Modified industrial inorganic powder and composite material containing modified industrial inorganic powder

A composite material and inorganic powder technology, which is applied in the field of modified industrial inorganic powder and composite materials containing modified industrial inorganic powder, can solve the problems of large land occupation, environmental hazards, etc., achieve reduced stacking and disposal costs, excellent water resistance, The effect of excellent mechanical properties

Active Publication Date: 2019-11-19
GUANGDONG PHOMI MCM CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of modern industry, various industrial enterprises will produce a large amount of waste slag in the production process, such as electroplating industry will produce electroplating slag, porcelain industry will produce porcelain slag, sulfuric acid or sulfurous acid industry will produce sulfuric acid slag, and waste slag Emissions are increasing day by day, which not only requires a large amount of land to be stacked, but also causes great harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified industrial inorganic powder and composite material containing modified industrial inorganic powder
  • Modified industrial inorganic powder and composite material containing modified industrial inorganic powder
  • Modified industrial inorganic powder and composite material containing modified industrial inorganic powder

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the above-mentioned modified industrial inorganic powder comprises the following steps: uniformly mixing acrylic polymer emulsion or / and redispersible latex powder and polyether polyurethane, then adding inorganic waste residue powder, fully mixing uniformly, and drying to obtain the package Coated modified industrial inorganic powder.

[0033] A composite material containing the above-mentioned modified industrial inorganic powder, comprising the following raw materials in parts by mass:

[0034] 100 parts of modified industrial inorganic powder; 0-3 parts of fiber; 0-1 part of methyl cellulose; 0-5 parts of pigment; 20-60 parts of active inorganic powder;

[0035] Or, 100 parts of modified industrial inorganic powder; 0-3 parts of fiber; 0-1 part of methyl cellulose; 0-5 parts of pigment; 3-60 parts of elastic polymer;

[0036] Or, 100 parts of modified industrial inorganic powder; 0-3 parts of fiber; 0-1 part of methyl cellulose; 0-5 parts ...

Embodiment 1

[0048] A modified industrial inorganic powder, comprising the following raw materials in parts by mass: sulfuric acid slag powder: 100 parts; acrylic polymer emulsion: 3 parts; polyether polyurethane: 10 parts.

[0049] The preparation method of the modified industrial inorganic powder includes the following steps: uniformly mixing the acrylic polymer emulsion and polyether polyurethane, adding sulfuric acid slag powder, fully mixing uniformly, and drying to obtain the coated modified industrial inorganic powder.

[0050] A composite material containing modified industrial inorganic powder, comprising the following raw materials in parts by mass: the above-mentioned modified industrial inorganic powder: 100 parts; polyvinyl alcohol fiber: 1 part; methyl cellulose: 0.5 part; pigment: 2 parts; Granulated water-quenched steel slag powder: 30 parts.

[0051] The preparation method of the composite material containing the modified industrial inorganic powder includes the following ...

Embodiment 2

[0053] A modified industrial inorganic powder, comprising the following raw materials in parts by mass: porcelain slag powder: 100 parts; redispersible latex powder: 10 parts; polyether polyurethane: 15 parts.

[0054] The preparation method of the modified industrial inorganic powder includes the following steps: uniformly mixing redispersible latex powder and polyether polyurethane, adding porcelain slag powder, fully mixing uniformly, and drying to obtain coated modified industrial inorganic powder.

[0055] A composite material containing modified industrial inorganic powder, comprising the following raw materials in parts by mass: the above-mentioned modified industrial inorganic powder: 100 parts; polyvinyl alcohol fiber: 1.5 parts; methyl cellulose: 1 part; granulated electric furnace phosphorus slag Powder: 20 parts.

[0056] The preparation method of the composite material containing modified industrial inorganic powder includes the following steps: uniformly mixing m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses modified industrial inorganic powder and a composite material containing the modified industrial inorganic powder. The modified industrial inorganic powder is prepared from 100 parts of inorganic waste slag powder, 3-40 parts of acrylic polymer emulsion or / and 1-10 parts of redispersible latex powder and 3-30 parts of polyether polyurethane. The modified industrial inorganic powder can replace a traditional packing, waste resources are recycled, the piling and disposal costs are reduced, and certain economic benefits can be also brought. The composite material containing the modified industrial inorganic powder has excellent mechanical properties such as toughness and impact resistance, excellent water resistance and resistance to chemical corrosion and microbes, can be formed at a time without steaming, pressing and curing during manufacturing, can be widely used for laying highway pavements, sidewalk pavements, road traffic stones, bridges and the like, and the composite material added with an elastomeric polymer can be used for laying runways, sports floors and the like.

Description

technical field [0001] The invention relates to a modified industrial inorganic powder and a composite material containing the modified industrial inorganic powder, belonging to the technical field of composite materials. Background technique [0002] With the rapid development of modern industry, various industrial enterprises will produce a large amount of waste slag in the production process, such as electroplating industry will produce electroplating slag, porcelain industry will produce porcelain slag, sulfuric acid or sulfurous acid industry will produce sulfuric acid slag, and waste slag Emissions are increasing day by day, which not only requires a large amount of land to be stacked, but also causes great harm to the environment. In fact, it is only necessary to process industrial waste slag, and it can be converted into useful raw materials, which can not only solve the environmental pollution problems existing in the conventional treatment of waste slag, but also b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/32C04B28/08
CPCC04B28/08C04B28/082C04B28/087C04B40/0039C04B2111/20C04B2201/50C04B18/0427C04B24/26C04B24/32C04B24/383C04B16/0641C04B2103/54C04B18/165C04B18/0472
Inventor 石磊
Owner GUANGDONG PHOMI MCM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com