A method for flotation purification of hemimorphite from quartz

A hemimorphite and flotation technology, applied in flotation, solid separation, etc., can solve the problems of complex process flow and large influence of sulfide-amine method, and achieve the effects of simple process flow, good water solubility, and simple chemical system

Active Publication Date: 2019-09-06
NORTHEASTERN UNIV LIAONING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the slime and soluble salt minerals have a great influence on the sulfide-amine method, and both activators and inhibitors need to be added during the flotation process, so the process is also relatively complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for flotation purification of hemimorphite from quartz

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) The hemimorphite and quartz are configured into a mixed ore sample according to a mass ratio of 3:17, and 5g of the ore sample is weighed and put into a flotation cell and deionized water is added, wherein the mass ratio of deionized water to the ore sample is The ratio is 5:1; using a hanging tank flotation machine, under the condition of 1992r / min, stirring and pulping for 2min;

[0027] (2) After pulping, add 750 g / t of collector N,N'-difatty acyl ethylenediamine sodium dipropionate at room temperature 13°C and natural pulp pH (pH=6.63), and stir for 2 minutes. Flotation, the flotation time is 3min. After the flotation, dry and weigh the foam product, namely the concentrate, and the tailings, the product in the tank, respectively, and take samples to test the grade, and calculate the recovery rate, among which the Zn grade in the flotation concentrate is 51.90%, and the recovery rate can reach 84.76%.

Embodiment 2

[0029] (1) The hemimorphite and quartz are configured into a mixed ore sample according to a mass ratio of 3:17, and 5g of the ore sample is weighed and put into a flotation cell and deionized water is added, wherein the mass ratio of the deionized water to the ore sample is 5:1; using a hanging tank flotation machine, under the condition of 1992r / min, stirring and pulping for 2min;

[0030] (2) After pulping, add collector N,N'-difatty acyl ethylenediamine dipropionate 900g / t under the condition of room temperature 13°C and natural pulp pH (pH=6.63), and stir for 2 minutes. Flotation, the flotation time is 3min. After the flotation, dry and weigh the foam product, namely the concentrate, and the tailings, the product in the tank, respectively, and take samples to test the grade, and calculate the recovery rate, among which the Zn grade in the flotation concentrate is 49.45%, and the recovery rate can reach 88.03%.

Embodiment 3

[0032] (1) The hemimorphite and quartz are configured into a mixed ore sample according to a mass ratio of 3:17, and 5g of the ore sample is weighed and put into a flotation cell and deionized water is added, wherein the mass ratio of the deionized water to the ore sample is 5:1; use the hanging tank flotation machine, under the condition of 1992r / min, stir and adjust the pulp for 2 minutes; add NaOH solution with a concentration of 1mol / L to the pulp to adjust the pH value of the pulp to 7.71, and then adjust the pulp for 2 minutes;

[0033] (2) After pulping, under the conditions of room temperature 13°C and pulp pH 7.71, add collector N,N′-difatty acyl ethylenediamine sodium dipropionate 900g / t, stir for 2min and then carry out flotation. The selected time is 3 minutes. After the flotation, dry and weigh the foam product, namely the concentrate, and the tailings, the product in the tank, respectively, and take samples to test the grade, and calculate the recovery rate, amon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for flotation and purification of hemimorphite from quartz, specifically to a flotation separation method for hemimorphite and quartz, and belongs to the technical field of mineral flotation separation in the field of mineral processing engineering. A method for flotation and purification of hemimorphite from quartz. Mix the mixed mineral sample of hemimorphite and quartz to be processed with deionized water, and add a collector to the evenly stirred slurry. The amount of collector is 750 ~900g / t; stir the slurry added with the collector evenly and then perform flotation, wherein the collector is sodium N,N'-bis-fatty acyl ethylenediamine dipropionate. The process proposed by the present invention for flotation and purification of hemimorphite from quartz has a simple process flow, simple chemical system, convenient operation, and good industrial feasibility prospects.

Description

technical field [0001] The invention relates to a method for flotation purification of hemimorphite from quartz, in particular to a flotation separation method of hemimorphite and quartz, and belongs to the technical field of mineral flotation separation in the field of mineral processing engineering. Background technique [0002] Zinc is the fourth "common" metal, after iron, aluminum and copper. Due to its suitable mechanical properties and anti-corrosion properties, zinc is widely used in automobile, construction, shipbuilding, light industry and other industries, especially in modern industrial battery manufacturing, which has an irreplaceable position. Since entering the 21st century, with the rapid growth of my country's economy, the demand for zinc resources is also increasing. my country has become the world's largest zinc producer and zinc resource consumer. From 2006 to 2014, my country's zinc metal production increased by nearly 85%. In 2014, my country's zinc c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B03D1/016B03D1/02B03D101/02B03D103/04
Inventor 刘文刚赵亮刘文宝魏德洲崔宝玉赵强
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com