Brazing material for aluminum-steel dissimilar-material connection brazing

A dissimilar and brazing technology, applied in welding/cutting medium/material, welding medium, welding equipment, etc., can solve the problem of low welding efficiency of brazing material, and achieve the effect of improving welding efficiency

Inactive Publication Date: 2017-06-30
XIAN AERONAUTICAL UNIV
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the welding efficiency of brazing filler metals is low, and in the spirit of excellence, continuous improvement and innovation are required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be further described below:

[0012] The invention consists of tin, lead, zinc, porous graphene, copper, ammonium triacetate, aluminum-based powder, zinc fluoride, tetrahydro sugar alcohol, and hydrogenated rosin.

[0013] Specifically, by weight, the tin accounts for 10%, the lead accounts for 10%, the zinc accounts for 10%, the porous graphene accounts for 2%, the copper accounts for 50%, and the ammonium acetate accounts for 1% %, the aluminum-based powder accounts for 5%, the zinc fluoride accounts for 5%, the tetrahydrosugar alcohol accounts for 2%, and the hydrogenated rosin accounts for 5%.

[0014] Further, the copper is made into a strip, and tin, lead, zinc, porous graphene, ammonium triacetate, aluminum-based powder, zinc fluoride, tetrahydro sugar alcohol, and hydrogenated rosin are mixed and solidified on the strip-shaped copper surface.

[0015] Specifically, the cross-section of the strip-shaped copper is triangular.

[0016] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a brazing material for aluminum-steel dissimilar-material connection brazing. The brazing material for aluminum-steel dissimilar-material connection brazing is composed of tin, lead, zinc, porous graphene, copper, nitrilotriacetic acid, aluminum base powder, zinc fluoride, tetrahydrofurfuryl alcohol and hydrogenated rosin. The copper is made into a strip, and the tin, the lead, the zinc, the porous graphene, the nitrilotriacetic acid, the aluminum base powder, the zinc fluoride, the tetrahydrofurfuryl alcohol and the hydrogenated rosin are mixed and solidified on the surface of the strip-shaped copper. Compared with the prior art, the brazing material for aluminum-steel dissimilar-material connection brazing has the advantages that the copper is used as the main raw material, the tin, the lead and the zinc are mixed with an combustion improver composed of multiple assistants, so that the copper can be rapidly molten, the welding efficiency is improved, and the brazing material for aluminum-steel dissimilar-material connection brazing has application value and popularization value.

Description

technical field [0001] The invention relates to a welding technology, in particular to a brazing material for brazing aluminum-steel dissimilar connections. Background technique [0002] The welding of aluminum alloy and steel is difficult to weld due to the large difference in melting temperature and the formed alloy is very brittle and easy to crack. At present, the ideal ones are as follows. 1: Friction welding, mainly suitable for shafts. 2: Explosive welding, mainly suitable for welding aluminum plate and steel plate. 3: Brazing, mainly using gas welding flame as heat source, melting lead solder for welding. In the prior art, the welding efficiency of brazing filler metals is relatively low, and continuous improvement and innovation are required in the spirit of excellence. Contents of the invention [0003] The object of the present invention is to provide a brazing material for brazing aluminum-steel dissimilar connections in order to solve the above problems. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K35/363
CPCB23K35/302B23K35/362
Inventor 高韩锋
Owner XIAN AERONAUTICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com