Method for producing multi-functional aerated concrete block

A kind of technology of air-entrained concrete and production method, which is applied in the direction of building components, applications, household appliances, etc., can solve the problems of performance gap and different production processes, and achieve the effects of improving earthquake resistance, slow thermal migration, and reducing self-weight

Inactive Publication Date: 2017-09-22
HENGYANG HENGYU LIGHTWEIGHT INSULATION MATERIAL CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the formulations of various aerated concrete blocks are different, and the production processes are also different, resulting in a gap in performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A method for producing a multifunctional aerated concrete block, comprising the steps of:

[0056] 1) Ingredients, in parts by weight, the aerated concrete block raw materials include the following components: 250 parts of water; 3 parts of aluminum powder; 60 parts of gypsum; 80 parts of lime; 150 parts of tailings; 150 parts of silt; 30 parts; 60 parts of fly ash; 70 parts of cement; 3 parts of additives; 30 parts of foam stabilizer; The silicon dioxide content of the slag is more than 80wt%;

[0057] 2) mixing and stirring;

[0058] 3) After pouring, carry out gas generation and initial setting in the initial curing room, the temperature is 45-60°C, the initial curing time is 2 hours, and cut after the initial curing is completed;

[0059] 4) Autoclave curing, send the green body cut in step 3) together with the bottom mold into the autoclave, close the door of the autoclave after the green body is put into the autoclave, and vacuumize before passing the steam, the...

Embodiment 2

[0062] A method for producing a multifunctional aerated concrete block, comprising the steps of:

[0063] 1) Ingredients, in parts by weight, the aerated concrete block raw materials include the following components: 300 parts of water; 5 parts of aluminum powder; 70 parts of gypsum; 85 parts of lime; 170 parts of tailings; 180 parts of silt; 40 parts; 70 parts of fly ash; 80 parts of cement; 5 parts of additives; The silicon dioxide content of the slag is more than 80wt%;

[0064] 2) mixing and stirring;

[0065] 3) After pouring, carry out gas generation and initial setting in the initial curing room, the temperature is 45-60°C, the initial curing time is 2 hours, and cut after the initial curing is completed;

[0066] 4) Autoclave curing, send the green body cut in step 3) together with the bottom mold into the autoclave, close the door of the autoclave after the green body is put into the autoclave, and vacuumize before passing the steam, the vacuum degree is 800×10 5 P...

Embodiment 3

[0069] A method for producing a multifunctional aerated concrete block, comprising the steps of:

[0070] 1) Ingredients, in parts by weight, the aerated concrete block raw materials include the following components: 350 parts of water; 8 parts of aluminum powder; 80 parts of gypsum; 90 parts of lime; 200 parts of tailings; 200 parts of silt; 50 parts; 80 parts of fly ash; 90 parts of cement; 8 parts of additives; The silicon dioxide content of the slag is more than 80wt%;

[0071] 2) mixing and stirring;

[0072] 3) After pouring, carry out gas generation and initial setting in the initial curing room, the temperature is 45-60°C, the initial curing time is 2 hours, and cut after the initial curing is completed;

[0073] 4) Autoclave curing, send the green body cut in step 3) together with the bottom mold into the autoclave, close the door of the autoclave after the green body is put into the autoclave, and vacuumize before passing the steam, the vacuum degree is 800×10 5 P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing a multi-functional aerated concrete block. The method comprises 1) preparing 250 to 350 parts by weight of water, 3 to 8 parts by weight of aluminum powder, 60 to 80 parts by weight of gypsum, 80 to 90 parts by weight of lime, 150 to 200 parts by weight of tailings, 150 to 200 parts by weight of silt, 30 to 50 parts by weight of slag, 60 to 80 parts by weight of fly ash, 70 to 90 parts by weight of cement, 3 to 8 parts by weight of additives, 30 to 50 parts by weight of a foam stabilizer and 5 to 20 parts by weight of sodium carbonate, 2) carrying out mixing stirring, 3) carrying out pouring, then carrying out gas formation initial coagulation at 45-60 DEG C through an initial curing chamber, carrying out initial curing for 2h and then carrying out cutting, 4) carrying out segmented maintenance, and 5) processing a finished product, discharging the finished product out of a reactor, carrying out inspection and carrying out classification stacking.

Description

technical field [0001] The invention relates to a production method of a multifunctional aerated concrete block. Background technique [0002] Air-entrained concrete block is a new type of building material that is lightweight, porous, thermal insulation, good fire resistance, nailable, sawable, planable, and has certain earthquake resistance. As early as the early 1930s, China began to produce this product and it was widely used. For example: Shanghai International Hotel, Shanghai Building, Fuzhou Building, People's Bank of China Building and other high-rise buildings. It is an excellent new building material and has the advantages of environmental protection. However, the formulations of various aerated concrete blocks are different, and the production processes are also different, resulting in a gap in performance. Contents of the invention [0003] The object of the present invention is to provide a production method of a multifunctional aerated concrete block with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B38/02E04C1/00C04B111/20C04B111/27C04B111/28C04B111/40C04B111/52
CPCC04B28/02C04B2111/20C04B2111/27C04B2111/28C04B2111/40C04B2111/52C04B2201/50E04C1/00C04B14/34C04B14/365C04B2/02C04B18/12C04B14/068C04B18/10C04B18/08C04B22/10C04B40/024C04B2103/48C04B2103/0068C04B38/02
Inventor 谭泽林
Owner HENGYANG HENGYU LIGHTWEIGHT INSULATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap