Non-toxic efficient rust-proof oil

An anti-rust oil and high-efficiency technology, applied in the petroleum industry, lubricating compositions, etc., can solve the problem of insignificant effect of anti-rust oil, and achieve the effect of good anti-rust effect, no pollution to the environment, and guaranteeing the quality of workpieces.

Inactive Publication Date: 2017-02-15
MAANSHAN NIUZE TECH SERVICE
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to statistics, the direct economic loss caused by metal corrosion accounts for about 2% to 4% of the total output value of the national economy every year; in order to avoid corrosion and reduce l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example one:

[0014] The component ratios used are: 10 parts castor oil, 3 parts lanolin magnesium soap, 10 parts paraffin wax, 1 part antioxidant, 8 parts oil-soluble vapor phase corrosion inhibitor, 4 parts sodium molybdate, 10 parts film former Parts, 8 parts of lauric acid, 5 parts of nano silica, 10 parts of sodium petroleum sulfonate, 1 part of polyacrylate, 5 parts of polyoxyethylene rosin acid.

[0015] The preparation process of this embodiment includes the following steps:

[0016] A. Mix castor oil, lanolin magnesium soap, paraffin wax, antioxidants, and oil-soluble vapor phase corrosion inhibitors and add them to a mixer for low-speed stirring. The mixer speed is 500 rpm and the stirring time is 20 minutes to obtain mixture A ;

[0017] B. Add sodium molybdate, film forming agent, lauric acid, nano silica, sodium petroleum sulfonate, polyacrylate, polyoxyethylene rosin acid to the mixture A, and add it to the reaction kettle after mixing, and the reaction kettle i...

Example Embodiment

[0019] Embodiment two:

[0020] The component ratios used are: 20 parts castor oil, 8 parts lanolin magnesium soap, 15 parts paraffin wax, 5 parts antioxidant, 15 parts oil-soluble gas phase corrosion inhibitor, 10 parts sodium molybdate, 15 parts film former Parts, 12 parts of lauric acid, 15 parts of nano-silica, 20 parts of sodium petroleum sulfonate, 4 parts of polyacrylate, 10 parts of polyoxyethylene rosin acid.

[0021] The preparation process of this embodiment includes the following steps:

[0022] A. Mix castor oil, lanolin magnesium soap, paraffin wax, antioxidants, and oil-soluble vapor phase corrosion inhibitors and add them to a mixer for low-speed stirring. The mixer speed is 500 rpm and the stirring time is 20 minutes to obtain mixture A ;

[0023] B. Add sodium molybdate, film forming agent, lauric acid, nano silica, sodium petroleum sulfonate, polyacrylate, polyoxyethylene rosin acid to the mixture A, and add it to the reaction kettle after mixing, and the reaction ...

Example Embodiment

[0025] Embodiment three:

[0026] The component ratios used are: 12 parts castor oil, 4 parts lanolin magnesium soap, 11 parts paraffin wax, 2 parts antioxidant, 9 parts oil-soluble gas phase corrosion inhibitor, 5 parts sodium molybdate, 11 parts film former Parts, 9 parts of lauric acid, 6 parts of nano-silica, 12 parts of sodium petroleum sulfonate, 2 parts of polyacrylate, 6 parts of polyoxyethylene rosin acid.

[0027] The preparation process of this embodiment includes the following steps:

[0028] A. Mix castor oil, lanolin magnesium soap, paraffin wax, antioxidants, and oil-soluble vapor phase corrosion inhibitors and add them to a mixer for low-speed stirring. The mixer speed is 500 rpm and the stirring time is 20 minutes to obtain mixture A ;

[0029] B. Add sodium molybdate, film-forming agent, lauric acid, nano silica, sodium petroleum sulfonate, polyacrylate, polyoxyethylene rosin acid to the mixture A, and add it to the reaction kettle after mixing, and the reaction ket...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses non-toxic efficient rust-proof oil which is prepared from the components of, by weight, 10-20 parts of castor oil, 3-8 parts of lanolin magnesium soap, 10-15 parts of paraffin wax, 1-5 parts of antioxidant, 8-15 parts of oil soluble gas phase corrosion inhibitor, 4-10 parts of sodium molybdate, 10-15 parts of film-forming agent, 8-12 parts of lauric acid, 5-15 parts of nanosilicon dioxide, 10-20 parts of petroleum sodium sulfonate, 1-4 parts of polyacrylate and 5-10 parts of rosin-polythylene oxide ester. According to the non-toxic efficient rust-proof oil, the preparation technology is simple, the preparation process is environmental-friendly and free of pollution, the rust-proof effect of the prepared rust-proof oil is good, the rust-proof period is long, and no pollution is caused to the environment; besides, the surface of a workpiece can be prevented from being scratched, and the workpiece quality is guaranteed.

Description

technical field [0001] The invention relates to the technical field of antirust oil preparation, in particular to a non-toxic and efficient antirust oil. Background technique [0002] Corrosion is one of the main forms of damage to fasteners, and it will cause great losses to automobiles, motorcycles and various vehicles and machinery. According to statistics, the direct economic loss caused by metal corrosion accounts for about 2% to 4% of the total output value of the national economy every year; in order to avoid corrosion and reduce losses, people have adopted various methods to protect metal with anti-rust grease. Fasteners are currently one of the most common protection methods; however, the current anti-rust oil is not effective. Contents of the invention [0003] The object of the present invention is to provide a kind of non-toxic high-efficiency anti-rust oil, to solve the problems raised in the above-mentioned background technology. [0004] In order to achiev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10N30/12
CPCC10M169/048C10M2201/08C10M2201/10C10M2203/02C10M2205/18C10M2207/126C10M2207/402C10M2209/084C10M2209/104C10M2219/044C10N2030/12C10N2030/64
Inventor 张伟施享
Owner MAANSHAN NIUZE TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap