Preparation method of anticoagulation hemodialysis membrane
A technology of hemodialysis and anticoagulation, which is applied in the field of preparation of anticoagulant hemodialysis membranes, can solve the problems of loss and loss of anticoagulation performance of hemodialysis membranes, achieve the alleviation of coagulation problems, be easy for industrial production, and the reaction conditions can be controlled control effect
Active Publication Date: 2017-03-01
江苏朗生生命科技有限公司
View PDF5 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, as a water-soluble polymer, polyvinylpyrrolidone (PVP) will dissolve in water and be lost during the preparation and use of the dialysis membrane, resulting in the loss of the anticoagulant performance of the hemodialysis membrane.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0019] A kind of preparation method of anticoagulant hemodialysis membrane of the present invention, carry out according to the following steps:
[0020] (1) Hydrolyzing polyvinylpyrrolidone.
[0021] In the present invention, polyvinylpyrrolidone and deionized water are added into the reactor at a mass ratio of 0.01-0.2:1, and then an acidic hydrolysis catalyst or an alkaline hydrolysis catalyst is added to make the polyvinylpyrrolidone aqueous solution undergo hydrolysis reaction at a temperature of 55-95°C. , the reflux time is controlled at 1.5~2h, and the modified polyvinylpyrrolidone with carboxyl and amine active groups is obtained, and the original chemically stable polyvinylpyrrolidone is hydrolyzed by hydrolysis reaction, and part of the amide bond is hydrolyzed to form a reactive amine group and carboxyl group to obtain reactive functional groups in the structure of polyvinylpyrrolidone. The remaining deionized water was evaporated by heating to obtain modified pol...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a preparation method of an anticoagulation hemodialysis membrane. The preparation method comprises the following steps: adding polyvinylpyrrolidone and deionized water into a reaction vessel according to mass ratio of 0.01-0.2:1, adding a hydrolysis catalyst and carrying out reflux at the temperature of 55-95 DEG C for 1.5-2 h so as to obtain modified polyvinylpyrrolidone with carboxyl and amino active groups; soaking a cleaned hemodialysis membrane in the modified polyvinylpyrrolidone aqueous solution and controlling soaking time within 0.5-50 h, taking the hemodialysis membrane out and standing, and air-drying; carrying out a cross-linking reaction by soaking the hemodialysis membrane in a cross-linking agent solution, and obtaining a functional layer containing modified polyvinylpyrrolidone group on the surface of the hemodialysis membrane and inside membrane holes; and cleaning the modified hemodialysis membrane with n-hexane, cleaning the modified hemodialysis membrane with ethanol, cleaning the modified hemodialysis membrane with deionized water, and removing residual reactant and solvent. As the stable anticoagulation functional layer is formed on the surface of the hemodialysis membrane and inside the membrane holes, performance of the hemodialysis membrane can be improved.
Description
technical field [0001] The invention relates to a preparation method of an anticoagulant hemodialysis membrane, belonging to the technical field of hollow fiber hemodialysis membranes. Background technique [0002] Hemodialysis is the main means of treating patients with acute and chronic renal failure, and hemodialysis membrane is very important in hemodialysis products. During the dialysis process, when the hemodialysis membrane with poor biocompatibility comes into contact with blood, it may destroy red blood cells, activate and aggregate platelets, and then form thrombus, cause blood coagulation, block the membrane fiber pipeline, affect the progress of dialysis and reduce the risk of dialysis. The effect of the treatment. [0003] At present, in clinical practice, there is no artificial medical biomaterial that can be perfectly applied in the human body. Hemocompatibility is the most important performance index of biomaterials, and anticoagulant performance is the dec...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): B01D71/82B01D69/08B01D69/02B01D67/00A61M1/18
Inventor 戈旭亚于海军
Owner 江苏朗生生命科技有限公司