Water-soluble blue jun porcelain glaze material and preparation method thereof

A water-soluble, blue technology, applied in the field of Jun porcelain, can solve the problems of poor wear resistance and mechanical resistance of the glaze surface, easy cracks on the surface of blue Jun porcelain glaze, difficult matching of finished products or complete sets, etc. The effect of transparency, strong mechanical resistance and less cracks

Inactive Publication Date: 2017-03-15
崔松伟
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Different enamel formulas lead to different firing colors, and when traditionally firing Jun porcelain, a layer of glaze is applied on the surface of the plain body. According to the firing environment in the kiln, the Jun glaze will change in the kiln, and some uncontrollable patterns will appear. Or color blocks, the finished products are difficult to match or configure as a set
[0005] In the prior art, there are few formulations and preparation methods of water-soluble blue enamel glazes, and the surface of the prepared blue enamel glazes is prone to cracks, the glaze surface has poor wear resistance and mechanical resistance, and the jade feeling is insufficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] A preparation method of the above-mentioned water-soluble blue Jun porcelain glaze, comprising the following steps:

[0020] (1) Pulverization: firstly take the calcite, quartz, sapphire, Hatoyama herbal medicine, copper ore, soda stone and talc powder in the above parts by weight and put them into a ball mill to pulverize them, mix them evenly and sieve to get the mixture powder;

[0021] (2) Smelting: Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney. There is also a supplementary dye room on the furnace. When the heat of the flue gas is insufficient or the kiln stops burning, That is to say, it can be roasted in a supplementary combustion chamber. There is a small hole at the bottom of the crucible, which is blocked with a hard quartz ball. The melt splits into crisp and transparent pieces;

[0022] (3) Grass and tree ash washing: Prepare several large tanks for washing, pour an appropriate ...

Embodiment 1

[0025] A water-soluble blue Jun porcelain glaze, which is made of the following raw materials in parts by weight: 0.7 parts of calcite, 30 parts of quartz, 10 parts of rudolite, 60 parts of Hatoyama herbal medicine, 3 parts of plant ash, and 0.3 parts of copper ore parts, 20 parts of soda stone, 2 parts of talcum powder, 35 parts of ammonium fluozirconate and 15 parts of zinc fluosilicate.

[0026] A preparation method of the above-mentioned water-soluble blue Jun porcelain glaze, comprising the following steps:

[0027] (1) Pulverization: firstly take the calcite, quartz, sapphire, Hatoyama herbal medicine, copper ore, soda stone and talc powder in the above parts by weight and put them into a ball mill to pulverize them, mix them evenly and sieve to get the mixture powder;

[0028] (2) Smelting: Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney. There is also a supplementary dye room on the furnace. ...

Embodiment 2

[0032] A water-soluble blue enamel glaze, which is made of the following raw materials in parts by weight: 1.0 parts of calcite, 40 parts of quartz, 15 parts of sapphire, 65 parts of Hatoyama herb, 4 parts of plant ash, and 0.4 parts of copper ore 30 parts, 30 parts of soda stone, 3 parts of talcum powder, 40 parts of ammonium fluozirconate and 20 parts of zinc fluosilicate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A water-soluble blue jun porcelain glaze material is prepared from, by weight, 0.5-1.0 part of calcite, 20-40 parts of quartz, 5-15 parts of blue stones, 55-65 parts of Hatoyama traditional Chinese medicine composition, 2-4 parts of plant ash, 0.2-0.4 part of copper ores, 10-30 parts of soda lime, 1-3 parts of talcum powder, 30-40 parts of ammonium fluozirconate and 10-20 parts of zinc fluosilicate. The prepared blue jun porcelain glaze material is very transparent, has stereo impression and good liquidity, does not easily blister and is good in gloss, and fired blue jun porcelain glaze is bright and smooth in color, contains few cracks and is strong in mechanical resistance capability.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain, and in particular relates to a water-soluble blue Jun porcelain glaze and a preparation method thereof. Background technique [0002] Jun porcelain is based on the thickness of the glaze. Its color is either sunken under the glaze, suspended in the glaze, or floating on the surface of the glaze. The glaze is thick and lively, and the glaze layer is opalescent and moist. Jun porcelain is transformed into a god by the kiln, and the natural transformation of the kiln is the essence of Jun porcelain art, and it is also the rarity of Jun porcelain that is famous all over the world and famous in the porcelain forest. The same kind of glaze is applied during firing, and once fired, it will be colorful, that is, "one color when entering the kiln, and many colors when leaving the kiln". The ever-changing kiln transformation effect forms the magic of infinitely changing colors, purple in red, dark b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 崔松伟
Owner 崔松伟