A kind of diatom mud of roll coating type and preparation method thereof

A diatom mud, roll-coating technology, applied in the field of architectural coatings, can solve the problems of reducing the amount of diatom earth, reducing the function of diatom mud, and cumbersome construction, etc., to achieve a strong three-dimensional effect

Active Publication Date: 2018-10-26
SHANDONG CUIBAO NEW MATERIAL TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The amount of diatomaceous earth is reduced, the functional materials are reduced, and the function of diatom mud is greatly reduced. The construction in the existing technology is cumbersome and must be operated by a professional construction team to obtain the required decorative effect. A roll-on diatom ooze that is simple in construction and does not affect the function of diatom ooze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A roll-coating type diatom mud is composed of the following components in parts by weight: 32 parts of diatomite, 5.5 parts of potato flour, 0.4 part of cellulose, 9 parts of talcum powder, 8 parts of kaolin, attapulgite powder 6 parts, 10 parts of titanium dioxide, 6 parts of heavy calcium carbonate, 8 parts of white carbon black, 10 parts of medical stone, 10 parts of ash calcium powder, 2 parts of wood fiber, 10 parts of sepiolite powder, 3 parts of negative oxygen ion powder , 0.3 parts of powder antifungal agent, 0.3 parts of powder defoamer

[0062] The preparation method of above-mentioned roll coating type diatom mud:

[0063] 1: first suck the diatomite into the grinder, grind it, and pass it through an 80-mesh sieve for later use;

[0064] 2: 32 parts of diatomite after grinding, 5.5 parts of potato powder, 0.4 part of cellulose, 9 parts of talcum powder, 8 parts of kaolin, 6 parts of attapulgite powder, 10 parts of titanium dioxide, 6 parts of heavy calcium ...

Embodiment 2

[0070] A roll-coating type diatom mud is composed of the following components in parts by weight: 35 parts of diatomite, 6.3 parts of potato flour, 0.3 part of cellulose, 2 parts of talcum powder, 10 parts of kaolin, attapulgite powder 4 parts, 5 parts of titanium dioxide, 10 parts of heavy calcium carbonate, 2 parts of white carbon black, 4 parts of medical stone, 10 parts of ash calcium powder, 1 part of wood fiber, 5 parts of pumice powder, 5 parts of negative oxygen ion powder, 0.2 parts of powder antifungal agent, 0.2 parts of powder defoamer.

[0071] The preparation method of above-mentioned roller coating type diatom mud:

[0072] 1: first suck the diatomite into the grinder, grind it, and pass it through an 80-mesh sieve for later use;

[0073] 2: 35 parts of diatomite after grinding, 6.3 parts of potato powder, 0.3 part of cellulose, 2 parts of talcum powder, 10 parts of kaolin, 4 parts of attapulgite powder, 5 parts of titanium dioxide, 10 parts of heavy calcium ca...

Embodiment 3

[0080] A roll-coating type diatom mud is composed of the following components in parts by weight: 40 parts of diatomite, 15 parts of potato flour, 0.5 part of cellulose, 12 parts of talcum powder, 5 parts of kaolin, attapulgite powder 10 parts, 18 parts of titanium dioxide, 18 parts of heavy calcium carbonate, 8 parts of white carbon black, 12 parts of medical stone, 18 parts of ash calcium powder, 3 parts of wood fiber, 15 parts of sepiolite powder, 10 parts of negative oxygen ion powder , 0.5 parts of powder antifungal agent, 0.5 parts of powder defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of building coatings, in particular to roller coating type diatom ooze and a preparation method thereof. The roller coating type diatom ooze is prepared from the following components in parts by weight: 35 parts of diatomite, 6.3 parts of dried potato powder, 0.3 part of cellulose, 2 parts of talcum powder, 10 parts of kaolin, 4 parts of attapulgite powder, 5 parts of titanium dioxide, 10 parts of heavy calcium carbonate, 2 parts of white carbon black, 4 parts of medical stone, 10 parts of ash calcium powder, 1 part of wood fiber, 5 parts of afrodite powder, 5 parts of negative oxygen ion powder, 0.2 part of powdery mildew preventive and 0.2 part of powder defoaming agent. The diatom ooze disclosed by the invention has the advantages of weak base, mildew resistance, nature, environmental protection, high content of the diatomite, high adsorption capacity and high stability; the industry limit is broken; a product has the effects of releasing negative ions, removing formaldehyde, and purifying and refreshing air.

Description

technical field [0001] The invention relates to the technical field of architectural coatings, in particular to a roll-coating type diatom mud and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the requirements for the living environment are also getting higher and higher. From meeting the basic living needs to reflecting the personality and taste of the owner. The demand for personalization and quality is increasingly strong, so that people's home decoration is not only to meet the needs of beauty, but also home decoration is no longer the same. changes in demand. [0003] Diatom mud is an interior decoration material with diatom earth as the main raw material. The main reason why diatom mud can function is to maintain the maximum degree of naturalness of diatom mud, which can automatically adjust the indoor temperature. The amount of diatomite is reduced, the functional materials are reduced, and the functi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B30/02
CPCC04B30/02C04B2111/00025C04B2111/00482C04B14/08C04B24/38C04B24/383C04B14/042C04B14/106C04B14/102C04B14/305C04B14/28C04B14/06C04B14/04C04B22/062C04B18/24C04B2103/67C04B2103/50
Inventor 姜成民穆宝翠袁秀芳马道芹
Owner SHANDONG CUIBAO NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com