Luminous lace fabric and preparation method thereof

A lace and fabric technology, applied in the field of luminous lace fabric and its preparation, can solve the problems of complicated process, harmful to the body, unstable luminous performance, etc., and achieve the effects of simple preparation process, improved melting quality, and improved living standards

Inactive Publication Date: 2017-08-04
苏州博秀科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, similar products currently on the market have complex processes and contain fluorescent agents, which are harmful to the body and have unstable luminous performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Luminous lace fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A luminous lace fabric, the luminous lace fabric comprises 5 parts of polyurethane fiber, 15 parts of polyamide fiber, 10 parts of luminous fiber, 3 parts of polypropylene fiber and 10 parts of polyvinyl formal fiber by weight; Both the front and the back of the luminous lace fabric contain synthetic softeners, and the synthetic softeners include amino silicon microemulsion and polyethylene.

[0019] The weight ratio of the amino silicon microemulsion and polyethylene is 3:2; the luminescent fiber includes a fiber core material, and the fiber core material is coated with a polyethylene terephthalate coating; the fiber core material is as follows: Parts by weight include S i o 2 15 parts, Al 2 o 3 18 parts, L i F8 copies, C a f 2 5 copies, S m f 3 0.5 parts, D y f 3 0.05 parts, C e o 2 0.05 parts and Tb 4 o 7 0.1 part.

[0020] A preparation method of luminous lace fabric, comprising the following steps:

[0021] Step 1, re-combing: 50 polyurethane fibers...

Embodiment 2

[0029] A luminous lace fabric, the luminous lace fabric comprises 6 parts of polyurethane fiber, 16 parts of polyamide fiber, 11 parts of luminous fiber, 3.5 parts of polypropylene fiber and 10.5 parts of polyvinyl formal fiber by weight; Both the front and the back of the luminous lace fabric contain synthetic softeners, and the synthetic softeners include amino silicon microemulsion and polyethylene.

[0030] The weight ratio of the amino silicon microemulsion and polyethylene is 3:2; the luminescent fiber includes a fiber core material, and the fiber core material is coated with a polyethylene terephthalate coating; the fiber core material is as follows: Parts by weight include S i o 2 15 parts, Al 2 o 3 18 parts, L i F8 copies, C a f 2 5 copies, S m f 3 0.5 parts, D y f 3 0.05 parts, C e o 2 0.05 parts and Tb 4 o 7 0.1 part.

[0031] A preparation method of luminous lace fabric, comprising the following steps:

[0032] Step 1, re-combing: 50 polyurethane fi...

Embodiment 3

[0040]A luminous lace fabric, the luminous lace fabric comprises 7 parts of polyurethane fiber, 17 parts of polyamide fiber, 13 parts of luminous fiber, 4 parts of polypropylene fiber and 11 parts of polyvinyl formal fiber by weight; Both the front and the back of the luminous lace fabric contain synthetic softeners, and the synthetic softeners include amino silicon microemulsion and polyethylene.

[0041] The weight ratio of the amino silicon microemulsion and polyethylene is 3:2; the luminescent fiber includes a fiber core material, and the fiber core material is coated with a polyethylene terephthalate coating; the fiber core material is as follows: Parts by weight include S i o 2 15 parts, Al 2 o 3 18 parts, L i F8 copies, C a f 2 5 copies, S m f 3 0.5 parts, D y f 3 0.05 parts, C e o 2 0.05 parts and Tb 4 o 7 0.1 part.

[0042] A preparation method of luminous lace fabric, comprising the following steps:

[0043] Step 1, re-combing: 50 polyurethane fibers,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of fabric techniques and fabric preparation and discloses a luminous lace fabric and a preparation method thereof. The luminous lace fabric is prepared from, by weight, 5-8 parts of polyurethane fibers, 15-18 parts of polyamide fibers, 10-15 parts of luminous fibers, 3-5 parts of polypropylene fibers and 10-12 parts of formalized polyvinyl alcohol fibers. The preparation method of the luminous lace fabric includes steps of recombing, winding and twisting, weaving and after-treatment for shaping. The luminous lace fabric is excellent in fitting performance and free of any chemical additives, and due to addition of fluorides, melting quality of the luminous fiber core material is improved, and phonon energy of a substrate of the luminous fiber core material is reduced. In addition, the luminous lace fabric is free of fluorescent agents and harmless to bodies, the preparation process is simple, a significant function in improvement of living standard and realization of low carbon and environmental friendliness is achieved, and easiness in implementation is realized.

Description

technical field [0001] The invention relates to a lace fabric and a preparation method thereof, belonging to the field of fabric technology and preparation, in particular to a luminescent lace fabric and a preparation method thereof. Background technique [0002] With the advancement of science and technology, the textile industry has developed in pursuit of dreams, and people's requirements for the craftsmanship and use of lace fabrics have become higher and higher. Luminous lace fabrics have attracted great attention and are widely used in dangerous industries such as transportation and mining to protect human safety and have a broad market prospect. However, similar products currently on the market have complex processes and contain fluorescent agents, which are harmful to the body and have unstable luminous performance. Contents of the invention [0003] In order to solve the above problems, the invention discloses a luminescent lace fabric and a preparation method th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M15/227D06M15/507D01F9/08D02G3/04D02G3/18D02G3/28D04C1/02D06M101/38D06M101/34D06M101/20D06M101/24
CPCD06M15/6436D01F9/08D02G3/045D02G3/18D02G3/28D04C1/02D06M15/227D06M15/507D06M2101/20D06M2101/24D06M2101/34D06M2101/38D06M2200/50D10B2101/06D10B2321/022D10B2321/06D10B2331/02D10B2331/10
Inventor 胡永明
Owner 苏州博秀科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com