A kind of material for making grinding wheel and the manufacturing method of grinding wheel

A manufacturing method and a grinding wheel technology, which are applied in the directions of abrasives, manufacturing tools, grinding tools, etc., can solve the problems of low processing accuracy and efficiency, and achieve the effect of improving smoothness, good smoothness and improving grinding accuracy.

Active Publication Date: 2018-09-21
深圳市鑫金泉精密技术有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing single crystal diamond cutting tools are ground and passivated by grinding wheels. The material of the grinding wheel plays a very important role in the processing of the cutting tool, but the processing accuracy and efficiency of the existing grinding wheels are not high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present embodiment provides a kind of manufacturing method of grinding wheel, comprises the following steps:

[0022] S1) The following mass percentages of materials: abrasive 65%, adhesive 35%, are mixed and stirred evenly to form a mixed material: the abrasive is mixed with plastic raw material, diamond powder, and blue wax powder according to the following mass percentage: plastic raw material 61%, diamond powder 24%, blue wax powder 15%; plastic raw materials are hydrogenated nitrile rubber, polypropylene, medium alkali glass fiber mixed according to the following mass percentages: hydrogenated nitrile rubber 37%, polypropylene 31%, medium Alkali glass fiber 32%; binder is phenolic resin, furfural, dibutyl ester mixed according to the following mass percentage: phenolic resin 60%, furfural 23%, dibutyl ester 17%.

[0023] S2) inject the mixed material into the grinding wheel mold, and press to form a grinding wheel blank; specifically, preheat the temperature of...

Embodiment 2

[0028] The present embodiment provides a kind of manufacturing method of grinding wheel, comprises the following steps:

[0029] S1) Mix the following mass percentages of materials: 70% abrasive, 30% adhesive, and mix and stir evenly to form a mixed material; the abrasive is mixed with plastic raw material, diamond powder, and blue wax powder according to the following mass percentage: plastic powder 71%, diamond powder 18%, blue wax powder 11%; plastic raw materials are hydrogenated nitrile rubber, polypropylene, medium alkali glass fiber mixed according to the following mass percentages: hydrogenated nitrile rubber 42%, polypropylene 28%, medium Alkali glass fiber 30%; binder is phenolic resin, furfural, dibutyl ester mixed according to the following mass percentage: phenolic resin 65%, furfural 20%, dibutyl ester 15%.

[0030] S2) inject the mixed material into the grinding wheel mold, and press to form a grinding wheel blank; specifically, preheat the temperature of the gr...

Embodiment 3

[0035] The present embodiment provides a kind of manufacturing method of grinding wheel, comprises the following steps:

[0036] S1) The following mass percentages of materials: 75% of abrasives, 25% of adhesives, are mixed and stirred evenly to form a mixed material; the abrasives are mixed with plastic raw materials, diamond powder, and blue wax powder according to the following mass percentages: plastic powder 81%, diamond powder 12%, blue wax powder 7%; plastic raw materials are hydrogenated nitrile rubber, polypropylene, medium alkali glass fiber mixed according to the following mass percentages: hydrogenated nitrile rubber 47%, polypropylene 25%, medium Alkali glass fiber 28%; binder is phenolic resin, furfural, dibutyl ester mixed according to the following mass percentage: phenolic resin 70%, furfural 17%, dibutyl ester 13%.

[0037] S2) inject the mixed material into the grinding wheel mold, and press to form a grinding wheel blank; specifically, preheat the temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a material for manufacturing a grinding wheel and a manufacturing method for the grinding wheel. The material contains the following substances by weight percent: a grinding material and a binding material, wherein the grinding material is prepared by mixing the following substances by weight percent: plastic raw material, diamond powder and blue wax powder; the plastic raw material, the diamond powder and the blue wax powder are served as the grinding material; the plastic is formed by mixing hydrogenated nitrile rubber, polypropylene and medium alkali containing glass fiber; the hydrogenated nitrile rubber is suitable for higher temperature and is not adhered to a cutting tool under the effect of high temperature in a grinding process; the polypropylene is easily molded and has a certain adhesive effect; the medium alkali containing glass fiber is capable of increasing the hardness of the grinding wheel and bearing larger centrifugal acting force; the diamond powder can increase the grinding precision and grinding speed of the grinding wheel; the blue wax can enhance the polishing effect and increase the smoothness of the cutting tool. The grinding wheel prepared from the material is high in processing precision and smoothness in the passivation process of the cutting tool.

Description

technical field [0001] The invention relates to the technical field of grinding wheels, in particular to a material for making grinding wheels and a manufacturing method of grinding wheels. Background technique [0002] In the production process of knives, it is not only necessary to grind the blade of the knives to make the knives sharper, but also to passivate the knives. After the passivation treatment, the blade of the tool forms a rounded corner, which is not easy to crack, and the service life is increased. Existing single crystal diamond tools are ground and passivated by grinding wheels, and the material of the grinding wheels plays a very important role in the processing of the tools, while the existing grinding wheels have low machining accuracy and efficiency. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a material for making a grinding wheel and a method for manufacturing a grinding wheel, aiming ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B24B37/11B24D3/28B24D3/34B24D18/00C09K3/14
CPCB24B37/11B24D3/285B24D3/346B24D18/0009C09K3/1454
Inventor 陈朋跃窦明乾
Owner 深圳市鑫金泉精密技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap