Indoor fireproof paint based on vinylcyclohexene dioxide

A technology of vinyl cyclohexenedione and fireproof coatings, which is applied in fireproof coatings, coatings, etc., can solve the problems of limited protection range and short fireproof time, and achieve the effect of reinforcing performance

Inactive Publication Date: 2017-12-19
江阴市尤乐防火阻燃材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing fire retardant coatings often have shortcomings such as short fire protection time and limited protection range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The interior fireproof coating based on vinyl cyclohexenedione contains the following components in parts by mass in its raw materials:

[0024] 20 parts of vinyl cyclohexenedione,

[0025] 15 parts of magnesium hydroxide,

[0026] 10 parts of ethanol,

[0027] Calcium carbonate 10 parts,

[0028] 15 parts of talcum powder,

[0029] 10 parts of silane,

[0030] 12 parts of silicone,

[0031] 5 parts glass sand,

[0032] Resin 5 parts.

[0033] Mix vinylcyclohexenedione and magnesium hydroxide first, heat to 75-125°C, keep warm for 30-240min, then add ethanol, calcium carbonate, talcum powder, silane, siloxane, glass sand, resin, Adjust the temperature to 60-85°C and keep it warm for 50-120 minutes to get the fireproof coating.

Embodiment 2

[0035] The interior fireproof coating based on vinyl cyclohexenedione contains the following components in parts by mass in its raw materials:

[0036] 25 parts of vinyl cyclohexenedione,

[0037] 30 parts of magnesium hydroxide,

[0038] 5 parts of ethanol,

[0039] Calcium carbonate 10 parts,

[0040] 15 parts of talcum powder,

[0041] 10 parts of silane,

[0042] 8 parts of silicone,

[0043] 8 parts glass fiber,

[0044] 6 parts resin,

[0045] 3 parts of leveling agent,

[0046] 2 parts of defoamer.

[0047] Mix vinylcyclohexenedione and magnesium hydroxide first, heat to 75-125°C, keep warm for 30-240min, then add ethanol, calcium carbonate, talcum powder, silane, siloxane, glass fiber, resin, fluid Add leveling agent and defoamer, adjust the temperature to 60-85°C, keep warm for 50-120min, and then get the fireproof coating.

Embodiment 3

[0049] The interior fireproof coating based on vinyl cyclohexenedione contains the following components in parts by mass in its raw materials:

[0050] 15 parts of vinyl cyclohexenedione,

[0051] Aluminum hydroxide 25 parts,

[0052] 5 parts of ethanol,

[0053] Calcium carbonate 7 parts,

[0054] Talcum powder 25 parts,

[0055] 6 parts of silane,

[0056] 12 parts of silicone,

[0057] 5 parts glass sand,

[0058] 8 parts resin,

[0059] 8 parts of water,

[0060] Thickener 2 parts.

[0061] Mix vinylcyclohexenedione, aluminum hydroxide and water first, heat to 75-125°C, keep warm for 30-240min, then add ethanol, calcium carbonate, talcum powder, silane, siloxane, glass sand, resin and Thickener is added, the temperature is adjusted to 60-85°C, and the temperature is kept for 50-120min to obtain the fireproof coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an indoor fireproof paint based on vinylcyclohexene dioxide. The indoor fireproof paint based on vinylcyclohexene dioxide comprises the following main components by mass: 15-25 parts of vinylcyclohexene dioxide, 15-30 parts of metal hydroxide, 5 to 12 parts of ethanol, 7-10 parts of calcium carbonate, 15-25 parts of talcum powder, 6-12 parts of silane, 6-12 parts of siloxane, 5-8 parts of glass sand and 5-8 parts of resin. According to the invention, vinylcyclohexene dioxide and metal hydroxide are compounded, so the fireproof paint can maintain fire-retardant properties and fireproof capabilities like flame resistance, flame prevention and fire retardance, and can effectively protect surrounding flammable materials.

Description

technical field [0001] The invention relates to a fireproof coating, in particular to a polyorganic acid-based fireproof coating for indoor fireproofing. Background technique [0002] At present, fire prevention measures at home and abroad are divided into dredging method and interception method in principle, and interception method is divided into outsourcing sealing method, shielding method and spraying method. Fireproof material is widely used as a material coated on the surface of objects with functions of heat insulation, fire prevention and flame retardancy. It can effectively delay the development of fire and prevent the spread of flame when used in building materials. [0003] The patent application of application publication number CN103923545A discloses a kind of fireproof coating. The coating is non-toxic and non-irritating, and has good adhesion, beauty and good flame-retardant effect when coating. Existing fireproof coatings often have shortcomings such as sho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D7/12C09D5/18
CPCC09D4/06C09D5/18
Inventor 刘明贤
Owner 江阴市尤乐防火阻燃材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com