PLA (Polylactic Acid) biodegradable plastic product material

A technology for degrading materials and degrading plastics, applied in the field of PLA biodegradable plastic products, can solve the problems of polluting the atmosphere, slow decomposition, affecting the absorption of nutrients and moisture by crops, and achieve the effect of reducing manufacturing costs.

Inactive Publication Date: 2017-11-14
HEILONGJIANG XINDA ENTERPRISE GRP
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the main component of plastic is synthetic resin, the decomposition rate is very slow in the natural environment, and it is extremely harmful to the land, changing its pH, affecting the absorption of nutrients and water by crops, resulting in the landfill of soil containing plastic waste for a long time not recovered
If the plastic waste is disposed of by incineration, a large amount of harmful smoke will be produced, polluting the atmosphere
The cheap and easy availability of plastic packaging makes it easy for people to throw it away, causing visual and environmental damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A PLA biodegradable plastic product material of the present invention is characterized in that it is composed of 30kg biodegradable materials and 70kg PLA plastics, wherein the biodegradable materials are soybean protein and starch, and the soybean protein and starch The ratio is 1:3.

[0018] The oxygen transmission rate of the biodegradable plastic film produced by casting method is as low as 1.0(ml·mm) / (m 2 ·d·Pa), the water permeability is as low as 1.6 / (m·s·Pa), the tensile strength can reach 11MPa, and the elongation is as high as 70%.

[0019] The tensile strength of biodegradable plastic parts produced by molding method can reach 45MPa, the bending strength can reach 65MPa, and the density can reach 1.5g / cm 3 , can withstand high temperature of 260 ℃. Using accelerated aging experiments, it is estimated that the natural aging time of biodegradable plastics is 20 years.

Embodiment 2

[0021] A PLA biodegradable plastic product material of the present invention is characterized in that it is composed of 35kg biodegradable materials and 65kg PLA plastics, wherein the biodegradable materials are soybean protein and starch, and the soybean protein and starch The ratio is 1:3.

[0022] The oxygen transmission rate of the biodegradable plastic film produced by casting method is as low as 1.2(ml·mm) / (m 2 ·d·Pa), the water permeability is as low as 1.3 / (m·s·Pa), the tensile strength can reach 14MPa, and the elongation is as high as 75%.

[0023] The tensile strength of biodegradable plastic parts produced by molding method can reach 55MPa, the bending strength can reach 60MPa, and the density can reach 1.7g / cm 3 , can withstand high temperature of 270 ℃. Using accelerated aging experiments, the estimated natural aging time of biodegradable plastics is 15 years.

Embodiment 3

[0025] A PLA biodegradable plastic product material of the present invention is characterized in that it consists of 50kg of biodegradable materials and 50kg of PLA plastics, wherein the biodegradable materials are soybean protein and starch, and the soybean protein and starch The ratio is 1:3.

[0026] The oxygen transmission rate of the biodegradable plastic film produced by casting method is as low as 1.05(ml·mm) / (m 2 ·d·Pa), the water permeability is as low as 1.9 / (m·s·Pa), the tensile strength can reach 17MPa, and the elongation is as high as 77%.

[0027] The tensile strength of biodegradable plastic parts produced by molding method can reach 50MPa, the bending strength can reach 56MPa, and the density can reach 1.25g / cm 3 , can withstand high temperature of 280 ℃. Using accelerated aging experiments, it is estimated that the natural aging time of biodegradable plastics is 10 years.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a PLA (Polylactic Acid) biodegradable plastic product material. The PLA biodegradable plastic product material is prepared from 30 to 60 percent by weight of biodegradable material and 50 to 70 percent by weight of PLA plastic, wherein the biodegradable material is prepared from soy protein and starch in a ratio of 1 to 3. Compared with the conventional synthetic plastic product, biodegradable synthetic plastic has higher light transmittance, oxygen permeability, heat resistance, toughness, softness, elasticity, tensile strength and anti-aging performance than an ordinary synthetic plastic product; by adopting biomass synthetic plastic, the manufacturing cost is lowered greatly; a bioplastic product material is completely decomposed into a high-quality organic fertilizer in soil within 5 to 8 months.

Description

technical field [0001] The invention relates to a PLA biodegradable plastic product material, which belongs to the field of plastic product materials. Background technique [0002] With the rapid development of the plastics industry, the resulting environmental problems are becoming increasingly serious. The waste of plastic products accounts for 10% of the total amount of urban garbage and 30% of the volume. Since the main component of plastic is synthetic resin, it decomposes very slowly in the natural environment, and it is very harmful to the land, changing its pH, affecting the absorption of nutrients and water by crops, resulting in the landfill of soil containing plastic waste for a long time Cannot be restored. If the plastic waste is disposed of by incineration, a large amount of harmful smoke will be produced, which will pollute the atmosphere. The cheap and easy availability of plastic packaging makes it easy for people to discard it at will, resulting in visua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L3/02C08L89/00C08J5/18B29C43/58B29C45/77B29C45/78B29C47/92B29C48/92
CPCC08L67/04B29C43/58B29C45/77B29C45/78B29C48/92B29C2043/5808B29C2043/5816B29C2948/92704C08J5/18C08J2367/04C08J2403/02C08J2489/00C08L2201/06C08L2205/03C08L3/02C08L89/00
Inventor 于敬阳崔成杰谢众
Owner HEILONGJIANG XINDA ENTERPRISE GRP