Fiber-reinforced thermal insulation board and preparation method thereof

A fiber-reinforced and thermal insulation board technology, applied in the field of thermal insulation boards, can solve the problems of low compressive performance and easy cracking of thermal insulation boards, and achieve the effect of low cost, not easy to crack, and good compressive performance

Inactive Publication Date: 2017-11-03
HEFEI HUAGAI PHOTOVOLTIAC TECH CO LTD
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing insulation boards have problems such as low compressive performance and easy cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A fiber-reinforced thermal insulation board, comprising the following raw materials: 65 parts of modified magnesium oxysulfide cement slurry, 35 parts of desulfurized gypsum, 30 parts of modified expanded perlite, 29 parts of modified diatomite, and 24 parts of fly ash parts, 24 parts of waste glass powder, 15 parts of additives and 75 parts of water;

[0032] The modified magnesium oxysulfide cement slurry includes the following raw materials: 15 parts of magnesium sulfate solution, 15 parts of magnesium oxide powder, 10 parts of modifier, 10 parts of modified carbon fiber and 20 parts of water;

[0033] The auxiliary agent includes the following raw materials: 3 parts of foaming agent, 3 parts of water reducing agent, 2 parts of inorganic binder and 1 part of curing agent.

[0034] Wherein, the modifier includes the following raw materials in parts: 3 parts of silicone water repellent powder, 3 parts of zinc borate, 1 part of paraffin, and 1 part of stearic acid.

[...

Embodiment 2

[0052] A fiber reinforced insulation board, comprising the following raw materials: 70 parts of modified magnesium oxysulfide cement slurry, 40 parts of desulfurized gypsum, 30.5 parts of modified expanded perlite, 29.5 parts of modified diatomite, and 25 parts of fly ash parts, 25 parts of waste glass powder, 15.5 parts of additives and 80 parts of water;

[0053] The modified magnesium oxysulfide cement slurry includes the following raw materials: 20 parts of magnesium sulfate solution, 17.5 parts of magnesium oxide powder, 12.5 parts of modifier, 11 parts of modified carbon fiber and 21 parts of water;

[0054] The auxiliary agent includes the following raw materials: 3.5 parts of foaming agent, 3.5 parts of water reducer, 2.5 parts of inorganic binder and 1.5 parts of curing agent.

[0055] Wherein, the modifying agent includes the following raw materials in parts: 3.5 parts of organosilicon water repellent powder, 3.5 parts of zinc borate, 1.5 parts of paraffin, and 1.5 p...

Embodiment 3

[0073] A fiber-reinforced thermal insulation board, comprising the following raw materials: 75 parts of modified magnesium oxysulfide cement slurry, 45 parts of desulfurized gypsum, 31 parts of modified expanded perlite, 30 parts of modified diatomite, and 26 parts of fly ash parts, 26 parts of waste glass powder, 16 parts of additives and 85 parts of water;

[0074] The modified magnesium oxysulfate cement slurry includes the following raw materials: 25 parts of magnesium sulfate solution, 20 parts of magnesium oxide powder, 15 parts of modifier, 12 parts of modified carbon fiber and 22 parts of water;

[0075] The auxiliary agent includes the following raw materials: 4 parts of foaming agent, 4 parts of water reducer, 3 parts of inorganic binder and 2 parts of curing agent.

[0076] Wherein, the modifying agent includes the following raw materials in parts: 4 parts of silicone water repellent powder, 4 parts of zinc borate, 2 parts of paraffin, and 2 parts of stearic acid. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fiber-reinforced thermal insulation board and a preparation method thereof, and relates to the technical field of thermal insulation boards.The fiber-reinforced thermal insulation board is prepared from the following raw materials in parts by weight: 65 to 75 parts of modified magnesium oxysulfate cement slurry, 35 to 45 parts of desulfuration gypsum, 30 to 31 parts of modified expanded perlite, 29 to 30 parts of modified diatomite, 24 to 26 parts of fly ash, 24 to 26 parts of waste glass powder, 15 to 16 parts of auxiliary agents and 75 to 85 parts of water. The fiber-reinforced thermal insulation board has a better compressive property and is not easy to crack, the preparation method is simple and the cost is relatively low.

Description

technical field [0001] The invention relates to the technical field of thermal insulation boards, in particular to a fiber-reinforced thermal insulation board and a preparation method thereof. Background technique [0002] As a big country in construction, my country's building energy consumption accounts for about 27% of the country's total energy consumption, but the level of building energy conservation is far lower than that of developed countries in the world, and the unit building energy consumption is 3-5 times that of developed countries with similar climates. The development of new building energy-saving and environmentally friendly materials has important practical significance for improving resource utilization, improving the environment, saving energy and reducing emissions. Building insulation boards are mainly used in building walls, roofs, windows, floors and other parts to play a role in heat insulation and are important indicators of building energy conserva...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30C04B38/10C04B20/02C04B111/40C04B111/27C04B111/20
CPCC04B28/30C04B20/023C04B38/10C04B2111/00017C04B2111/20C04B2111/27C04B2111/40C04B11/264C04B14/185C04B14/08C04B18/08C04B14/22C04B14/386C04B9/00C04B24/42C04B22/08C04B24/08C04B22/16C04B24/121C04B2103/302C04B24/045C04B24/128C04B24/124
Inventor 王磊
Owner HEFEI HUAGAI PHOTOVOLTIAC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap