Spread ceramic surface sintered silver paste and preparation method thereof

A ceramic surface and smear-type technology, which is applied in the field of ceramic surface processing, can solve the problems of not being able to meet the needs of the public and high cost, and achieve the effects of low cost, safe use, and simple manufacturing process

Active Publication Date: 2017-05-10
河北银瓷天成文化传播有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the application of silver in catering utensils is mostly directly ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] A smear-type ceramic surface sintered silver paste, which includes the following components in parts by weight: 45 parts of silver powder, 3 parts of sodium alginate, 2 parts of glass powder, 20 parts of polyethylene glycol, and 8 parts of sucrose isobutyrate , 1 part of rosin acid, 3 parts of pinitol oil, 20 parts of water.

[0018] The particle size of the silver powder is 0.2-1 μm.

[0019] The preparation method of the glass powder is as follows: Weigh the raw material according to the following mass percentage: SiO 2 15%, BaO 40%, TiO 2 30%, ZnO 9%, K 2 O 3.99%, B 2 O 3 2%, NiO0.01%, mixed uniformly, melted at 1200-1300℃ for 2 hours to obtain a glass liquid. The glass liquid is quenched in water at 10-20℃, dried and ball milled in a ball mill for 12 hours. Glass powder.

[0020] The preparation method of the smeared ceramic surface sintered silver paste is as follows: dissolve sodium alginate in water, add polyethylene glycol and stir evenly, record it ...

Example Embodiment

[0021] Example 2

[0022] A smear type ceramic surface sintered silver paste, which includes the following components in parts by weight: 50 parts of silver powder, 2 parts of sodium alginate, 15 parts of polyethylene glycol, 5 parts of sucrose isobutyrate, 2 parts of rosin acid , 4 parts of pinitol oil, 22 parts of water.

[0023] The particle size of the silver powder is 0.2-1 μm.

[0024] The preparation method of the glass powder is as follows: Weigh the raw material according to the following mass percentage: SiO 2 20%, BaO 30%, TiO 2 40%, ZnO 3%, K 2 O 5%, B 2 O 3 1.98%, NiO0.02%, mixed uniformly, melted at 1200-1300℃ for 3 hours to obtain glass liquid, then the glass liquid is quenched in water at 10-20℃, dried and then ball milled in a ball mill for 12 hours. Glass powder.

[0025] The preparation method of the smeared ceramic surface sintered silver paste is as follows: dissolve sodium alginate in water, add polyethylene glycol and stir evenly, record it as liquid A, dissolv...

Example Embodiment

[0026] Example 3

[0027] A smear type ceramic surface sintered silver paste, which includes the following components in parts by weight: 55 parts of silver powder, 3 parts of sodium alginate, 18 parts of polyethylene glycol, 7 parts of sucrose isobutyrate, and 1 part of rosin acid , 5 parts of pinitol oil, 25 parts of water.

[0028] The particle size of the silver powder is 0.2-1 μm.

[0029] The preparation method of the glass powder is as follows: Weigh the raw material according to the following mass percentage: SiO 2 18%, BaO 32%, TiO 2 35%, ZnO 3.98%, K 2 O 2%, B 2 O 3 9%, NiO0.02%, mixed uniformly, melted at 1200-1300℃ for 2 hours to obtain a glass liquid. The glass liquid is quenched in water at 10-20℃, dried and then ball milled in a ball mill for 12 hours. Glass powder.

[0030] The preparation method of the smeared ceramic surface sintered silver paste is as follows: dissolve sodium alginate in water, add polyethylene glycol and stir evenly, record it as liquid A, dissolv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses spread ceramic surface sintered silver paste, which comprises the following components in parts by weight: 45 to 55 parts of silver powder, 2 to 3 parts of sodium alginate, 2 to 3 parts of glass powder, 15 to 20 parts of polyethylene glycol, 5 to 8 parts of sucrose isobutyrate, 1 to 2 parts of an abietic acid, 3 to 5 parts of terpenic oil and 20 to 25 parts of water. A preparation method comprises the following steps: adding the silver powder into the water, adding the sodium alginate and the polyethylene glycol with stirring at 200 to 300rpm, and continuing stirring for 15 to 20min to obtain a solution A; dissolving the abietic acid into the terpenic oil, adding the sucrose isobutyrate, and performing uniform stirring to obtain a solution B; adding the solution B into the solution A, and performing stirring for 1 to 2h at 500 to 600rpm. According to the silver paste, the raw materials are readily available, a preparation process is simple, the silver paste is relatively low in cost, free of heavy metals, safe in use, green and environment-friendly, and no harmful gas is generated during sintering.

Description

technical field [0001] The invention relates to the technical field of ceramic surface processing, in particular to a smear-type ceramic surface sintered silver paste and a preparation method thereof. Background technique [0002] Silver is a kind of precious metal that people love. It has good decorative properties and is one of the most commonly worn decorations. In addition, silver also has bactericidal properties, so silver has begun to be applied to dining utensils to play It has the functions of disinfection, sterilization and preservation. [0003] At present, the application of silver in catering utensils is mostly directly made into cups, bowls, etc., which is relatively expensive and cannot meet the needs of the public. Using ceramic ware as a base and coating it with a silver layer can reduce the cost and give full play to the decorative and functional properties of silver. It has become the main direction of silver application in catering utensils. Contents of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/88C03C8/04
CPCC03C8/04C04B41/009C04B41/5116C04B41/88C04B41/5022C04B41/4803C04B41/4896C04B41/46C04B41/474C04B35/00
Inventor 任云王博杨儒林王天星
Owner 河北银瓷天成文化传播有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap