Preparation method of nest-like Sb2Se3 electrode material for sodium ion battery negative electrode
A technology for sodium ion batteries and electrode materials, applied in battery electrodes, nanotechnology for materials and surface science, secondary batteries, etc. , High electrochemical capacity, short cycle effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] 1) Add 0.675g of potassium antimony tartrate to 50mL of deionized water, magnetically stir until potassium antimony tartrate is completely dissolved to obtain mixed solution A, stirring speed is 500r / min, stirring time is 20min;
[0027] 2) Disperse 0.2369g of selenium powder in 3ml of hydrazine hydrate (50% by mass), stir it magnetically for 40min (speed of 500r / min, stirring temperature of 70℃) to obtain mixed solution B;
[0028] 3) Add the mixed liquid B to the mixed liquid A dropwise to obtain the mixed liquid C. Ultrasound the mixed solution C for 90 minutes (ultrasonic power is 80W, ultrasonic temperature is 70 ℃), and then transferred to the PTFE hydrothermal kettle, the PTFE hydrothermal kettle is placed in a homogeneous reactor (Yantai Keli Chemical Equipment Co., Ltd., KLJX-8A), react at 120℃ for 24h, cool to room temperature after the reaction, and then wash several times (washing solvent is acetone, ethanol and distilled water; washing method i...
Example Embodiment
[0031] Example 2
[0032] 1) Add 0.6759g of potassium antimony tartrate to 60mL of deionized water, magnetically stir until potassium antimony tartrate is completely dissolved to obtain mixed solution A, stirring speed is 500r / min, stirring time is 20min;
[0033] 2) Disperse 0.2369g of selenium powder in 5ml of hydrazine hydrate (50% by mass), sonicate for 7min (ultrasonic power is 120W; ultrasonic temperature is 40℃) to obtain mixed solution B;
[0034] 3) Add the mixed liquid B to the mixed liquid A dropwise to obtain the mixed liquid C. The mixture C was magnetically stirred for 3h (speed of 500r / min, stirring temperature of 70 ℃) and then transferred to the PTFE hydrothermal kettle, the PTFE hydrothermal kettle was placed in a homogeneous reactor (Yantai Keli Chemical Equipment Co., Ltd., KLJX-8A) was reacted at 140°C for 18 hours. After the reaction, it was cooled to room temperature and washed several times (the washing solvent was acetone, ethanol and distilled water; the wa...
Example Embodiment
[0037] Example 3
[0038] 1) Add 0.7322g potassium antimony tartrate into 70mL deionized water, magnetically stir until potassium antimony tartrate is completely dissolved to obtain mixed solution A; stirring speed is 500r / min, stirring time is 20min;
[0039] 2) Disperse 0.2566g of selenium powder in 7ml of hydrazine hydrate (50% by mass), and magnetically stir for 20min (speed of 700r / min, stirring temperature of 50℃) to obtain mixed solution B;
[0040] 3) Drop the mixed liquid B into the mixed liquid A dropwise to obtain the mixed liquid C. The mixed solution C was sonicated for 60min (ultrasonic power is 100W; ultrasonic temperature is 50℃) and then transferred to a PTFE hydrothermal kettle, and the PTFE hydrothermal kettle is placed in a homogeneous reactor (Yantai Keli Chemical Equipment Co., Ltd., KLJX-8A), react at a temperature of 150℃ for 12h, cool to room temperature after the reaction, and wash several times (the washing solvent is acetone, ethanol and distilled water; ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap