Vortex spinning technology with Tencel, cotton and cupro blended

A technology of eddy current spinning and blended yarns, which is applied in the direction of yarn, textiles and papermaking, etc., can solve the problems of high cost, low strength, short service life, etc., and achieve good integration and innovation, high dry and wet strength, and good development prospects Effect

Inactive Publication Date: 2017-11-07
ZHEJIANG SHUANGDUN TEXTILE TECH CO LTD
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, cotton fiber also has many disadvantages: more hairiness, easy to pilling, high humidity and heavy sweating, it cannot conduct moisture, forming sticky paste, large heat release during moisture absorption, slow drying after wet, poor shape retention, poor wrinkle resistance, Especially after washing, the wrinkles are serious and ironing is required; the flame retardancy is poor; the strength is low, the wear resistance is poor, and the service life is short
The dry strength of cupro fiber is close to that of viscose fiber, but its wet strength is higher than that of viscose fiber, and its abrasion resistance is also better than that of viscose fiber. It has four functions: breathing, refreshing, antistatic, and good drapability. The disadvantage is that it is relatively expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vortex spinning technology with Tencel, cotton and cupro blended

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] 1. Raw materials: 60% tencel by mass, 25% cotton and 15% cupro ammonium, weaving tencel cotton cupro ammonia fiber by blending eddy current spinning.

[0021] 2. Spinning process flow: Tencel, cotton and copper ammonia pass through FA002A automatic cotton grabbing machine → FA022 multi-storey cotton blending machine → FA106A cotton opener → FA046A vibrating cotton box feeder → A076F single beater lapping machine → After the FA224B carding machine, it goes through the HSD961 draw frame (one parallel, two parallel)→TD03-600 draw frame (three parallel)→MVS861 vortex spinning machine.

[0022] 3. Technical points of the main process technology:

[0023] 3.1. Opening and cleaning process: Tencel, cotton and copper ammonia are respectively opened and cleaned according to the principle of "low speed opening, less beating, less falling, and anti-sticking rolls". The beating speeds are 550r / min, 500r / min and 450r / min respectively The quantitative wet weights are 480g / m, 400g / m ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a vortex spinning technology with Tencel, cotton and cupro blended. The blended yarn includes, by mass, 60% of Tencel, 25% of cotton and 15% of cupro; after opening and cleaning and carding are conducted on Tencel, cotton and cupro respectively, the yarn is spun through drawing and vortex spinning technologies. The composite fibers have the advantages of good elasticity, high wet-and-dry strength, soft hand feeling, elegant gloss, low cost and the like, and have the functions of good moisture absorption and releasability, antistatic property, good drapability and good hydrophilic property.

Description

technical field [0001] The invention relates to the technical field of blended yarns, in particular to a tencel cotton-cupro-ammonia blended vortex spinning process. Background technique [0002] Tencel is a kind of cellulose fiber. It adopts solvent spinning technology. The dry strength is slightly lower than that of polyester, but it is obviously higher than that of ordinary viscose fiber. The wet strength is significantly improved compared with viscose. It has very high rigidity and good Dimensional stability after washing (shrinkage rate is only 2%), high hygroscopicity, round or oval fiber cross section, beautiful luster, soft hand feeling, good drapability, good flow, cheap price, and has the characteristics of cotton Softness, high strength of polyester, and warmth retention of wool, but it tends to harden under hot and humid conditions, and the fleece performance in cold water is not good. [0003] Cotton is an important raw material for the textile industry. It ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04
CPCD02G3/04D10B2201/02D10B2201/20
Inventor 钟亚余涛
Owner ZHEJIANG SHUANGDUN TEXTILE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com