Slag adhesion preventing separant for stirring head and preparation method thereof

A technology of anti-sticking slag and release agent, which is applied in the field of refractory materials, can solve the problems of high labor intensity, unsafety, non-center alignment of the mixing head, etc., and achieve the effects of reducing labor intensity, increasing service life, and high bonding strength

Active Publication Date: 2018-02-13
北京利尔高温材料股份有限公司
View PDF16 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the use of the mixing head, the sticky slag and hanging slag of the mixing head become unfavorable factors
First, it is not easy to clean up the slag after sticking. If the manual cleaning of slag is labor-intensive, the working environment is poor and high-temperature operation has great potential safety hazards
Second, if the slag is not cleaned in time, the uneven sticky slag will cause the center of the mixing head to rotate and shake, which will affect the service life of the mixing head and also pose a safety hazard
Third, when the slag line part of the mixing head sticks to the slag seriously, the diameter of the slag line part becomes larger, which affects the movement of the stirring head up and down at the round hole of the operation platform, and affects the normal production
In addition, after a lot of research and practical work, it is found that the desulfurization efficiency of the three-blade KR mixing head is higher than that of the four-blade mixing head, and the service life can also be greatly improved. The mixing head is more prone to eccentric rotation, which affects the service life, and also increases the load on the challenge mechanism, which has a large unsafe factor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An anti-sticking slag release agent for a stirring head, comprising the following raw materials in parts by weight:

[0020] 55 parts of quartz powder; 5 parts of earthy graphite; 5 parts of silicon carbide; 3 parts of clay; 0.5 part of sodium carboxymethyl cellulose; 1 part of paper fiber; 0.03 part of organic fiber.

[0021] A preparation method of an anti-sticking slag release agent for a stirring head, comprising the steps of:

[0022] According to the order of 55 parts of quartz powder, 5 parts of earthy graphite, 5 parts of silicon carbide and 3 parts of clay, add them to the forced mixer in turn, and while stirring, add 0.5 parts of sodium carboxymethyl cellulose, 1 part of paper fiber and organic fiber 0.03 parts, of which paper fibers and organic fibers should be sieved into the mixer, after the addition of materials, continue to stir for 8-10 minutes, then add water 40wt.% ~ 60wt.%, after adding water, continue to stir for 10 to 15 minutes to discharge. Put i...

Embodiment 2

[0024] An anti-sticking slag release agent for a stirring head, comprising the following raw materials in parts by weight:

[0025] 63 parts of quartz powder; 11 parts of earthy graphite; 12 parts of silicon carbide; 5 parts of clay; 1 part of sodium carboxymethyl cellulose; 2 parts of paper fiber; 0.1 part of organic fiber.

[0026] A preparation method of an anti-sticking slag release agent for a stirring head, comprising the steps of:

[0027] According to the order of 63 parts of quartz powder, 11 parts of earthy graphite, 12 parts of silicon carbide, and 5 parts of clay, add them to the forced mixer in sequence, and while stirring, add 1 part of sodium carboxymethyl cellulose and 2 parts of paper fiber; 0.1 part, of which the paper fiber and organic fiber should be sieved into the mixer, continue stirring for 8-10 minutes after feeding, then add 40wt.%~60wt.% of water, continue stirring for 10~15 minutes after adding water, and discharge. Put it into a pouch containing t...

Embodiment 3

[0029] An anti-sticking slag release agent for a stirring head, comprising the following raw materials in parts by weight:

[0030] 75 parts of quartz powder; 15 parts of earthy graphite; 15 parts of silicon carbide; 8 parts of clay; 2 parts of sodium carboxymethyl cellulose; 3.5 parts of paper fiber; 0.15 part of organic fiber.

[0031] A preparation method of an anti-sticking slag release agent for a stirring head, comprising the steps of:

[0032] According to the order of 75 parts of quartz powder, 15 parts of earthy graphite, 15 parts of silicon carbide, and 8 parts of clay, they were added to the forced mixer in sequence, and while stirring, 2 parts of sodium carboxymethyl cellulose, 3.5 parts of paper fiber, and organic fiber were added. 0.15 parts, of which paper fibers and organic fibers should be sieved into the mixer, after the addition of materials, continue to stir for 8-10 minutes, then add water 40wt.% ~ 60wt.%, after adding water, continue to stir for 10 to 15 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a slag adhesion preventing separant for a stirring head and a preparation method thereof and solves the problem of slag adhesion of the stirring head. The slag adhesion preventing separant for the stirring head is prepared from the following raw materials in parts by weight: 55 to 75 parts of quartz powder, 5 to 15 parts of amorphous graphite, 5 to 15 parts of silicon carbide, 3 to 8 parts of clay, 0.5 to 2 parts of sodium carboxymethylcellulose, 1 to 3.5 parts of paper fiber and 0.03 to 0.15 parts of organic fiber. The prepared separant disclosed by the invention has the characteristics of good adhesion under a normal temperature, high low-temperature bonding strength, reduction or loss of high-temperature bonding strength and benefit to automatic falling off; theseparant can generate larger volume expansion or contraction along with temperature rise and fall, so that the separant is favorable for self crack generating and has an automatic structure collapsingeffect. When being applied to the surface of a refractory material of the KR stirring head, the separant has an effect of preventing slag adhesion; thus, labor intensity is reduced, and service lifeof the stirring head is improved.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to an anti-sticking slag release agent for a stirring head and a preparation method thereof. Background technique [0002] With the increasing development of various high-quality steels and special steels, the deep desulfurization technology of molten iron is also constantly researched and optimized. Among them, the KR stirring method has become the pretreatment method of molten iron with obvious advantages and widely used. However, during the use of the mixing head, the sticky slag and hanging slag of the mixing head become unfavorable factors. First, it is not easy to clean up slag after sticking. If manual slag removal is labor-intensive, the working environment is poor and high-temperature operation has great potential safety hazards. Second, if the slag is not cleaned in time, the uneven sticky slag will cause the center of the mixing head to rotate and shake, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66C04B35/80
CPCC04B35/803C04B35/66C04B2235/3201C04B2235/327C04B2235/3418C04B2235/349C04B2235/3826C04B2235/425C04B2235/9607
Inventor 赵冉刘建岭张晓波万小宝丁海瑞曹仁锋刘丽刘美荣车晓梅王伟伟刘洋张盛
Owner 北京利尔高温材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products