnesium chloride, add ultra high molecular polyethylene, 3,5-di-tert-butyl-4-hydroxytoluene, 4-benzoyloxy-2,2,6,6-tetramethylpiperidine, sodium octadecyl quaternary ammonium and lauric acid are fed into the extruder from the second feed port, white oil is fed from the first The feed port of the pore agent and the feed port of the second pore forming ag...

Embodiment 3

[0263] The method used in this embodiment is similar to the method used in Example 2, except that the polyethylene composition comprises the following components by weight:

[0264]

[0265] in,

[0266] The number average molecular weight of high molecular weight polyethylene is 400,000.

[0267] The number average molecular weight of UHMWPE is 1.4 million.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a polyethylene composition for preparing a heat-shrinkage-resistant lithium ion battery diaphragm. The composition comprises high-molecular polyethylene, ultra-high-molecular polyethylene and an optional additive. The lithium ion battery diaphragm prepared from the composition has high heat shrinkage resistance, high tensile strength, high puncture strength, relatively high diaphragm-rupture temperature and relatively low closed-hole temperature, thereby ensuring safety in preparation and usage of the lithium ion battery.

Description

technical field [0001] The invention relates to the field of lithium-ion battery separators, in particular to a heat-shrinkable lithium-ion battery separator and a polyolefin (especially polyethylene) composition used. Background technique [0002] Lithium-ion batteries are widely used in the fields of electronic communication, energy storage, and power supply. They are mainly composed of positive electrodes, negative electrodes, electrolytes, and battery separators. Among them, the battery separator is non-conductive and is located between the positive and negative electrodes to prevent positive and negative electrodes. The latter is short-circuited due to contact, and at the same time allows the electrolyte ions to pass through, thereby generating current. The current battery separator is mostly a polyolefin film with a microporous structure, and its performance determines the interface structure and internal resistance of the battery, which directly affects the capacity of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/14H01M2/16H01M10/0525H01M50/403H01M50/411H01M50/417
CPCH01M10/0525H01M50/40H01M50/409Y02E60/10
Inventor 张汉鸿
Owner LIAOYUAN HONGTU LI ION BATTERY DIAPHRAGM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com