Anion glaze, blank, preparation method and application thereof

A technology of negative ions and negative ion powder, which is applied in the field of ceramics, can solve the problems of weak health care function, weak ability to release negative ions, and sacrifice the ornamental quality of ceramic products, etc., to achieve the effect of rich colors and strong health care functions

Active Publication Date: 2017-05-17
江苏地球蓝环保科技有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But above-mentioned two kinds of solutions have the defects that the cost is too high and the appreciation of ceramic products is sacrificed.
[0005] In addition, most of the ceramic products on the market are simply used as utensils, for example, to hold food, and their functions are relatively single, which cannot meet the needs of consumers for health care functions.
At present, there are also negative ion ceramic products on the market, but their ability to release negative ions is weak and their health care functions are not strong.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion glaze, blank, preparation method and application thereof
  • Anion glaze, blank, preparation method and application thereof
  • Anion glaze, blank, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The present invention also relates to a preparation method of the above-mentioned negative ion glaze, which comprises mixing small red mud, feldspar, calcite, negative ion generating agent and zeolite.

[0047] The present invention also relates to the application of the above-mentioned anion glaze in preparing ceramic products.

[0048] In the above application of the present invention, the negative ion glaze is used to prepare ceramic products, and the ceramic products prepared by the glaze are lead-free, chromium-polluted, rich in color and have health care functions.

[0049] The invention also relates to an anion blank, which comprises the following components: purple sand mud, feldspar, calcite, kaolin, and anion generating agent.

[0050] Zisha mud, also known as "five-color soil", has a variety of colors, including purple, black, green, yellow, azure and reddish brown. Because the blank includes purple sand mud, the green blank fired from the blank according to...

Embodiment 1

[0092] 1. Preparation of green body

[0093] Prepare the blank by the following parts by weight: 47 parts of purple sand mud, 15 parts of feldspar, 7 parts of calcite, 3.2 parts of kaolin, 18 parts of hexacyclic stone, negative ion powder (nano-level, negative ion generation: 50000ions / cm 3 ) 9.8 copies.

[0094] The preparation method of the biscuit includes the following steps: crushing and mixing the components of the above-mentioned raw materials respectively, adding water with 60% of the total weight of the raw materials for ball milling, passing through a 40-mesh sieve, sedimentation, pressure filtration, and placing in a slurry storage tank Store the slurry in the storage tank for later use, then take out the slurry from the slurry storage tank, put it into a vacuum mud refining machine to practice mud, remove water, and then conduct a second mud refining to obtain a plastic billet, which is extruded by a vacuum extrusion molding machine. After drying and molding, it i...

Embodiment 2

[0099] The glaze is prepared according to the following parts by weight: 35 parts of small red mud, 28 parts of feldspar, 16 parts of calcite, 10 parts of hexacyclic stone, negative ion powder (nano-level, negative ion generation: 50000ions / cm 3 ) 15 parts, 6 parts of zeolite.

[0100] The blank was prepared with reference to the blank formula described in Example 1, and the biscuit and glaze were prepared with reference to the method described in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anion glaze, a blank, a preparation method and an application thereof. The anion glaze provided by the invention comprises the following components: red mud, feldspar, calcite, anion generating agent and zeolite, wherein the anion generating agent is added, so that the glaze can release anion; the red mud is added, so that the ceramics can have bright and abundant colors under the condition that no pigment is used; meanwhile, the red mud also can promote the mixing of the anion generating agent in the glaze. According to the invention, the purple grit mud and the anion generating agent added into the glaze also have the functions of supplying abundant colors and releasing anions. Thus, the glaze provided by the invention and the ceramics prepared from the glaze have the advantages of non-toxicity, high ornamental value and healthcare function.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to an anion glaze, a blank, a preparation method and application thereof. Background technique [0002] Ceramic products are indispensable daily necessities in people's daily life. With the improvement of living standards, consumers have higher and higher requirements for the safety, aesthetics and health care of ceramic products, and hope that the three can be achieved at the same time. [0003] The safety problem of daily-use ceramics mainly lies in that the content of lead and chromium exceeds the standard, which is easy to dissolve from ceramic products and endanger human health. The main sources of heavy metals such as lead and chromium in ceramics are: first, lead or lead oxide is used as a flux in the glazing process of ceramic products, so that lead exists in the glaze and there is a risk of dissolution; second, in order to keep the color bright and not fade, Many pigments used in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C03C8/00C04B33/34C04B41/86
CPCC03C8/00C04B33/13C04B33/34C04B41/5022C04B41/86C04B2235/3208C04B2235/3272C04B2235/3463C04B2235/96C04B41/4539C04B41/0072
Inventor 孙古桂孙丽军钱培楼
Owner 江苏地球蓝环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com