A PVC resin and cable sheathing technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of environmental cracking resistance, high and low temperature resistance and weather resistance, internal transmission medium leakage, long service life of rubber, etc. Problems, to achieve the effect of good thermal stability, poor thermal conductivity and good extensibility

Inactive Publication Date: 2018-05-18
南京化学工业园环保产业协同创新有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Rubber is a highly elastic polymer material with reversible deformation. It is elastic at room temperature. It can produce a large deformation under the action of a small external force, and it can return to its original shape after the external force is removed. During use, due to friction with other objects, resulting in The surface of the rubber is damaged or even loses its original performance, and the rubber is used for too long, and the aging speed becomes faster, especially the wear and erosion of the rubber pipeline, which will lead to the leakage of the internal transmission medium, and under extreme conditions, Environmental cracking resistance, high and low temperature resistance and weather resistance are poor, and it is not easy to degrade after being discarded and buried, polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An environment-friendly PVC resin cable sheath material, comprising the following raw materials in parts by weight: 80 parts of PVC resin, 35 parts of nanofiber, 12 parts of modified nylon material, 1.25 parts of sulfur powder, 52 parts of white carbon black, and 18 parts of nano-active calcium carbonate 18 parts of silica powder, 15 parts of boron carbide, 19 parts of glass wool, 35 parts of nano silicon dioxide, 32.5 parts of organic bentonite, 1.75 parts of methyl silicone oil, 0.75 parts of anti-aging agent MB, 1 part of antioxidant 3114, anti-aging RD 1.2 parts, 2.2 parts of accelerator CZ, 1.8 parts of accelerator D, 0.5 parts of compatibilizer, 0.4 parts of hindered amine light stabilizer, 0.6 parts of inorganic binder, 2.25 parts of barium stearate and 2.5 parts of zinc oxide;

[0030] Among them, the modified nylon material is prepared by the following process: mix 0.3-0.6 parts of resorcinol, 2-3 parts of formaldehyde, 6-12 parts of water and 23-26 parts of car...

Embodiment 2

[0036] An environmentally friendly PVC resin cable sheath material, comprising the following raw materials in parts by weight: 70 parts of PVC resin, 30 parts of nanofiber, 10 parts of modified nylon material, 1 part of sulfur powder, 50 parts of white carbon black, and 12 parts of nano-active calcium carbonate 12 parts of silica powder, 10 parts of boron carbide, 15 parts of glass wool, 30 parts of nano-silica, 30 parts of organic bentonite, 1.5 parts of methyl silicone oil, 0.5 parts of anti-aging agent MB, 0.8 parts of antioxidant 3114, anti-aging RD 1 part, 2 parts of accelerator CZ, 1.6 parts of accelerator D, 0.4 parts of compatibilizer, 0.3 parts of hindered amine light stabilizer, 0.4 parts of inorganic binder, 1.5 parts of barium stearate and 2 parts of zinc oxide;

[0037]Among them, the modified nylon material is prepared by the following process: mix 0.3-0.6 parts of resorcinol, 2-3 parts of formaldehyde, 6-12 parts of water and 23-26 parts of carboxylated styrene-b...

Embodiment 3

[0043] An environment-friendly PVC resin cable sheath material, comprising the following raw materials in parts by weight: 90 parts of PVC resin, 40 parts of nanofiber, 14 parts of modified nylon material, 1.5 parts of sulfur powder, 54 parts of white carbon black, and 24 parts of nano-active calcium carbonate 24 parts of silica powder, 20 parts of boron carbide, 23 parts of glass wool, 40 parts of nano-silica, 35 parts of organic bentonite, 2 parts of methyl silicone oil, 1 part of anti-aging agent MB, 1.2 parts of antioxidant 3114, anti-aging RD1 .4 parts, 2.4 parts of accelerator CZ, 2 parts of accelerator D, 0.6 parts of compatibilizer, 0.5 part of hindered amine light stabilizer, 0.8 part of inorganic binder, 3 parts of barium stearate and 3 parts of zinc oxide;

[0044] Among them, the modified nylon material is prepared by the following process: mix 0.3-0.6 parts of resorcinol, 2-3 parts of formaldehyde, 6-12 parts of water and 23-26 parts of carboxylated styrene-butadie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an environment-friendly PVC (Polyvinyl chloride) resin cable sheath material and a preparation method thereof and relates to the technical field of high molecular materials. Theenvironment-friendly PVC resin cable sheath material is prepared from the following raw materials in parts by weight: PVC resin, nano fiber, a modified nylon material, sulfur powder, white carbon black, nano activated calcium carbonate, silica powder, boron carbide, glass wool, nano silicon dioxide, organic bentonite, methyl silicone oil, an anti-aging agent MB, an antioxidant 3114, an anti-agingagent RD, an accelerant CZ, an accelerant D, a compatilizer, a hindered amine light stabilizer, an inorganic binder, barium stearate and zinc oxide. The preparation method comprises the following steps: (1) weighing raw materials; (2) stirring; (3) banburying; (4) extruding out; (5) pelleting, cooling and packaging. The prepared environment-friendly PVC resin cable sheath material disclosed by the invention has the advantages of environmental friendliness, small in environmental pollution when being buried, high tensile strength and tear strength in a use process and good aging resistance.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an environment-friendly PVC resin cable sheath material and a preparation method thereof. Background technique [0002] Rubber is a highly elastic polymer material with reversible deformation. It is elastic at room temperature. It can produce a large deformation under the action of a small external force, and it can return to its original shape after the external force is removed. During use, due to friction with other objects, resulting in The surface of the rubber is damaged or even loses its original performance, and the rubber is used for too long, and the aging speed becomes faster, especially the wear and erosion of the rubber pipeline, which will lead to the leakage of the internal transmission medium, and under extreme conditions, Environmental crack resistance, high and low temperature resistance and weather resistance are poor, and it is not easy t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L77/00C08L83/04C08L13/00C08L67/02C08K13/04C08K3/26C08K7/14C08K3/36C08K3/38C08K7/26C08K5/3435C08K3/34H01B3/44
CPCC08L27/06C08K2003/265C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/202C08L2205/035C08L2205/08C08L2205/16H01B3/443C08L77/00C08L83/04C08L13/00C08K13/04C08K3/26C08K7/14C08K3/36C08K3/38C08K7/26C08K5/3435C08K3/34C08L67/02
Inventor 张颖鹤王明秀
Owner 南京化学工业园环保产业协同创新有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap