Y/Gd2O3/ZSM-23/ZSM-5/ASA composite material and preparation method thereof
A technology of ZSM-23 and composite materials, which is applied in the direction of chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve the problems of adding auxiliary equipment, increasing the cost of synthesizing composite molecular sieves, and long preparation time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0053] Example 1:
[0054] Y / Gd 2 O 3 / ZSM-23 / ZSM-5 / ASA composite material synthesis
[0055] (1) Preparation of directing agent: Take 24.7g of sodium hydroxide (Beijing Chemical Plant, analytically pure) into 45.9g of water, stir until all the sodium hydroxide is dissolved, and then add 6.5g of sodium metaaluminate (Shandong Aluminum Company Research) Hospital, industrial products, Al 2 O 3 The content is 49.1wt%), stirring until all the sodium metaaluminate is dissolved, and the sodium metaaluminate solution A is obtained. 70g solution A and 100g water glass (Beijing Red Star Sodium Alkaline Plant, SiO 2 Content 27.81wt%, Na 2 O content 8.74wt%) was sequentially poured into 65.5g of deionized water, stirred evenly and statically aged at 30°C for 22h to obtain a directing agent. The molar ratio of each component of the directing agent is: 16Na 2 O:Al 2 O 3 :16SiO 2 :330H 2 O.
[0056] (2)Gd 2 O 3 / ZSM-23 / ZSM-5 precursor preparation: using a solid-like synthesis method (single pot ...
Example Embodiment
[0060] Example 2:
[0061] Unless otherwise specified, the sources of all raw materials are the same as in Example 1.
[0062] (1) Preparation of the directing agent: add 32.1g of sodium hydroxide to 45.9g of water, stir until the sodium hydroxide is completely dissolved, then add 6.5g of sodium metaaluminate, and stir until the sodium metaaluminate is completely dissolved to obtain metaaluminate Sodium solution A. Pour 70 g of solution A and 112 g of water glass into 79 g of deionized water in sequence, stir evenly, and statically age at 30°C for 22 hours to obtain a directing agent. The molar ratio of each component of the directing agent is: 20Na 2 O:Al 2 O 3 :18SiO 2 :440H 2 O.
[0063] (2)Gd 2 O 3 / ZSM-23 / ZSM-5 precursor preparation: using a solid-like synthesis method (50% solid content in a single pot), using coarse-pored silica gel, sodium metaaluminate, deionized water, trimethylamine and hexamethylene diamine as raw materials, Crystallize at a constant temperature of 100...
Example Embodiment
[0067] Example 3
[0068] Unless otherwise specified, the sources of all raw materials are the same as in Example 1.
[0069] (1) Preparation of directing agent: Take 24.7g of sodium hydroxide and add it to 45.9g of water, stir until the sodium hydroxide is completely dissolved, then add 6.5g of sodium metaaluminate, and stir until the sodium metaaluminate is completely dissolved to obtain metaaluminate Sodium solution A. Pour 70 g of solution A and 100 g of water glass into 65.5 g of deionized water in turn, stir evenly and statically age at 30° C. for 22 hours to obtain a directing agent. The molar ratio of each component of the directing agent is: 16Na 2 O:Al 2 O 3 :16SiO 2 :330H 2 O.
[0070] (2)Gd 2 O 3 / ZSM-23 / ZSM-5 precursor preparation: using a solid-like synthesis method (50% solid content in a single pot), using coarse-pored silica gel, sodium metaaluminate, deionized water, trimethylamine and hexamethylene diamine as raw materials, Crystallize at a constant temperature ...
PUM
Property | Measurement | Unit |
---|---|---|
Total pore volume | aaaaa | aaaaa |
Pore volume | aaaaa | aaaaa |
Mesopore volume | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap