a cds/ag/g-c 3 n 4 Heterojunction composite photocatalyst and preparation method thereof

A technology of g-c3n4 and composite light, which is applied in the direction of physical/chemical process catalysts, chemical instruments and methods, water/sludge/sewage treatment, etc., can solve the problem of low crystallinity, high exciton binding energy, photogenerated carrier small mobility issues

Active Publication Date: 2019-08-27
东台市溱东科技发展有限公司 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

g-C 3 N 4 The energy gap position is unique, and it can complete the photocatalytic reaction that requires high semiconductor under visible light, but due to the g-C 3 N 4 High exciton binding energy and low crystallinity make it difficult to separate photogenerated electrons and holes, and the mobility of photogenerated carriers is small, resulting in low quantum efficiency in the photocatalytic process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a cds/ag/g-c <sub>3</sub> n <sub>4</sub> Heterojunction composite photocatalyst and preparation method thereof
  • a cds/ag/g-c <sub>3</sub> n <sub>4</sub> Heterojunction composite photocatalyst and preparation method thereof
  • a cds/ag/g-c <sub>3</sub> n <sub>4</sub> Heterojunction composite photocatalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) g-C 3 N 4 Preparation of nanosheets:

[0034] 5g of melamine was calcined, moved to a 550°C muffle furnace for calcination for 4 hours, and the heating rate was 2.5°C / min. After the calcination is finished, take out and grind; then the powder is calcined in the same procedure to obtain g-C 3 N 4 Nanosheets. Then add 1 g of g-C 3 N 4 The nanosheets are placed in a 90cm 3 Mechanically stir in a beaker of deionized water and 0.40g NaOH for 30min; then, transfer the solution to a 110°C reactor for 18h constant temperature thermal reaction; Dried to give g-C 3 N 4 Nanosheets.

[0035] (2) Ag / g-C 3 N 4 Preparation of:

[0036] 0.20g of g-C 3 N 4 nanosheets and 0.05g AgNO 3 Dissolve in 60ml deionized water and stir; then put the solution under UV light for 3h to reduce AgNO 3 , after the reaction is finished, wait until it drops to room temperature, wash the solid product with deionized water and ethanol, and dry to obtain Ag / g-C 3 N 4 ,spare;

[0037] ...

Embodiment 2

[0041] By the steps in Example 1, the difference is (2) the g-C of 0.20g 3 N 4 nanosheets and 0.01g AgNO 3 Dissolve in 60ml deionized water and stir; then put the solution under UV light for 3h to reduce AgNO 3 , after the reaction is finished, wait until it drops to room temperature, wash the solid product with deionized water and ethanol, and dry to obtain Ag / g-C 3 N 4 .

[0042] The sample in (2) was taken to carry out the photocatalytic degradation test in the photochemical reaction apparatus, and it was measured that the degradation rate of tetracycline by the photocatalyst reached 30.56% within 90 minutes.

Embodiment 3

[0044] By the steps in Example 1, the difference is (2) the g-C of 0.20g 3 N 4 nanosheets and 0.03g AgNO 3 Dissolve in 60ml deionized water and stir; then put the solution under UV light for 3h to reduce AgNO 3 , after the reaction is finished, wait until it drops to room temperature, wash the solid product with deionized water and ethanol, and dry to obtain Ag / g-C 3 N 4 .

[0045] The sample in (2) was taken to carry out the photocatalytic degradation test in the photochemical reaction apparatus, and it was measured that the degradation rate of tetracycline by the photocatalyst reached 50.41% within 90 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a CdS / Ag / g‑C 3 N 4 Heterojunction composite photocatalyst and preparation method, the steps are as follows: Step 1. Preparation of g‑C 3 N 4 Nanosheets; step 2, preparation of Ag / g‑C 3 N 4 ; Step 3. Preparation of CdS / Ag / g‑C 3 N 4 Composite photocatalyst. The present invention realizes the use of CdS / Ag / g-C 3 N 4 For the purpose of catalyst degradation of antibiotic wastewater. Semiconductor materials act as photocatalysts and visible light acts as excitations. They achieve special catalytic or transformation effects through interface interactions with pollutant molecules, exciting the surrounding oxygen and water molecules into free negative ions with great oxidizing power, thereby degrading harmful substances in the environment. For the purpose of organic matter, this method will not cause waste of resources and the formation of additional pollution, and is easy to operate. It is a green, environmentally friendly and efficient treatment technology.

Description

technical field [0001] The invention belongs to the technical field of environmental material preparation, and relates to the synthesis of CdS / Ag / g-C by photodecomposition deposition method and hydrothermal method 3 N 4 Preparation method and application of composite photocatalyst. Background technique [0002] Antibiotics mainly refer to some secondary metabolites or some artificially synthesized analogues produced by bacteria, molds or other microorganisms. It is mainly used to treat various bacterial infections or diseases caused by pathogenic microorganisms. It plays an extremely important role in human health and life safety. It is one of the great achievements of human beings in the field of medical science. In recent years, the residual situation of antibiotic substances in the water environment has become increasingly serious. Among them, antibiotic wastewater pollution represented by tetracycline is particularly significant, posing a serious threat to aquatic eco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/24C02F1/30C02F101/38
CPCC02F1/30B01J27/24C02F2305/10C02F2101/38B01J35/39Y02W10/37
Inventor 刘馨琳秦莹莹吕鹏王爽冯永强