Waterborne acrylic amino resin silver powder paint and preparation method thereof

A technology of acrylic amino and water-based acrylate, which is applied in the direction of epoxy resin coatings, latex paints, metal-free paints, etc., can solve the problems of low impact strength, slow drying speed, poor hiding power, etc., and achieve good stability, Not easy to reunite, improve the effect of covering power

Inactive Publication Date: 2017-10-20
周荣
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But current silver powder paint also has the defects of slow drying speed, poor gloss, poor adhesion, easy to fall off, low impact strength, poor hiding power, and difficult storage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] Take 30g of aluminum powder and add it to 60mL of isopropanol, stir at 300r / min at 40°C for 1h, then add 50mL of butyl titanate dropwise at a rate of 1mL / min, mix well and adjust the pH with 2% acetic acid solution 4.0, and in a constant temperature water bath at 80°C, stirred and reacted at 200r / min for 3h, filtered to obtain the filter residue, and air-dried the filter residue naturally to obtain titanium dioxide-coated aluminum powder; then take 0.3g of wetting and dispersing agent, 8g of titanium dioxide-coated aluminum powder Add 15mL of deionized water, stir at 300r / min for 20min to obtain water-based aluminum silver paste; finally take 60g of water-based acrylate emulsion, 8g of amino resin, 4g of ethylene glycol butyl ether, 0.2g of defoamer, 0.2g of leveling agent, 1.5g of anti-settling agent, 15mL of deionized water, stirred at 1000r / min for 20min, then added 8g of water-based aluminum silver paste, stirred at 200r / min for 20min, to obtain water-based acrylic a...

example 2

[0026] First take 38g of aluminum powder and add it to 75mL of isopropanol, stir at 350r / min for 2h at 45°C, then add 80mL of butyl titanate dropwise at a rate of 2mL / min, mix well and adjust the pH with 2% acetic acid solution 4.5, and in a constant temperature water bath at 85°C, stirred and reacted at 250r / min for 4h, filtered to obtain the filter residue, and air-dried the filter residue naturally to obtain titanium dioxide-coated aluminum powder; then take 0.4g of wetting and dispersing agent, 9g of titanium dioxide-coated aluminum powder Add 18mL of deionized water, stir at 350r / min for 25min to obtain water-based aluminum silver paste; finally take 65g of water-based acrylate emulsion, 9g of amino resin, 5g of butyl glycol ether, 0.3g of defoamer, 0.3g of leveling agent, 1.8g of anti-settling agent, 18mL of deionized water, stirred at 1100r / min for 25min, then added 9g of water-based aluminum silver paste, stirred at 250r / min for 25min, to obtain water-based acrylic amin...

example 3

[0028] First take 45g of aluminum powder and add it to 90mL of isopropanol, stir at 400r / min for 2h at 50°C, then add 100mL of butyl titanate dropwise at a rate of 2mL / min, mix well and adjust the pH with 2% acetic acid solution 5.0, and stirred and reacted at 300r / min for 4 hours in a constant temperature water bath at 90°C, filtered to obtain the filter residue, and air-dried the filter residue naturally to obtain titanium dioxide-coated aluminum powder; then take 0.5g of wetting and dispersing agent, 10g of titanium dioxide-coated aluminum powder Add 20mL of deionized water, stir at 400r / min for 30min to obtain water-based aluminum silver paste; finally take 70g of water-based acrylate emulsion, 10g of amino resin, 6g of ethylene glycol butyl ether, 0.3g of defoamer, 0.3g of leveling agent, 2.0g of anti-settling agent, 20mL of deionized water, stirred at 1200r / min for 30min, then added 10g of water-based aluminum silver paste, stirred at 300r / min for 30min to obtain water-ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses waterborne acrylic amino resin silver powder paint and a preparation method thereof, and belongs to the field of chemical paint. The silver powder paint is prepared from the following raw materials in parts by weight: 60 to 70 parts of waterborne acrylate emulsion, 8 to 10 parts of amino resin, 4 to 6 parts of ethylene glycol monobutyl ether, 0.2 to 0.3 part of a de-foaming agent, 0.2 to 0.3 part of a flatting agent, 1.5 to 2.0 parts of an anti-settling agent, 15 to 20 parts of de-ionized water and 8 to 10 parts of waterborne aluminum silver paste. The preparation method comprises the following steps: adding a wetting dispersant and titanium dioxide cladded aluminum powder into the de-ionized water, and stirring to prepare the waterborne aluminum silver paste; then stirring and mixing the waterborne acrylate emulsion, the amino resin, the ethylene glycol monobutyl ether, the de-foaming agent, the flatting agent, the anti-settling agent and the de-ionized water, and adding the waterborne aluminum silver paste to prepare the silver powder paint. The waterborne acrylic amino resin silver powder paint disclosed by the invention has the beneficial effects of relatively good adhesion force and covering power, and a paint film has good comprehensive performance.

Description

technical field [0001] The invention relates to a water-based acrylic amino resin silver powder paint and a preparation method thereof, belonging to the field of chemical coatings. Background technique [0002] Silver powder paint is a liquid mixed with silver powder (aluminum powder, etc.) and thinner. It is mostly used for painting the surface of plumbing pipes in old buildings. It is also suitable for heating equipment, vehicles, oil tanks, iron towers, metal pipes, anti-corrosion of metal surfaces and silver decoration of various objects. [0003] Silver powder paint is divided into non-leafing flash silver powder paint and silicone high temperature resistant silver powder paint. Non-leafing glitter silver powder paint is to first soak non-leafing glitter silver paste or pearl powder with appropriate fineness in xylene and other solvents, then slowly add it to the stirred paint, stir at low speed for more than ten minutes, and adjust the appropriate viscosity. Prepared...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/08C09D161/28C09D161/24C09D163/00C09D5/02C09D5/38C09D7/06C09D7/02C09D7/45C09D7/47
CPCC09D133/08C08K2003/0812C09D5/024C09D5/028C09D5/38C08L61/28C08L77/00C08L83/04C08K9/02C08K3/08C08K5/06C08L61/24C08L63/00
Inventor 陈合华方晓俊王之霖
Owner 周荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com