A method for making artificial wigs from palm fibers

A palm fiber and wig technology, applied in the field of palm fiber artificial wigs, can solve the problems of easily broken wires, high price, and difficulty in knotting, and achieve the effects of improving touch comfort and low cost

Active Publication Date: 2019-04-12
HUNAN XINYUAN HAIR PROD CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wig made of human hair is made of treated pure human hair. It has high fidelity, is not easy to knot, can be rounded, dyed, and permed, and is easy to change hairstyles, but the price is relatively high; chemical fiber wigs are made of chemical fiber. Although the price is low, the fidelity is poor, and it feels itchy after wearing, and it is easy to react with the scalp. Similarly, although the cost of plant fiber wigs is also low, the air permeability is not good, and it is easy to break when a little force is applied.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for making artificial wigs from palm fiber, including the following processing steps:

[0017] (1) Roughening treatment: Put the palm fiber in a vacuum chamber with a vacuum degree of 0.42MPa, and at the same time pass steam into the vacuum chamber to keep the temperature in the vacuum chamber at 80°C for 10 minutes, adjust the vacuum degree in the vacuum chamber to 0.85MPa, Pass steam into the vacuum chamber again to keep the temperature in the vacuum chamber at 120°C for 1 minute;

[0018] (2) Softening treatment: immerse the palm fiber in a calcium chloride solution with a mass concentration of 2.5%, heat it to 42°C, add α-amylase at a ratio of 2%, enzymatically react for 6 hours, and use hot air for primary drying , The initial drying temperature is 27℃, the hot wind speed is 1.1m / s, the relative humidity of the air is 42%, and the drying time is 18 minutes. The palm fiber after the initial drying is immersed in a calcium chloride solution with a mass concentrat...

Embodiment 2

[0022] A method for making artificial wigs from palm fiber, including the following processing steps:

[0023] (1) Roughing treatment: Put palm fiber in a vacuum chamber with a vacuum degree of 0.42MPa, and at the same time pass steam into the vacuum chamber to keep the temperature in the vacuum chamber at 85°C for 12 minutes, adjust the vacuum degree in the vacuum chamber to 0.85MPa, Pass steam into the vacuum chamber again to keep the temperature in the vacuum chamber at 130°C for 1.5 minutes;

[0024] (2) Softening treatment: immerse palm fiber in a calcium chloride solution with a mass concentration of 2.8%, heat it to 50°C, add α-amylase at a ratio of 3%, enzymatically react for 8 hours, and use hot air for primary drying , The first drying temperature is 30℃, the hot air speed is 1.15m / s, the relative humidity of the air is 48%, and the drying time is 22 minutes. The palm fiber after the first drying is immersed in a calcium chloride solution with a mass concentration of 2.8%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of wigs replacing hairs and concretely relates to a method of manufacturing an artificial wig by palm fibers. The method concretely comprises steps of de-roughing the palm fibers, softening the palm fibers, decoloring the palm fibers and dyeing the palm fibers. The palm fibers processed via the de-roughing step, the softening step, the decoloring step and the dyeing step can be applied for wig manufacture, has great naturalness and flexibility, is uneasy to knot, and has light weight, great ventilating property and high wearing comfortableness.

Description

Technical field [0001] The invention relates to the field of hair substitute wigs, in particular to a method for making artificial wigs with palm fiber. Background technique [0002] In recent years, people’s life rhythm has been accelerating and the pressure of life has been increasing. Many people have symptoms of hair loss at a young age. In addition, many people like to change their hair style frequently. In order to reduce the damage to hair, wigs are used. It became their best choice. The wig made of real human hair is made of pure human hair that has been treated. It has high fidelity, is not easy to knot, can be cut, dyed, and permed, and is convenient to change the hairstyle, but the price is higher; the chemical fiber wig is made of chemical fiber It is made of low price but poor fidelity. It feels itchy after wearing, and it is easy to react with the scalp. The same plant fiber wig is low in cost, but it has poor air permeability, and it is easy to break silk when you...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41G3/00
CPCA41G3/0075
Inventor 郭平
Owner HUNAN XINYUAN HAIR PROD CO LTD