A phenol-based propane epoxy resin, high adhesion technology, applied in the field of coatings, can solve the problems that affect the quality of the building and the service life of the building, self-protection, weak adhesion, single function of the fireproof material, etc., to achieve tensile strength Strong, easy to make, good anti-aging effect

Inactive Publication Date: 2017-10-24
屈德顺
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantages are that its strength is not high, self-protection and adhesion are not strong; and the function of this fireproof material is relatively single, which directly affects the quality of the building and the service life of the building to a large extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A high-adhesion paint, comprising the following components by weight: 20 parts of phenolic propane epoxy resin, 8 parts of pentaerythritol, 20 parts of amino resin, 15 parts of iron oxide red, 20 parts of isophorone diisocyanate, activated carbonic acid 20 parts of calcium, 5 parts of general leveling agent, 8 parts of lignocellulose.

Embodiment 2

[0018] A high-adhesion paint, comprising the following components by weight: 30 parts of phenolic propane epoxy resin, 3 parts of pentaerythritol, 25 parts of amino resin, 10 parts of iron oxide red, 30 parts of isophorone diisocyanate, activated carbonic acid 15 parts of calcium, 8 parts of general leveling agent, 5 parts of lignocellulose.

Embodiment 3

[0020] A high-adhesion paint, comprising the following components by weight: 20.8 parts of phenolic propane epoxy resin, 7.4 parts of pentaerythritol, 20.4 parts of amino resin, 14.5 parts of iron oxide red, 21.2 parts of isophorone diisocyanate, activated carbonic acid 19.4 parts of calcium, 5.2 parts of general leveling agent, 7.4 parts of lignocellulose.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-adhesion material, in particular to a high-adhesion paint containing phenolic propane epoxy resin, which belongs to the technical field of paint. A high-adhesion paint containing phenolic propane epoxy resin, comprising the following components in parts by weight: 20-30 parts of phenolic propane epoxy resin, 3-8 parts of pentaerythritol, 20-25 parts of amino resin, iron oxide red 10-15 parts, 20-30 parts of isophorone diisocyanate, 15-20 parts of activated calcium carbonate, 5-8 parts of general leveling agent, 5-8 parts of lignocellulose. The high-adhesion paint containing phenolic propane epoxy resin of the present invention has simple technical formula, strong coating film adhesion and relatively scratch resistance.

Description

technical field [0001] The invention relates to a high-adhesion material, in particular to a high-adhesion paint containing phenolic propane epoxy resin, and belongs to the technical field of paints. Background technique [0002] At present, the fire protection of various buildings is a key issue. The commonly used fireproof materials are all kinds of fireproof coils, fireproof coatings, fireproof glue and so on. Fireproof coils are generally mainly constructed by heat, mostly by fire. The main disadvantage is that the bonding is not comprehensive, there are seams, and it is difficult to handle some special parts, such as corners, nozzles, etc., and it is easy to seep water. Not easy to repair. Fire retardant coatings are generally cold-applied. After the fire retardant coatings are mixed well, they are painted at one time, with seamless construction and strong adhesion. The disadvantage is that the strength is not high, self-protection and adhesion are not strong; and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D161/20C09D5/18C09D7/12
CPCC09D163/00C08L2201/02C08L2201/08C08L2205/035C09D5/18C09D161/20
Inventor 屈德顺
Owner 屈德顺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap