Composite mica paper and preparation method thereof
A kind of technology of compound mica and mica paper
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] 1) Mix mica powder (120 mesh), urea-formaldehyde resin (weight-average molecular weight: 5,000), glass fiber (length: 0.3mm), polyacrylamide, ethylenediaminetetraacetic acid, and water in a weight ratio of 200:30: Stir and mix at 10:5:5:100 to make mica pulp; finally, make mica paper from the obtained mica pulp, and the mica paper is a mica layer; before 1), wash the mica with water with a liquid-solid ratio of 4 slices until the turbidity of water is 11°, and washed 3 times with water.
[0023] 2) earlier novolac epoxy resin (weight-average molecular weight is 20,000), polyimide resin (weight-average molecular weight is 30,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water Mix according to the weight ratio of 100:50:10:1:1:100, then perform heat treatment at 180° C. for 1.5 hours, and finally extrude to obtain a resin layer.
[0024] 3) The prepared mica paper was placed on the prepared resin layer, and at 170°C, the pressure was selected to ...
Embodiment 2
[0026] 1) Mix mica powder (180 mesh), urea-formaldehyde resin (weight-average molecular weight: 20,000), glass fiber (length: 0.5mm), polyacrylamide, ethylenediaminetetraacetic acid, and water in a weight ratio of 220:33: Stir and mix at 15:7:8:100 to make mica pulp; finally make mica paper from the obtained mica pulp, and the mica paper is a mica layer; before 1), wash the mica with water with a liquid-solid ratio of 5 slices until the turbidity of water is 10°, and washed 3 times with water.
[0027] 2) earlier novolac epoxy resin (weight-average molecular weight is 30,000), polyimide resin (weight-average molecular weight is 40,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water The mixture was mixed according to the weight ratio of 100:80:13:3:3:130, followed by heat treatment at 190° C. for 1.0 h, and finally extruded to obtain a resin layer.
[0028] 3) Place the prepared mica paper on top of the prepared resin layer, heat press and compound at ...
Embodiment 3
[0030] 1) Mix mica powder (200 mesh), urea-formaldehyde resin (weight-average molecular weight: 25,000), glass fiber (length: 0.6mm), polyacrylamide, ethylenediaminetetraacetic acid, and water in a weight ratio of 250:35: Stir and mix at 20:10:9:100 to make mica pulp; finally make mica paper from the obtained mica pulp, and the mica paper is a mica layer; before 1), wash the mica with water with a liquid-solid ratio of 6 Slice until the turbidity of water is 11°, and wash 2 times with water.
[0031] 2) earlier novolac epoxy resin (weight-average molecular weight is 40,000), polyimide resin (weight-average molecular weight is 50,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water Mixing according to the weight ratio of 100:95:15:5:5:150, followed by heat treatment at 200°C for 0.5h, and finally extrusion molding to obtain a resin layer.
[0032] 3) Place the prepared mica paper on top of the prepared resin layer, heat press and compound at 175° C. wit...
PUM
Property | Measurement | Unit |
---|---|---|
size | aaaaa | aaaaa |
length | aaaaa | aaaaa |
length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com