POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition and preparation method thereof

A technology of vinyl ester resin and composition, which is applied in the field of flame retardancy, can solve the problems of high resin viscosity, poor compatibility, high smoke density and smoke toxicity, and achieve good compatibility, good thermal stability, The effect of simple preparation method

Active Publication Date: 2017-12-08
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to improve the flame retardant properties of vinyl ester resins, while solving the problems of high smoke density and smoke toxicity in the combustion process of traditional flame retardants and vinyl ester resins, as well as the traditional flame retardants and v

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition and preparation method thereof
  • POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition and preparation method thereof
  • POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A POSS modified flame-retardant low-smoke and low-toxic vinyl ester resin composition includes bisphenol A epoxy vinyl ester resin, curing agent methyl ethyl ketone peroxide, accelerator cobalt isooctanoate and flame retardant potassium sulfonate POSS, ladder type The mixture of POSS and phosphorus-containing POSS, the mass percent of each component is as follows:

[0041]

[0042]

[0043] A preparation method of a POSS modified flame-retardant low-smoke and low-toxicity vinyl ester resin composition, the specific preparation steps are:

[0044] 1) Add 154g of bisphenol A epoxy vinyl ester resin, 10g of potassium sulfonate POSS, 15g of ladder-type POSS and 15g of phosphorus-containing POSS into the mixing kettle, and stir at 25°C until uniformly mixed;

[0045] 2) Control the temperature of the bisphenol A epoxy vinyl ester resin mixture in 1) at 25°C, add 6g of curing agent methyl ethyl ketone peroxide, and then stir until the curing agent and the resin system a...

Embodiment 2

[0049] A POSS modified flame-retardant low-smoke and low-toxic vinyl ester resin composition includes bisphenol A epoxy vinyl ester resin, curing agent methyl ethyl ketone peroxide, accelerator cobalt isooctanoate and flame retardant potassium sulfonate POSS, ladder type The mixture of POSS and phosphorus-containing POSS, the mass percent of each component is as follows:

[0050]

[0051] A preparation method of a POSS modified flame-retardant low-smoke and low-toxicity vinyl ester resin composition, the specific preparation steps are:

[0052] 1) Add 153g of bisphenol A epoxy vinyl ester resin, 10g of potassium sulfonate POSS, 15g of ladder-type POSS and 15g of phosphorus-containing POSS into the mixing kettle, and stir at 25°C until uniformly mixed;

[0053] 2) Control the temperature of the bisphenol A epoxy vinyl ester resin mixture in 1) at 25°C, add 6g of curing agent methyl ethyl ketone peroxide, and then stir until the curing agent and the resin system are evenly mi...

Embodiment 3

[0058] A POSS modified flame-retardant low-smoke and low-toxicity vinyl ester resin composition comprises phenolic epoxy vinyl ester resin, curing agent cyclohexanone peroxide, accelerator cobalt naphthenate and flame retardant potassium sulfonate POSS, ladder Type POSS and the mixture of phosphorus-containing POSS, the mass percent of each component is as follows:

[0059]

[0060] A preparation method of a POSS modified flame-retardant low-smoke and low-toxicity vinyl ester resin composition, the specific preparation steps are:

[0061] 1) Add a mixture of 169g novolac epoxy vinyl ester resin, 9g potassium sulfonate POSS, 7g ladder type POSS and 6g phosphorus-containing POSS into the mixing kettle, and stir at 25°C until the system is evenly mixed;

[0062] 2) Adjust the temperature of the novolak epoxy vinyl ester resin mixture in 1) to 25°C, add 8g of curing agent cyclohexanone peroxide, and then stir until the curing agent is evenly mixed;

[0063] 3) Control the temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition and a preparation method thereof, and belongs to the technical field of flame retardance. Vinyl ester resin is used as a raw material, one or a combination of any two or three of potassium sulfonate POSS, trapezoidal POSS and phosphorus-containing POSS is used as a flame retardant, methyl ethyl ketone peroxide or the like is used as a curing agent, cobalt isooctanoate or the like is used as an accelerator, and finally the POSS-modified flame-retardant, low-smoke and low-toxicity vinyl ester resin composition is obtained. The vinyl ester resin composition has strong flame retardance, good heat stability and good compatibility of the POSS and the vinyl ester resin, does not contain halogen, can achieve the effects of flame retardance, low toxicity and smoke suppression at the same time, and can be mixed in the molecular level; the preparation method is simple, and is suitable for mass production.

Description

technical field [0001] The invention relates to a POSS modified flame-retardant low-smoke and low-toxicity vinyl ester resin composition and a preparation method thereof, belonging to the technical field of flame retardancy. Background technique [0002] Vinyl ester resin is a product of addition polymerization of epoxy resin and unsaturated monocarboxylic acid containing double bonds. Its technological performance is similar to that of unsaturated polyester resin, and its chemical structure is similar to that of epoxy resin. Therefore, it can be called a combination A new type of resin produced by the advantages of both polyester resin and epoxy resin. As a kind of unsaturated polyester resin, vinyl ester resin has excellent mechanical properties, high temperature resistance, chemical corrosion resistance and fast The advantages of solidification, low viscosity and easy flow have been widely used in FRP corrosion-resistant products and chemical corrosion-resistant projects....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/10C08L83/08
CPCC08L63/10C08L2201/02C08L2201/08C08L2201/22C08L2205/025C08L2205/03C08L2205/035C08L83/08
Inventor 杨荣杰王小霞张文超
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap