High-barrier degradable packaging material and preparation method thereof

A packaging material and high-barrier technology, applied in the field of packaging materials, can solve environmental damage and other problems, and achieve the effects of good degradation performance, excellent barrier performance, and good mechanical properties

Inactive Publication Date: 2017-03-15
汕头市东发印务有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the extensive use of packaging materials in recent years, most of which are refractory materials, which have caused serious damage to the environment. Therefore, on the basis of developing functional packaging materials and considering their degradability, research and development have a wider range of applications. Packaging Effective and environmentally friendly packaging materials have long-term value and significance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A high-barrier degradable packaging material, prepared from the following ingredients in parts by weight: 20 parts of polyethylene naphthalate, 20 parts of polypropylene carbonate, 10 parts of polycaprolactone, petroleum 2 parts of resin, 10 parts of ethylene-vinyl alcohol copolymer, 1 part of sodium montmorillonite, 1 part of nano-titanium dioxide, 0.5 parts of chitin, 2 parts of hydroxypropyl methylcellulose, 0.1 part of erucamide, stearic acid 0.2 parts of n-butyl ester, 0.5 parts of castor oil, and 2 parts of glycerin.

[0018] The preparation method of the above-mentioned easily degradable packaging material is:

[0019] (1) Polyethylene 2,6-naphthalate, polypropylene carbonate, polycaprolactone, petroleum resin, ethylene-vinyl alcohol copolymer, sodium montmorillonite, nano-titanium dioxide, chitin and The hydroxypropyl methylcellulose was mixed, and stirred for 3 minutes with a high-speed mixer at a speed of 600r / min;

[0020] (2) Add erucamide, n-butyl stearat...

Embodiment 2

[0024] A high-barrier degradable packaging material prepared from the following ingredients in parts by weight: 25 parts of polyethylene naphthalate, 30 parts of polypropylene carbonate, 11 parts of polycaprolactone, petroleum 3 parts of resin, 12 parts of ethylene-vinyl alcohol copolymer, 1.2 parts of sodium montmorillonite, 1.5 parts of nano-titanium dioxide, 0.6 parts of chitin, 2.5 parts of hydroxypropyl methylcellulose, 0.15 parts of erucamide, stearic acid 0.3 parts of n-butyl ester, 0.6 parts of castor oil, and 3 parts of glycerol.

[0025] The preparation method of the above-mentioned easily degradable packaging material is:

[0026] (1) Polyethylene 2,6-naphthalate, polypropylene carbonate, polycaprolactone, petroleum resin, ethylene-vinyl alcohol copolymer, sodium montmorillonite, nano-titanium dioxide, chitin and The hydroxypropyl methylcellulose was mixed, and stirred for 4 minutes with a high-speed mixer at a speed of 650r / min;

[0027] (2) Add erucamide, n-buty...

Embodiment 3

[0031] A high-barrier degradable packaging material prepared from the following ingredients in parts by weight: 30 parts of polyethylene-2,6-naphthalate, 35 parts of polypropylene carbonate, 12.5 parts of polycaprolactone, petroleum 3.5 parts of resin, 15 parts of ethylene-vinyl alcohol copolymer, 1.5 parts of sodium montmorillonite, 2 parts of nano-titanium dioxide, 0.75 parts of chitin, 3 parts of hydroxypropyl methylcellulose, 0.2 parts of erucamide, stearic acid 0.35 parts of n-butyl ester, 0.75 parts of castor oil, and 3.5 parts of glycerin.

[0032] The preparation method of the above-mentioned easily degradable packaging material is:

[0033] (1) Polyethylene 2,6-naphthalate, polypropylene carbonate, polycaprolactone, petroleum resin, ethylene-vinyl alcohol copolymer, sodium montmorillonite, nano-titanium dioxide, chitin and The hydroxypropyl methylcellulose was mixed, and stirred for 4 minutes with a high-speed mixer at a speed of 700r / min;

[0034] (2) Add erucamide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Transmittanceaaaaaaaaaa
Weight loss rateaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-barrier degradable packaging material and a preparation method thereof. The preparation method comprises the following steps that 1, 2,6-naphthalic acid glycol ester, polypropylene carbonate, polycaprolactone, petroleum resin, an ethylene-ethenol copolymer, sodium-based montmorillonite, nano titanium dioxide, chitin and hydroxypropyl methyl cellulose are mixed and are stirred with a high-speed mixer; 2, erucyl amide, n-butyl stearate, castor oil and glycerol are added, and stirring continues by using the high-speed mixer; 3, the mixture is charged into a double-screw extruder for extrusion and granulation; 4, blow-molding is performed with a blow-molding machine after cooling. The high-barrier degradable packaging material has good mechanical properties, excellent barrier performance, meanwhile has good degradation performance and is green and environmentally friendly.

Description

technical field [0001] The invention relates to the field of packaging materials, in particular to a high-barrier degradable packaging material and a preparation method thereof. Background technique [0002] With the development of society and the improvement of people's living standards, the classification of products is becoming more and more detailed. The packaging of products is not only limited to the basic functions of protecting products, but also according to the characteristics of products and market demand, towards visual and Development in the direction of functionalization. In recent years, with the advancement of technology, the functional development trend of packaging materials has become increasingly obvious. High-demand, high-tech packaging materials are becoming the pillar industry and research and development goals of many companies. Their packaging functions are diverse, except for the most basic In addition to the requirements, the packaging material ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/02C08L69/00C08L67/04C08L57/02C08L23/08C08L5/08C08L1/28C08L91/00C08K13/02C08K3/34C08K3/22C08K5/20C08K5/053B65D65/46
CPCB65D65/466C08K2201/011C08L67/02C08L69/00C08L2201/06C08L2205/02C08L2205/035C08L67/04C08L57/02C08L23/0861C08L5/08C08L1/284C08L91/00C08K13/02C08K3/346C08K2003/2241C08K5/20C08K5/053Y02W90/10
Inventor 金福兴
Owner 汕头市东发印务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com