Raw full-polish glaze with high abrasion resistance and method for preparing raw full-polish glaze

A high wear-resisting, full-glazing technology, applied in the field of architectural ceramic glaze, can solve the problems of many pinholes on the glaze surface, the wear resistance cannot meet the high requirements for use, and the stain resistance is poor, and the glaze has high hardness, The effect of widening the melting temperature range and increasing wear resistance

Inactive Publication Date: 2017-09-19
JIANGSU BAIFU TECH CO LTD
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also some wear-resistant glazes on the market. Adding alumina to the glaze can also improve these properties at high temperatures, but the glaze has many pinholes and poor stain resistance.
Some experts have also studied the ultra-wear-resistant full-polish glaze. The glaze wear resistance of the glaze is also 2100 rpm level 3. Although it is a grade higher than the ordinary full-polish glaze glaze wear resistance 1500 rpm level 3, its resistance Abrasiveness is still not up to high requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. The formula composition of the full glaze, according to parts by weight: 38 parts of potassium feldspar, 4 parts of kaolin, 5 parts of burnt talc, 10 parts of dolomite, 20 parts of barium carbonate, 5 parts of burnt zinc oxide, 10 parts of fused quartz, 3 parts of corundum powder, 5 parts of lithium-containing minerals, and 5 parts of additives. The lithium-containing mineral is spodumene, and the additive is silica sol.

[0022] 2. At a firing temperature of 1160°C, the holding time during the firing process is 10 minutes, and the total firing time is 50 minutes to obtain the product after firing. The Mohs hardness of the wear-resistant glaze is determined to be 5.5, and the wear resistance is 12000 rpm 4.

Embodiment 2

[0024] 1. The composition of the full glaze glaze formula is as follows in parts by weight: 28 parts of potassium feldspar, 4 parts of kaolin, 5 parts of burnt talc, 10 parts of dolomite, 22 parts of barium carbonate, 8 parts of burnt zinc oxide, 15 parts of fused quartz, 3 parts of corundum powder, 5 parts of lithium-containing minerals, and 10 parts of additives. The lithium-containing mineral is petalite, and the additive is silica sol.

[0025] 2. At a firing temperature of 1180°C, the holding time during the firing process is 10 minutes, and the total firing time is 60 minutes to obtain the product after firing. The Mohs hardness of the wear-resistant glaze is determined to be 5.5, and the wear resistance is 12000 rpm 4.

Embodiment 3

[0027] 1. The formula composition of the full glaze, according to parts by weight: 32 parts of potassium feldspar, 4 parts of kaolin, 5 parts of burnt talc, 10 parts of dolomite, 22 parts of barium carbonate, 5 parts of burnt zinc oxide, 10 parts of fused quartz, 7 parts of corundum powder, 5 parts of lithium-containing minerals, and 8 parts of additives. The lithium-containing mineral is eucryptite, and the additive is silica sol.

[0028] 2. At a firing temperature of 1180°C, the holding time during the firing process is 8 minutes, and the total firing time is 55 minutes to obtain the product. The Mohs hardness of the wear-resistant glaze is determined to be 5.5, and the wear resistance is 12000 rpm 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses raw full-polish glaze with high abrasion resistance and a method for preparing the raw full-polish glaze. The raw full-polish glaze comprises, by weight, 28-38 parts of potassium feldspar, 4-7 parts of kaolin, 5-10 parts of sintered talc, 5-10 parts of dolomite, 16-22 parts of barium carbonate, 5-8 parts of sintered zinc oxide, 10-18 parts of fused quartz, 3-12 parts of corundum micro-powder, 1-5 parts of lithium-containing mineral and 5-10 parts of additives. The raw full-polish glaze and the method have the advantages that corundum particles and fused quartz particles are led into the raw full-polish glaze, accordingly, the availability of partial original abrasion-resistant particles can be guaranteed, large quantities of anorthite and celsian micro-crystals further can be generated, and the abrasion resistance of glaze surfaces can be improved; the lithium-containing mineral is added into the raw full-polish glaze, and accordingly liquid phases can be generated by the raw full-polish glaze at the low temperatures; lithium element ions have small radiuses, tight glass networks can be formed, and accordingly the abrasion resistance of the glaze surfaces can be improved.

Description

technical field [0001] The invention relates to the technical field of architectural ceramic glazes, in particular to a raw material high wear-resistant full polished glaze and a preparation method thereof. Background technique [0002] Full-polished glazed tile is a special glaze that can be polished after applying full-polished glazed glaze to the bottom glaze of inkjet printing and other colors. Fully polished glazed tiles combine the advantages of polished tiles and marble tiles. The glazed surface is as smooth and bright as polished tiles. Its surface glaze is characterized by transparency, no color, and does not cover the bottom glaze and various flower glazes underneath. When the glaze is polished, only a thin layer of transparent surface glaze is thrown away. The emergence of full glaze brings the tiles back to the "bright light era", thus raising the smooth, bright and magnificent effect of tile decoration to a whole new level. At present, fully glazed products ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/89
CPCC03C8/14C04B41/52C04B41/89C04B41/504C04B41/5022
Inventor 王美兰包启富周建儿王传胜黄骏许行强
Owner JIANGSU BAIFU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com