Composite material for preparing carbon fiber fishing rod and preparation method thereof

A carbon fiber and composite material technology, applied in fishing rods, fishing, animal husbandry, etc., can solve the problems of low antistatic performance, toughness and aging resistance, achieve good antioxidation performance and antistatic performance, and novel formula technology , The effect of low raw material cost

Inactive Publication Date: 2017-06-13
舒城鑫泰碳纤维制品有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the continuous improvement of people's living standards, fishing has become an important entertainment and leisure activity for people, and competitive fishing is also in full swing. At present, most of the fishing rods on the market are carbon fiber fishing rods, all of which are made of shuttleless carbon fiber. Longitudinal cloth tubes are made by soaking resin and curing. The carbon fiber content used in the production of fishing rods directly determines the value and grade of fishing rods. Generally, the carbon content is about 30% and 90%. Fishing rods made of carbon fibers have light weight. , Solid, and high tensile strength. Although the existing materials for manufacturing fishing rods have excellent mechanical properties such as tensile strength, yield strength, and elongation, their antistatic properties, toughness, and aging resistance are not high. , there are still many limitations in the use process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1: A composite material for preparing a carbon fiber fishing rod, prepared from the following components in parts by mass: 50 parts of polyimide, 20 parts of carbon fiber, 15 parts of polyethylene fiber, 10 parts of titanium alloy wire, 2 parts of aramid fiber, 13 parts of Teflon, 8 parts of magnesium carbonate, 10 parts of calcium stearate, 5 parts of diphenylsilanediol, 8 parts of coumarone indene resin, 5 parts of rosin;

[0018] The preparation method of the composite material of preparing carbon fiber fishing rod is:

[0019] 1) Put polyimide, carbon fiber, polyethylene fiber, titanium alloy wire, aramid fiber, and Teflon into the mixer, and mix evenly at a speed of 500r / min and a temperature of 40°C;

[0020] 2) Ultrasonic the raw materials in the above steps for 15 min;

[0021] 3) Then put it into the reaction kettle, add magnesium carbonate, calcium stearate, diphenylsilanediol, coumarone indene resin, and rosin to react, and react at a temperature of ...

Embodiment 2

[0024] A composite material for preparing a carbon fiber fishing rod, which is prepared from the following components in parts by mass: 60 parts of polyimide, 25 parts of carbon fiber, 20 parts of polyethylene fiber, 15 parts of titanium alloy wire, and 4 parts of aramid fiber Parts, 8 parts of Teflon, 6 parts of magnesium carbonate, 7 parts of calcium stearate, 4 parts of diphenylsilanediol, 6 parts of coumarone indene resin, 8 parts of rosin;

[0025] The preparation method of above-mentioned composite material is:

[0026] 1) Put polyimide, carbon fiber, polyethylene fiber, titanium alloy wire, aramid fiber, and Teflon into the mixer, and mix evenly at a speed of 500r / min and a temperature of 48°C;

[0027] 2) Ultrasound the raw materials in the above steps for 12 minutes;

[0028] 3) Then put it into the reaction kettle, add magnesium carbonate, calcium stearate, diphenylsilanediol, coumarone indene resin, and rosin to react, and react at a temperature of 350°C for 38 min...

Embodiment 3

[0031] A composite material for preparing a carbon fiber fishing rod, which is prepared from the following components in parts by mass: 70 parts of polyimide, 30 parts of carbon fiber, 30 parts of polyethylene fiber, 20 parts of titanium alloy wire, and 8 parts of aramid fiber Parts, 13 parts of Teflon, 8 parts of magnesium carbonate, 4 parts of calcium stearate, 3 parts of diphenylsilanediol, 5 parts of coumarone indene resin, 5 parts of rosin;

[0032] The preparation method of above-mentioned composite material is:

[0033] 1) Put polyimide, carbon fiber, polyethylene fiber, titanium alloy wire, aramid fiber, and Teflon into the mixer, and mix evenly at a speed of 500r / min and a temperature of 60°C;

[0034] 2) Ultrasonic the raw materials in the above steps for 10 min;

[0035] 3) Then put it into the reaction kettle, add magnesium carbonate, calcium stearate, diphenylsilanediol, coumarone indene resin, and rosin to react, and react at a temperature of 300°C for 45 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A composite material for preparing a carbon fiber fishing rod, relating to the technical field of fishing gear, prepared from the following components in parts by mass: polyimide, carbon fiber, polyethylene fiber, titanium alloy wire, aramid fiber, Teflon , Magnesium Carbonate, Calcium Stearate, Diphenylsilanediol, Coumarone Indene Resin, Rosin. The raw material of the invention has a novel formulation process and low raw material cost, and the fishing rod made of the raw material has good toughness, light weight, good oxidation resistance and antistatic performance.

Description

[0001] Technical field: [0002] The invention relates to the technical field of fishing gear, in particular to a composite material for preparing a carbon fiber fishing rod and a preparation method thereof. [0003] Background technique: [0004] With the continuous improvement of people's living standards, fishing has become an important entertainment and leisure activity for people, and competitive fishing is also in full swing. At present, most of the fishing rods on the market are carbon fiber fishing rods, all of which are made of shuttleless carbon fiber. Longitudinal cloth tubes are made by soaking resin and curing. The carbon fiber content used in the production of fishing rods directly determines the value and grade of fishing rods. Generally, the carbon content is about 30% and 90%. Fishing rods made of carbon fibers have light weight. , Solid, and high tensile strength. Although the existing materials for manufacturing fishing rods have excellent mechanical properti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/08C08L23/06C08L77/06C08L27/18C08L93/04C08K13/04C08K7/06C08K3/04C08K3/08C08K3/26C08K5/098A01K87/00
CPCC08L79/08A01K87/00C08L2201/04C08L2205/035C08L2205/16C08L23/06C08L77/06C08L27/18C08L93/04C08K13/04C08K7/06C08K3/04C08K3/08C08K2003/267C08K5/098
Inventor 李铁梅陈国闯黄洪军万贤宏王再发
Owner 舒城鑫泰碳纤维制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap