Flame-retardant thermal-insulating polyester fiber curtain and preparation method thereof

A polyester and curtain technology, which is applied in the field of flame-retardant and heat-insulating polyester curtains and its preparation, can solve the problems of increasing fire accidents, economic losses, endangering people's lives, etc., and achieve the effects of comfortable hand feeling and good flame-retardant and heat-insulation performance.

Inactive Publication Date: 2017-11-10
句容市恒鑫遮阳科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the number of fire accidents caused by the ignition of textiles ha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A flame-retardant and heat-insulating polyester curtain, comprising a polyester base cloth and a flame-retardant coating, wherein the flame-retardant coating is made of the following raw materials in parts by weight: 10 parts of water-based polyurethane emulsion, 3 parts of polyvinyl alcohol, tributyl phosphate 0.8 part of ester, 0.5 part of anionic surfactant, 0.2 part of coupling agent, 0.3 part of ultraviolet absorber, 0.2 part of triethanolamine, 0.1 part of glass fiber, 2 parts of filler, 0.4 part of defoamer, 1.2 part of ammonium phosphate, 5 parts of water share.

[0017] Wherein, the anionic surfactant is sodium dodecylbenzenesulfonate; the ultraviolet absorber is rutile titanium oxide; the diameter of the glass fiber is 5-10 μm; the filler is sea stone, asbestos fiber powder , diatomaceous earth, and sodium carboxymethyl cellulose, the weight ratio of sepiolite, asbestos fiber powder, diatomite, and sodium carboxymethyl cellulose is 1:1:1:1.

[0018] The prepa...

Embodiment 2

[0024] A flame-retardant and heat-insulating polyester curtain, comprising a polyester base cloth and a flame-retardant coating, wherein the flame-retardant coating is made of the following raw materials in parts by weight: 13 parts of water-based polyurethane emulsion, 4 parts of polyvinyl alcohol, tributyl phosphate 1.3 parts of ester, 0.7 part of anionic surfactant, 0.4 part of coupling agent, 0.4 part of ultraviolet absorber, 0.3 part of triethanolamine, 0.2 part of glass fiber, 3 parts of filler, 0.6 part of defoamer, 1.7 part of ammonium phosphate, 7 parts of water share.

[0025] Wherein, the anionic surfactant is sodium dodecylbenzenesulfonate; the ultraviolet absorber is rutile titanium oxide; the diameter of the glass fiber is 5-10 μm; the filler is sea stone, asbestos fiber powder , diatomaceous earth, and sodium carboxymethyl cellulose, the weight ratio of sepiolite, asbestos fiber powder, diatomite, and sodium carboxymethyl cellulose is 1:1:1:1.

[0026] The prep...

Embodiment 3

[0032] A flame-retardant and heat-insulating polyester curtain, comprising a polyester base cloth and a flame-retardant coating, wherein the flame-retardant coating is made of the following raw materials in parts by weight: 18 parts of water-based polyurethane emulsion, 6 parts of polyvinyl alcohol, tributyl phosphate 1.8 parts of ester, 0.9 part of anionic surfactant, 0.6 part of coupling agent, 0.6 part of ultraviolet absorber, 0.4 part of triethanolamine, 0.2 part of glass fiber, 4 parts of filler, 0.9 part of defoamer, 2.1 parts of ammonium phosphate, 8 parts of water share.

[0033] Wherein, the anionic surfactant is sodium dodecylbenzenesulfonate; the ultraviolet absorber is rutile titanium oxide; the diameter of the glass fiber is 5-10 μm; the filler is sea stone, asbestos fiber powder , diatomaceous earth, and sodium carboxymethyl cellulose, the weight ratio of sepiolite, asbestos fiber powder, diatomite, and sodium carboxymethyl cellulose is 1:1:1:1.

[0034] The pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Damage lengthaaaaaaaaaa
Damage lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a flame-retardant thermal-insulating polyester fiber curtain and a preparation method thereof. The curtain includes a polyester fiber base cloth and a flame retardant coating layer, the flame retardant coating layer is made from the materials of waterborne polyurethane emulsion, polyvinyl alcohol, tributyl phosphate, anionic surfactant, coupling agent, ultraviolet absorbent, triethanolamine, glass fiber, filler, defoaming agent, ammonium phosphate and water. The preparation method comprises the steps that firstly waterborne polyurethane emulsion, polyvinyl alcohol, tributyl phosphate, anionic surfactant, coupling agent, ultraviolet absorbent, triethanolamine, glass fiber, filler, defoaming agent, and ammonium phosphate are added into water, ultrasonic dispersion and grinding are conducted, and then coating is conducted on the polyester fabric, and after glue spraying and drying, the polyester fiber curtain is prepared. The flame-retardant thermal insulation polyester curtain has good flame-retardant and thermal-insulating properties and feels comfortable and soft.

Description

technical field [0001] The invention belongs to the technical field of curtain fabrics, and in particular relates to a flame-retardant and heat-insulating polyester curtain and a preparation method thereof. Background technique [0002] In recent years, with the continuous improvement of people's living standards, and the establishment and continuous improvement of fire protection regulations and textile flame-retardant standards, the number of decorative textiles and industrial textiles that need flame-retardant finishing has continued to increase. The fire safety issues of building interior decoration materials and so on are increasingly concerned by the government and the public. In home textiles, curtains account for a large proportion, of which polyester fibers are the most used. [0003] The use of polyester has penetrated into all aspects of household, civil and military use. It is currently the chemical fiber with the highest output and fastest development, and it r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00D06N3/14C09D5/18C09D7/12C09D175/04C09D129/04
CPCD06N3/0036C08K2003/2241C08L2205/03C09D5/18C09D175/04D06N3/0063D06N3/144D06N2203/068D06N2209/065D06N2209/067D06N2211/122C08L29/04C08L1/286C08K13/04C08K5/521C08K7/14C08K3/22C08K7/12C08K3/346
Inventor 王岳来
Owner 句容市恒鑫遮阳科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products