TiAl powder mechanical alloying preparation method

A mechanical alloying and alloying technology, applied in the field of material processing, can solve the problems of small production output, uneven particle size distribution of powder materials, expensive equipment, etc., to optimize the alloying effect, improve the uniformity of components, and inhibit oxidation The effect of the phenomenon

Inactive Publication Date: 2017-05-31
QINGDAO R & D INST XIAN JIAOTONG UNIV +1
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the main preparation methods of powder used in 3D printing are atomization method, chemical reduction method and mechanical alloying, etc. Among them, the process involved in atomization method is complicated, the equipment is expensive, and the components prepared by chemical reduction method are uniform, but the production capacity It is small and will produce chemical reagent wastewater at the same time. The main advantages of the mechanical alloying method are that the equipment is cheap and the processing method is simple. large-scale applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be further described below in combination with specific embodiments.

[0020] The mechanical alloying preparation method of TiAl powder comprises the following steps,

[0021] The selected alloy components include Al: 39-40%, Cr: 1.2-1.5-%, Nb: 1.6-1.8%, Si: 0.05-0.11%, Mo: 0.2-0.3%, V: 2.2- 2.8%, B: 0.03-0.04%, La: 0.02-0.04%, and the balance is Ti.

[0022] The element powder corresponding to the above components is selected according to the above atomic percentage. The particle size of the powder is 50-80 microns, and then it is added to the ethylene glycol solvent to obtain a mixture. The quality of the ethylene glycol solvent is 3% of the total mass of the element powder. -5 times, followed by ultrasonic vibration stirring, stirring for 3-5min and then heating and concentrating the above-mentioned solvent under the condition of continuing stirring, and concentrating ethylene glycol to 1-2 times the total mass of the element powder. When...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

A mechanical alloying preparation method includes the steps that proper powder is selected and added into ethylene glycol to be stirred, a concentrated product is added into a high-energy planetary ball mill and subjected to ball milling through milling balls of different sizes, and variable-angle ball milling is carried out with glucose as an antioxidant. By means of the mechanical alloying preparation method, the oxidation phenomenon in the alloying process is restrained, and the component uniformity of the alloying process is improved.

Description

technical field [0001] The invention belongs to the technical field of material processing, and in particular relates to a mechanical alloying preparation method of TiAl powder. Background technique [0002] Titanium-aluminum intermetallic compounds have low density, high strength, high hardness, high temperature resistance, high corrosion resistance and friction resistance, especially TiAl intermetallic compounds because of their high specific strength, high specific stiffness, corrosion resistance and wear resistance. , high temperature resistance and excellent oxidation resistance, etc., are becoming one of the excellent candidate structural materials in the contemporary aerospace industry, civil industry and other fields, especially in the field of aeroengine blades, which have broad application prospects. 3D printing, or additive manufacturing, is a rapid prototyping process that has emerged in recent years. It adopts layer-by-layer powder coating, laser or electron bea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C14/00B22F9/04B22F1/00C22C1/04
CPCB22F1/0003C22C1/0458C22C14/00B22F9/04B22F2009/041B22F2009/042C22C1/047
Inventor 余钊辉张建勋王茜
Owner QINGDAO R & D INST XIAN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com