Anti-microbial TPU material and preparing method thereof

An antibacterial agent and raw material technology, applied in the field of antibacterial TPU material and its preparation, can solve the problems that cannot be widely used, TPU material does not have antibacterial and bactericidal properties, etc., to promote widespread use, high antibacterial and antifungal properties, tear high intensity effect

Inactive Publication Date: 2017-03-29
SHANDONG FANGDING SAFETY GLASS TECH CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the TPU material itself does not have antibacterial and bactericidal p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] In the embodiment of the present invention, an antibacterial TPU material, the raw materials according to weight parts include: 1 part of polyether polyol, 15 parts of isocyanate, 3 parts of chain extender, 10 parts of polyamide, 0.5 part of antibacterial agent, polyethylene glycol 5 parts, antifungal agent 0.1 part, antioxidant 0.05 part, organic bismuth 1 part, antiblocking agent 0.1 part, filler 0.1 part.

[0018] The number average molecular weight of polyethylene glycol is 1000-5000. The chain extender is ethylene glycol.

[0019] A kind of preparation method of antibacterial TPU material, comprises the following steps:

[0020] 1) Weigh polyether polyol, isocyanate, chain extender, polyamide, antibacterial agent, polyethylene glycol, antifungal agent, antioxidant, organic bismuth, antiblocking agent, filler, and mix uniformly by weight ;

[0021] 2) Dry the mixture obtained in step 1), and then extrude it in a casting machine to obtain an antibacterial TPU mate...

Embodiment 2

[0023] In the embodiment of the present invention, an antibacterial TPU material, the raw materials according to weight parts include: 15 parts of polyether polyol, 55 parts of isocyanate, 25 parts of chain extender, 35 parts of polyamide, 6 parts of antibacterial agent, polyethylene glycol 40 parts, 5 parts of antifungal agent, 4 parts of antioxidant, 15 parts of organic bismuth, 8 parts of anti-blocking agent, 20 parts of filler. The number average molecular weight of polyethylene glycol is 1000-5000. The chain extender is 1,3-propanediol.

[0024] A kind of preparation method of antibacterial TPU material, comprises the following steps:

[0025] 1) Weigh polyether polyol, isocyanate, chain extender, polyamide, antibacterial agent, polyethylene glycol, antifungal agent, antioxidant, organic bismuth, antiblocking agent, filler, and mix uniformly by weight ;

[0026] 2) Dry the mixture obtained in step 1), and then extrude it in a casting machine to obtain an antibacterial ...

Embodiment 3

[0028] In the embodiment of the present invention, an antibacterial TPU material, the raw materials according to weight parts include: 2 parts of polyether polyol, 20 parts of isocyanate, 4 parts of chain extender, 12 parts of polyamide, 0.8 part of antibacterial agent, polyethylene glycol 8 parts, 0.2 parts of antifungal agent, 0.08 parts of antioxidant, 2 parts of organic bismuth, 0.2 parts of anti-blocking agent, and 0.5 parts of filler. The number average molecular weight of polyethylene glycol is 1000-5000. The chain extender is 1,4-butanediol.

[0029] A kind of preparation method of antibacterial TPU material, comprises the following steps:

[0030] 1) Weigh polyether polyol, isocyanate, chain extender, polyamide, antibacterial agent, polyethylene glycol, antifungal agent, antioxidant, organic bismuth, antiblocking agent, filler, and mix uniformly by weight ;

[0031] 2) Dry the mixture obtained in step 1), and then extrude it in a casting machine to obtain an antiba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-microbial TPU material and a preparing method thereof. The anti-microbial TPU material comprises raw materials including, by weight, 1-15 parts of polyether polyol, 15-55 parts of isocyanate, 3-25 parts of a chain extender, 10-35 parts of polyamide, 0.5-6 parts of an anti-microbial agent, 5-40 parts of polyethylene glycol, 0.1-5 parts of a mildew preventive, 0.05-4 parts of an antioxidant, 1-15 parts of organic bismuth, 0.1-8 parts of an antiblocking agent and 0.1-20 parts of a filler. The above raw materials are weighed according to the parts by weight and are evenly mixed; and an obtained mixture is dried, and extrusion is carried out in a casting machine to obtain the anti-microbial TPU material. The anti-microbial TPU material has the technical advantages of high abrasive resistance, good elastic toughness, high hydrolytic resistance, high hardness, high yellowing resistance, high transparency, high tearing strength and the like; the anti-microbial agent, the mildew preventive, the antioxidant and the antiblocking agent are added, and therefore the anti-microbial TPU material has the beneficial effect of being high in anti-microbial and mildew-preventing performance, and wide application of the TPU material in the field with high anti-microbial requirements is promoted; and the anti-microbial TPU material and the preparing method have the wide market prospect.

Description

technical field [0001] The invention relates to the technical field of thermoplastic polyurethane elastomer materials, in particular to an antibacterial TPU material and a preparation method thereof. Background technique [0002] Thermoplastic polyurethane elastomer (TPU) is a kind of elastomer that can be plasticized by heating and can be dissolved by solvent. It has excellent comprehensive properties such as high strength, high toughness, wear resistance, and oil resistance. It has good processing performance and is widely used in national defense, medical treatment, Food and other industries. Thermoplastic polyurethane elastomer, with its excellent performance and wide application, has become one of the important thermoplastic elastomer materials, its molecules are basically linear, with no or little chemical crosslinking. There are many physical cross-links formed by hydrogen bonds between the linear polyurethane molecular chains, and the hydrogen bonds strengthen its s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/66C08G18/48C08G18/65C08G18/60C08G18/32
CPCC08G18/6674C08G18/3206C08G18/4054C08G18/4808C08G18/4833C08G18/603C08G18/6511
Inventor 王超
Owner SHANDONG FANGDING SAFETY GLASS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap