Scratch-resistant aluminum alloy door window and preparation method thereof

A kind of aluminum alloy doors and windows, scratch-resistant technology, applied in the direction of coating, special surface, pretreatment surface, etc., can solve the problems of door and window surface being easily corroded, affecting the appearance and use, surface wear and so on

Inactive Publication Date: 2017-03-08
ANHUI KATA DOOR & WINDOW
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the currently commercially available aluminum alloy doors and windows are prone to surface wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) In parts by weight, 5 parts of glycerol, 5 parts of carbon black, 32 parts of propylene oxide, 41 parts of urea-formaldehyde resin, 5 parts of polyacrylamide and 11 parts of polyvinyl chloride with a weight average molecular weight of 70,000 are mixed to obtain a coating composition;

[0020] (2) The aluminum alloy door and window substrate is degreased with a soda ash solution with a pH value of 9 and sodium dodecylbenzenesulfonate in turn;

[0021] (3) Alternately washing the aluminum alloy door and window substrate after the degreasing treatment with water and ethanol, and the alternate washing is to first use water to wash;

[0022] (4) The coating composition was coated on the surface of the aluminum alloy door and window substrate after surface cleaning by multiple coating methods, and heated at a temperature of 110° C. for 35 minutes to prepare the scratch-resistant aluminum alloy door and window A1.

Embodiment 2

[0024] (1) In parts by weight, 5 parts of glycerol, 8 parts of carbon black, 40 parts of propylene oxide, 48 parts of urea-formaldehyde resin, 8 parts of polyacrylamide and 14 parts of polyvinyl chloride with a weight average molecular weight of 90,000 are mixed to obtain a coating composition;

[0025] (2) Degreasing the aluminum alloy door and window substrate with sodium silicate solution and fatty acid glyceride with a pH value of 13 in turn;

[0026] (3) Alternately washing the aluminum alloy door and window substrate after the degreasing treatment with water and ethanol, and the alternate washing is to first use water to wash;

[0027] (4) The coating composition was coated on the surface of the aluminum alloy door and window substrate after surface cleaning by multiple coating methods, and heated at a temperature of 130° C. for 50 min to obtain scratch-resistant aluminum alloy door and window A2.

Embodiment 3

[0029] (1) In parts by weight, 5 parts of glycerol, 6 parts of carbon black, 35 parts of propylene oxide, 45 parts of urea-formaldehyde resin, 7 parts of polyacrylamide and 13 parts of polyvinyl chloride with a weight average molecular weight of 80,000 are mixed to obtain a coating composition;

[0030] (2) Degreasing the aluminum alloy door and window substrate with sodium tripolyphosphate solution and sodium glycocholate with a pH value of 11 in turn;

[0031] (3) Alternately washing the aluminum alloy door and window substrate after the degreasing treatment with water and ethanol, and the alternate washing is to first use water to wash;

[0032] (4) The coating composition was coated on the surface of the aluminum alloy door and window substrate after surface cleaning by multiple coating methods, and heated at a temperature of 120° C. for 40 min to obtain scratch-resistant aluminum alloy door and window A3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a scratch-resistant aluminum alloy door window and a preparation method thereof. The preparation method includes: (1), mixing, by weight, 5 parts of glycerol, 4-8 parts of carbon black, 30-40 parts of epoxy propane, 40-50 parts of urea formaldehyde resin, 5-9 parts of polyacrylamide and 10-15 parts of polyvinyl chloride to obtain a coating composition; (2), sequentially using alkaline liquid and a surfactant to deoil an aluminum alloy door window matrix; (3), using alcohol and water to clean the surface of the deoiled aluminum alloy door window matrix; (4), coating the surface of the aluminum alloy door window matrix with the surface cleaned with the coating composition, and heating to obtain the scratch-resistant aluminum alloy door window. The scratch-resistant aluminum alloy door window prepared by the method has excellent mechanical performance, wear resistance and scratch resistance.

Description

technical field [0001] The invention relates to doors and windows, in particular to scratch-resistant aluminum alloy doors and windows and a preparation method thereof. Background technique [0002] Doors and windows are an important part of the building envelope structure system. According to their constituent materials, common doors and windows include wooden doors and windows, glass doors and windows, and aluminum alloy doors and windows. Wooden doors and windows are flammable, easy to deform, difficult to repair after being damaged, easy to crack, scar, poor corrosion resistance, susceptible to insects, etc., and prone to mildew when exposed to moisture. Glass doors and windows have fragile defects which limit their applications. Aluminum alloy doors and windows are widely used in industrial production because of their advantages such as not easy to rust, easy to process, relatively low price, light weight, and can be made into complex sections and structures. In additi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D161/24C09D127/06C09D7/12B05D7/14B05D3/10B05D5/00B05D3/02
CPCB05D3/0254B05D3/102B05D5/00B05D7/14B05D2202/25B05D2506/25B05D2518/00C08L2205/03C09D7/61C09D7/63C09D161/24C08L27/06C08L33/26C08K3/04C08K5/053
Inventor 洪长林
Owner ANHUI KATA DOOR & WINDOW
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap