Manufacturing method of electric wire with high-performance and high life

A manufacturing method and high-performance technology, applied in the direction of cable/conductor manufacturing, conductive core parts, circuits, etc., can solve the problems of environmental protection, low overload capacity of wires, etc., and achieve low power consumption, good electrical insulation performance, and overload protection powerful effect

Active Publication Date: 2017-05-31
重庆鸽牌电线电缆有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention intends to provide a manufacturing method of high-performance and long-life electric wires to solve the problems of low overload capacity and non-environmental protection of ordinary home improvement electric wires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of electric wire with high-performance and high life

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1, a method of manufacturing high-performance and long-life electric wires, including the steps of wire drawing, co-extrusion, testing, coiling and storage, using copper single wires with a purity greater than 99.99% as the core material 3, and the surface insulation materials include inner layer insulation Material 2 and outer insulation material 1, inner insulation material 2 is silane cross-linked polyethylene material, which is composed of the following materials: low density polyethylene resin 100kg, γ-chloropropyltriethoxysilane 0.5kg, diperoxide 0.2kg of (2-ethyl)hexyl carbonate, 0.3kg of N,N-diphenyl-p-aniline, and 0.2kg of catalyst. Outer insulating material 1 is silane cross-linked halogen-free low-smoke flame-retardant polyolefin insulating material; it is composed of the following materials: 200 kg of silane-grafted polyolefin; 50 kg of melamine polyphosphate; 0.3 kg of N,N-diphenyl-p-aniline; Processing aid 1.5kg; catalyst 0.5kg; anti-copper agent 0...

Embodiment 2

[0028]Embodiment 2, the difference between this embodiment and Embodiment 1 is that the inner insulating material 2 is a silane cross-linked polyethylene material, which is composed of the following materials: 100 kg of low-density polyethylene resin, γ-chloropropyltriethoxysilane 5kg, (2-ethyl)hexyl peroxydicarbonate 2kg, N,N-diphenyl-p-aniline 3kg, catalyst 1kg. Outer insulating material 1 is silane cross-linked halogen-free low-smoke flame-retardant polyolefin insulating material; it is composed of the following materials: silane-grafted polyolefin 200kg; melamine polyphosphate 150kg; N,N-diphenyl-p-aniline 1.2kg; Processing aid 5kg; catalyst 5kg; anti-copper agent 5kg. The thickness of the inner insulating material 2 is 0.15 mm, and the thickness of the outer insulating material 1 is 0.75 mm. During co-extrusion, the extrusion pressure is 80 MPa, the extrusion speed is 100 m / min, and the extrusion temperature is 155°C.

Embodiment 3

[0029] Embodiment 3, the difference between this embodiment and Embodiment 1 is that the inner insulating material 2 is a silane cross-linked polyethylene material, which is composed of the following materials: 100 kg of low-density polyethylene resin, γ-chloropropyltriethoxysilane 3kg, 1kg of (2-ethyl)hexyl peroxydicarbonate, 1.5kg of N,N-diphenyl-p-aniline, and 0.7kg of catalyst. Outer insulating material 1 is silane cross-linked halogen-free low-smoke flame-retardant polyolefin insulating material; it is composed of the following materials: 200 kg of silane-grafted polyolefin; 100 kg of melamine polyphosphate; 0.8 kg of N,N-diphenyl-p-aniline; Processing aid 3kg; catalyst 3kg; anti-copper agent 2.5kg. The thickness of the inner insulating material 2 is 0.12 mm, and the thickness of the outer insulating material 1 is 0.7 mm. During co-extrusion, the extrusion pressure is 75MPa, the extrusion speed is 75 m / min, and the extrusion temperature is 150°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of electric wire with high-performance and high life. The manufacturing method of electric wire with high-performance and high life comprises the steps of draw benching, twisting, co-extruding, detecting, looping, warehousing and the like, high purity copper mongline or copper stranded wire is core material, after draw benching, twisting and forming, through three extruder shared with one machine head, core materials, endothecium natural color insulations and exothecium colors insulations are formed by co-extruding. Endothecium uses organosilane crosslinked polyethylene insulation, exothecium uses silane crosslinked halogen-free low smoke antiflaming polyolefin insulation, which has the advantages of halogen-free, low smoke, environmental protection and non-toxic. Formed core materials of electric wire have the advantages of high purity, strong surge capability, double insulation and co-extruding. Overall performance of steam cross-linked insulation is good in whole, an operating temperature is high, service life is prolonged, environmental pollution is rarely in whole link of producing, using and recycling.

Description

technical field [0001] The invention relates to the field of electric wire manufacturing, in particular to a method for manufacturing electric wires with high performance and long service life. Background technique [0002] Ordinary home improvement wires generally use ordinary garden copper single wires as conductive cores, and ordinary PVC insulating plastics are used as single-layer insulation to extrude to form home improvement wires. It has many advantages as well as its disadvantages: [0003] 1. In order to reduce the cost, the purity of the copper material used in the copper single wire is usually about 99.95%. The purity is not very high, which leads to the weak overload capacity of the wire and high power consumption. [0004] 2. PVC insulation materials are mainly composed of PVC resin, which contains halogen factors, and will release a large amount of toxic smoke when burned; PVC insulation materials are not very adaptable when used in different environments, su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/14H01B7/00H01B7/02H01B7/28H01B7/295H01B3/44
CPCY02A30/14H01B13/00H01B3/441H01B7/0009H01B7/0216H01B7/0275H01B7/0291H01B7/28H01B7/295H01B13/141H01B13/148
Inventor 段敏陈文怡
Owner 重庆鸽牌电线电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap