Preparation method and application of heat-transfer printing silicone film and heat-transfer printing silicone membrane

A technology of silicone film and thermal transfer printing, applied in transfer printing, rotary printing machine, printing, etc., can solve the problems of limiting the application of silicone, and achieve the effect of solving poor firmness

Inactive Publication Date: 2017-03-29
广东省良展有机硅科技有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The thermal transfer process is a method that can quickly mass-print printing production. However, it is difficult to print silicone products on conventional thermal transfer products. Therefore, the application of silicone in this field is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: a kind of preparation method of thermal transfer printing silica gel film of the present invention, it comprises the following steps:

[0024] (1) Select a hot-melt adhesive film that melts between 120°C and 150°C;

[0025] (2) Prepare the coating silica gel, which is made by mixing the following components in parts by mass: 90 parts of two-component addition type liquid silica gel, 0.01 part of aluminate coupling agent, hydroxyhydrocarbyl modified polysiloxane 2-5 parts of alkane, 0.5 parts of linear methyl hydrogen silicone oil, 0.005 parts of platinum catalyst, 2-5 parts of epoxy modified silicone resin, 2.5 parts of toluene;

[0026] (3) Use a coating machine to coat the coating silica gel on the hot melt adhesive film to a thickness of 5-10 filaments, and dry it in an oven to obtain a thermal transfer printing silica gel film.

[0027] The hot melt adhesive film is a polyurethane film, and the thickness of the polyurethane film is 0.2 mm to 0.5 mm. ...

Embodiment 2

[0034] Embodiment 2: This embodiment is substantially the same as Embodiment 1, except that the coating silica gel is made by mixing the following components in parts by mass: 90 parts of two-component addition type liquid silica gel, aluminate 0.01 part of joint agent, 2 parts of hydroxyhydrocarbyl modified polysiloxane, 0.5 part of linear methyl hydrogen silicone oil, 0.005 part of platinum catalyst, 5 parts of epoxy modified silicone resin, and 2.5 parts of toluene.

Embodiment 3

[0035] Example 3, this example is basically the same as Example 1, except that the coating silica gel is made by mixing the following components in parts by mass: 90 parts of two-component addition type liquid silica gel, aluminate coupling 0.01 parts of agent, 3 parts of hydroxyhydrocarbyl modified polysiloxane, 0.5 parts of linear methyl hydrogen silicone oil, 0.005 parts of platinum catalyst, 3 parts of epoxy modified silicone resin, and 2.5 parts of toluene.

[0036] The heat transfer printing silicone film of the present invention is a composite film of silica gel and hot melt adhesive, which not only solves the problem of low efficiency when hot melt adhesive is used in current heat transfer printing, but also solves the problem of low efficiency when the silicone film is directly printed on ordinary heat transfer printing. The problem of poor printing firmness on the melt adhesive film allows silicone printing to be used for heat transfer printing in large quantities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a heat-transfer printing silicone film; the preparation method comprises the steps of (1) selecting hot-melt film, and melting the hot-melt film at 120 DEG C to 150 DEG C; (2) blending coating silicone that is made by mixing, by weight, 90 parts of bicomponent additional liquid silicone, 0.01 part of aluminate coupler, 2-5 parts of hydroxyalkyl modified silane, 0.5 part of linear methyl hydrogen silicone oil, 0.005 part of metal platinum catalyst, 2-5 parts of epoxy modified silicon resin, and 2.5 parts of toluene; (3) applying coating silicone to the hot-melt film to 5-10 si in thickness, and the heat-transfer printing silicone film is prepared by drying. Heat-transfer printing silicone film and application thereof are also disclosed. The problem that efficiency is low since hot-melt silicone used in current heat-transfer printing ins only suitable for single-sheet printing is solved, the problem that print durability is poor due to silicone being directly on common hot-melt silicone film is also solved, and silicone printing is suitable for batched heat-transfer printing.

Description

technical field [0001] The invention relates to the field of screen printing, in particular to a method for preparing a heat transfer printing silica gel film, an application of the heat transfer printing silica gel film and the heat transfer printing silica gel film. Background technique [0002] In the field of printing, silicone printing has been favored and recognized by more and more users because of its environmental protection, soft touch and various effects, and its market share has steadily increased. However, compared with conventional glue printing, due to the slower printing speed and lower efficiency, the market share of silicone printing is still small, so technology development and production process upgrading are relatively slow. [0003] At present, the printing field is in the process of shifting from manual production to semi-automatic production. Since the substrates for silicone printing vary greatly, and the demand is generally not very large, in order...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L83/06C08L83/05C08K5/10C08J7/04B41F16/00B41F16/02
CPCB41F16/00B41F16/02C08J7/0427C08J2375/04C08J2483/04C08L83/04C08L2205/025C08L2205/035C08L83/06C08K5/10
Inventor 尹清权王征乔梁王志良
Owner 广东省良展有机硅科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap