Raw material for preparing carbon fiber fishing rod and method for preparing fishing rod by using same

A carbon fiber and fishing rod technology, used in fishing rods, fishing, applications, etc., can solve the problems of low antistatic performance, toughness and aging resistance, and achieve the effects of superior performance, light weight and low raw material cost.

Inactive Publication Date: 2017-08-18
舒城鑫泰碳纤维制品有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the continuous improvement of people's living standards, fishing has become an important entertainment and leisure activity for people, and competitive fishing is also in full swing. At present, most of the fishing rods on the market are carbon fiber fishing rods, all of which are made of shuttleless carbon fiber. Longitudinal cloth tubes are made by soaking resin and curing. The carbon fiber content used in the production of fishing rods directly determines the value and grade of fishing rods. Generally, the carbon content is about 30% and 90%. Fishing rods made of carbon fibers have light weight. , Solid, and high tensile strength. Although the existing materials for manufacturing fishing rods have excellent mechanical properties such as tensile strength, yield strength, and elongation, their antistatic properties, toughness, and aging resistance are not high. , there are still many limitations in the use process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: A kind of raw material of making carbon fiber fishing rod, is prepared from the following components:

[0021] Glass fiber, nano-boron fiber, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester, oxidized starch, epoxy curing agent and organic solvent;

[0022] Then:

[0023] 1) Add polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester and oxidized starch to the reaction kettle in sequence in proportion, mix well and heat up the mixture to react, and filter to obtain the mixture after the reaction;

[0024] 2) Add the mixture prepared in step 1) into the reaction kettle, then add the epoxy curing agent, and mix well to obtain the composite material. The reaction temperature is 150°C, and the reaction time is 1h;

[0025] 3) Put the composite material in step 2) into a microwave environment for 15 minutes, and the microwave frequency is: 800M...

Embodiment 2

[0028] A raw material for making carbon fiber fishing rods, prepared from the following components:

[0029] Glass fiber, nano-boron fiber, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester, oxidized starch, epoxy curing agent and organic solvent;

[0030] Then:

[0031] 1) Add polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester and oxidized starch to the reaction kettle in sequence in proportion, mix well and heat up the mixture to react, and filter to obtain the mixture after the reaction;

[0032] 2) Add the mixture prepared in step 1) into the reaction kettle, then add the epoxy curing agent, and mix well to obtain a composite material. The reaction temperature is 130° C., and the reaction time is 2 hours;

[0033] 3) Put the composite material in step 2) into a microwave environment for 15 minutes, and the microwave frequency is: 900MHz;

[0034] 4) T...

Embodiment 3

[0036] A raw material for making carbon fiber fishing rods, prepared from the following components:

[0037] Glass fiber, nano-boron fiber, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester, oxidized starch, epoxy curing agent and organic solvent;

[0038] Then:

[0039] 1) Add polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl ester and oxidized starch to the reaction kettle in sequence in proportion, mix well and heat up the mixture to react, and filter to obtain the mixture after the reaction;

[0040] 2) Add the mixture prepared in step 1) into the reaction kettle, then add the epoxy curing agent, and mix well to obtain the composite material, the reaction temperature is 140°C, and the reaction time is 1.5h;

[0041] 3) Put the composite material in step 2) into the microwave environment for 15 minutes, and the microwave frequency is: 850MHzMHz;

[0042] 4)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a raw material for preparing a carbon fiber fishing rod, which belongs to the technical field of fishery tools. The raw material is prepared from the following components: fiberglass, nano boron fiber, carbon fiber, a titanium alloy wire, polyurethane, epoxy resin, propylene oxide, linear polypropylene, carnauba wax, dioctyl phthalate, oxidized starch, an epoxy hardener, and an organic solvent. The raw material of the invention has the advantages of novel formula process and low cost; and the fishing rod prepared with the raw material has good tenacity and light weight, and has certain insulating property.

Description

[0001] Technical field: [0002] The invention relates to the technical field of fishing gear, in particular to a raw material for preparing a carbon fiber fishing rod and a method for preparing a fishing rod using the raw material. [0003] Background technique: [0004] With the continuous improvement of people's living standards, fishing has become an important entertainment and leisure activity for people, and competitive fishing is also in full swing. At present, most of the fishing rods on the market are carbon fiber fishing rods, all of which are made of shuttleless carbon fiber. Longitudinal cloth tubes are made by soaking resin and curing. The carbon fiber content used in the production of fishing rods directly determines the value and grade of fishing rods. Generally, the carbon content is about 30% and 90%. Fishing rods made of carbon fibers have light weight. , Solid, and high tensile strength. Although the existing materials for manufacturing fishing rods have exce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L63/00C08L23/12C08L91/06C08L3/10C08K13/04C08K7/14C08K7/06A01K87/00
CPCC08L75/04A01K87/00C08K2201/011C08K2201/014C08L3/10C08L23/12C08L63/00C08L91/06C08L2205/035C08K13/04C08K7/14C08K7/06
Inventor 李铁梅陈国闯黄洪军万贤宏王再发
Owner 舒城鑫泰碳纤维制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap